Environmentally-friendly clothing material and processing method thereof

A processing method and an environmentally friendly technology, applied in the field of clothing materials, can solve the problems of reducing heat resistance, unable to use very environmentally friendly raw materials, etc., to achieve the effects of improving heat resistance, improving living standards, and improving quality of life

Inactive Publication Date: 2019-01-08
宁波元元之傲针织织造有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an environment-friendly clothing material and its processing method, which solves the problems that the existing environment-friendly clothing materials cannot use very environment-friendly raw materials and reduce the overall heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The invention also discloses a processing method of an environment-friendly clothing material, which specifically includes the following steps:

[0025] S1, the leaves are mechanically centrifuged, and chemical agents are added to centrifuge them together to improve the accessibility of the leaves, and then the leaves are subjected to alkali treatment in a sodium hydroxide solution with a mass percentage concentration of 15%-20%. The temperature is 50-55°C, and the alkali treatment time is 15-25min;

[0026] S2, washing the leaves in S1 after being treated with alkali, adjusting the pH with an acid solution after washing, and washing again after adjustment, then drying at a temperature of 80-96° C. for 25-30 minutes to obtain fibers in the leaves;

[0027] S3, using the fibers in the leaves obtained in S2 as a reinforcing phase, using nano-calcium carbonate and glue as a matrix to obtain a composite material through hot pressing, keeping the pressure of the hot press, a...

Embodiment 2

[0031] The invention also discloses a processing method of an environment-friendly clothing material, which specifically includes the following steps:

[0032] S1, the leaves are mechanically centrifuged, and chemical agents are added to centrifuge them together to improve the accessibility to the leaves, and then the leaves are subjected to alkali treatment in a sodium hydroxide solution with a mass percentage concentration of 25%-30%. The temperature is 60-70°C, and the alkali treatment time is 20-25min;

[0033] S2. Washing the leaves in S1 after being treated with alkali, adjusting the pH with an acid solution after washing, and washing again after adjustment, drying at a temperature of 70-96° C. for 20-30 minutes at this time to obtain fibers in the leaves;

[0034] S3, using the fibers in the leaves obtained in S2 as a reinforcing phase, using nano-calcium carbonate and glue as a matrix to obtain a composite material through hot pressing, keeping the pressure of the hot ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmentally-friendly clothing material, which is prepared from the following raw materials in parts by weight: 40 to 45 percent of tree leaves, 15 to 20 percent of a chemical agent, 10 to 15 percent of a sodium hydroxide solution, 8 to 10 percent of nano calcium carbonate, 10 to 15 percent of glue, 6 to 8 percent of polyether ester and 2 to 3 percent of polyamide. The polyether ester is a segmented copolymer, which is a polybutylene terephthalate-polyethylene oxide-polypropylene oxide thermoplastic elastomer, obtained by melting copolycondensation of dimethyl p-benzoate, butanediol, polyethylene oxide diol and propylene oxide diol, and relates to the technical field of clothing materials. According to the environmentally-friendly clothing material and a processing method thereof, extremely environmentally-friendly raw materials are used, so the environmental friendliness of the material is greatly improved; existing resources are effectively used, the living quality of people is improved, and the processing cost of a producer is reduced; and furthermore, the overall heat resistance is enhanced to a certain extent, and the overall quality is increased.

Description

technical field [0001] The invention relates to the technical field of clothing materials, in particular to an environment-friendly clothing material and a processing method thereof. Background technique [0002] Clothing materials are composite materials that use various forms of fibers, yarns, and fabrics as the reinforcing phase, and resin, rubber, metal, cement, ceramics, and other materials as the matrix phase. The structure and performance of clothing fabrics, the bonding strength of the interface between textile materials and the matrix, and the performance of the matrix determine the performance of composite materials. Environmental protection generally refers to the coordination of the relationship between humans and the environment in order to solve actual or potential environmental problems. , the general term for various actions taken to protect the living environment of human beings and ensure the sustainable development of the economy and society, so as to make...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L97/02C08L67/02C08L77/00C08K13/02C08K3/26C08K3/22
CPCC08K2003/2241C08K2003/2296C08K2003/265C08K2201/011C08L97/02C08L2201/08C08L2205/03C08L2207/04C08L67/02C08L77/00C08K13/02C08K3/26C08K3/22
Inventor 徐光辉
Owner 宁波元元之傲针织织造有限公司