Refractory Imitation "Xuan Paper"

A rice paper and refractory technology, which is used in the preparation and application of new inorganic refractory paper, and can solve problems such as turning into ashes

Active Publication Date: 2021-07-13
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flammability of rice paper is its most fatal weakness. Looking back at history, how many masterpieces of calligraphy and painting by masters were reduced to ashes in the fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Refractory Imitation "Xuan Paper"
  • Refractory Imitation "Xuan Paper"
  • Refractory Imitation "Xuan Paper"

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] 0.617g of silica fibers (6μm in diameter and 3mm in length) were formulated into an aqueous suspension, 2.468g of ultra-long hydroxyapatite nanowires were added, ultrasonically dispersed, and then 0.545g of self-made nano-scale inorganic adhesive was added. The preparation steps of nano-scale inorganic adhesive are as follows: mix sodium silicate, potassium pyrophosphate, aluminum sulfate, and boric acid in water according to the feed ratio (mass ratio) of 6:20:1:2, stir evenly, and prepare nano-scale adhesives through chemical reactions. Inorganic adhesive. The reaction temperature was 35°C, and the reaction time was 60 minutes. Image 6 A scanning electron microscope image of the obtained nano-scale inorganic adhesive is shown, and it can be seen that the nano-scale inorganic adhesive has a nano-particle shape and a particle size of 20-60 nm. The prepared slurry was filtered and formed on a Kaiser rapid paper sheet former, and the formed paper was pressed (at a press...

Embodiment 2

[0054] Put the new refractory imitation "xuan paper" obtained in Example 1 into a blast drying oven at 105°C for accelerated aging. 360 days of accelerated aging is equivalent to 3000 years of natural aging. Simulated aging results (see Figure 4 , 5 ) shows that compared with the traditional rice paper, the refractory imitation "Xuan paper" has more excellent durability. After artificial aging for 3000 years, its whiteness is still significantly higher than that of the traditional rice paper without aging; The ultralong nanowires of hydroxyapatite did not change significantly, while the fibers in traditional rice paper degraded to a certain extent.

Embodiment 3

[0056] The novel refractory imitation "xuan paper" gained in Example 1 is carried out anti-mildew test, and concrete method is: in the first group of experiments, the concentration is 10 6 The spores of three kinds of molds (Aspergillus niger, Trichoderma longibrachiae, and Trichoderma globosa) in cfu / ml were inoculated into red Bengal culture medium respectively, and then traditional rice paper (raw and cooked rice paper) and refractory imitation "Xuan paper" were placed in the On the culture medium inoculated with mold spores, place them in a microbial incubator with a temperature of 30°C and a humidity of 90%, cultivate them for 4 days, and observe the reproduction of mold spores on the paper. In the second set of experiments, the concentration was 10 4 The spores of three kinds of molds (Aspergillus niger, Trichoderma longibranchus, and Trichoderma globosa) with cfu / ml were sprayed on traditional rice paper (raw and cooked rice paper) and refractory imitation "Xuan paper" ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to refractory imitation "rice paper", and the composition of the refractory imitation "rice paper" includes hydroxyapatite ultra-long nanowires, inorganic fibers and nano-scale inorganic adhesives, wherein the diameter of the hydroxyapatite ultra-long nanowires The diameter of the inorganic fibers is 1-40 μm and the length is 1-12 mm; the morphology of the nano-scale inorganic adhesive is nano-particles, and the particle size is 5-12 mm. 100 nm.

Description

technical field [0001] The invention belongs to the field of preparation and application of novel inorganic fire-resistant paper, and in particular relates to a novel inorganic fire-resistant imitation "Xuan paper" prepared from hydroxyapatite ultra-long nanowires as the main raw material. Background technique [0002] Xuan paper is a unique art treasure of our country and is well-known at home and abroad. Xuan paper, as the best carrier of Chinese calligraphy and painting art, has provided reliable writing materials for the record, inheritance and development of Chinese civilization in the course of thousands of years of development, and has played an important role in promoting the development of Chinese calligraphy and painting art. In 2009, it was selected into the "Representative List of the Intangible Cultural Heritage of Humanity" by UNESCO. [0003] Traditional rice paper is made of green sandalwood bark in Jingxian County, Anhui Province and straw in Shatian, and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21H13/38D21H13/46D21H17/68D21H17/66D21H17/65
CPCD21H13/38D21H13/46D21H17/65D21H17/66D21H17/68D21H27/00
Inventor 朱英杰董丽颖
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com