Processing technology of carbonizing of recombined bamboos or recombined woods

A processing technology, a technology of recombining bamboo, applied in wood processing equipment, wood treatment, impregnated wood, etc., can solve the problems of low production efficiency, environmental pollution, high energy consumption, etc., achieve low cost, simple processing technology, and reduced production cost Effect

Active Publication Date: 2019-02-05
ZHEJIANG FORESTRY UNIVERSITY
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the carbonized recombined bamboo adopts high-temperature heat treatment processing technology at present, which has high energy consumption, long cycle, low production efficiency, and the mass loss rate is as high as about 10%-20%, and a large amount of waste gas and waste liquid are discharged during the heat treatment process, polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of carbonizing of recombined bamboos or recombined woods
  • Processing technology of carbonizing of recombined bamboos or recombined woods
  • Processing technology of carbonizing of recombined bamboos or recombined woods

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1: the processing technology of recombined bamboo or wood carbonization specifically comprises the following steps:

[0048] a, carbonization treatment: bamboo bundles are put into a treatment tank containing 100 parts of water, 1 part of ferric chloride and 0.2 part of tannin for immersion carbonization, the immersion temperature is 30 ℃, and the immersion time is 8 hours;

[0049] b, drying: dry the bamboo bundles at a temperature of 78°C to ensure that the moisture content of the bamboo bundles is 12% after drying;

[0050] c, dipping: get the phenolic resin glue with a solid content of 31%, soak the bamboo bundles in the phenolic resin glue for 15 minutes;

[0051] d, aging: the bamboo bundles after dipping were aged for 4 days;

[0052] e. Blank assembly: arrange the bamboo beams along the fiber direction and put them into the mold;

[0053] f. Hot pressing: put the slab into a hot pressing machine for hot pressing, the hot pressing pressure is 1.8MPa, t...

Embodiment 2

[0055] Embodiment 2: the processing technology of recombined bamboo or wood carbonization, specifically comprises the following steps:

[0056] a, carbonization treatment: put the bamboo bundles into a treatment tank containing 100 parts of water, 5 parts of calcium chloride and 0.1 part of phenol for immersion carbonization, the immersion temperature is 45-55 ℃, and the immersion time is 8 hours;

[0057] b, drying: the bamboo bundles are dried at a temperature of 60°C until the moisture content of the bamboo bundles is 10%;

[0058] c, dipping: get the phenolic resin glue with solid content of 32%, soak the bamboo bundles in the phenolic resin glue for 10 minutes;

[0059] d, aging: the bamboo bundles after dipping are aged for 3-4 days;

[0060] e. Blank assembly: arrange the bamboo beams along the fiber direction and put them into the mold;

[0061] f. Hot pressing: put the slab into a hot pressing machine for hot pressing, the hot pressing pressure is 1.7MPa, the hot pr...

Embodiment 3

[0063] Embodiment 3: the processing technology of recombined bamboo or wood carbonization, specifically comprises the following steps:

[0064] Put 100 parts of water, 1 part of hydrochloric acid, 1 part of ferrous sulfate and 0.08 parts of sodium Y-type molecular sieve catalyst into a mixing treatment tank, raise the temperature to 60 ° C, place bamboo bundles in it, and soak for 8 hours; The bundles are dried at a temperature of 60°C until the water content of the bamboo bundles is 10%; then the bamboo bundles are soaked in phenolic resin glue with a solid content of 32% for 10 minutes, and the bamboo bundles are taken out and left at room temperature for 3 days. Bamboo bundles after dipping are arranged along the fiber direction to form a blank, hot pressing, hot pressing pressure is 1.7MPa, hot pressing temperature is 145 °C, hot pressing time is 1 hour, hot pressing is cooled to 65 °C after hot pressing for 1 hour, and then cooled after hot pressing Shaped to get the fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing technology of carbonizing of recombined bamboos or recombined woods. The processing technology sequentially comprises the following steps of performing carbonizingtreatment, performing drying, performing gum dipping, performing displaying, performing assembling, performing hot pressing and performing aging, specifically comprises the following steps of duringcarbonizing treatment, placing bamboo bundles in a treatment tank containing 0.2-1 part of a carbonizing agent and 0.05-0.2 part of a catalyst for impregnating and carbonizing, wherein the impregnating temperature is 25-80 DEG C, and the impregnating time is 2-6 hours. The processing technology disclosed by the invention has good mold resistance and good size stability, and has the characteristicsof being simple in technology, low in cost, free from discharging, free from pollution, high in maneuverability, stable in medicament performance, capable of being recycled, and good in absorbability; and valuable timbers can be replaced, and valuable timber resources are saved.

Description

technical field [0001] The invention relates to a processing technology of recombined bamboo or recombined wood, in particular to a processing technology of recombined bamboo or recombined wood carbonization, and relates to the field of wood floor manufacturing. Background technique [0002] Carbonized recombined bamboo is a new type of bamboo composite material that reorganizes and strengthens bamboo after carbonization. It has the characteristics of high strength, good toughness, high hardness, and mildew resistance. It is widely used in indoor and outdoor floors, furniture, and structural buildings. materials, decoration materials, etc. However, most of the current carbonized recombined bamboo adopts high-temperature heat treatment processing technology, which has high energy consumption, long cycle, low production efficiency, and a mass loss rate of about 10%-20%, and a large amount of waste gas and waste liquid are discharged during the heat treatment process, polluting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K9/00B27K3/02
CPCB27K3/02B27K3/52B27K5/04B27K9/002B27N1/0209B27N3/14B27N3/18
Inventor 孙芳利姜俊沈健孙伟圣杨旭
Owner ZHEJIANG FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com