A kind of rumen-passed choline chloride microcapsules and preparation method thereof

A technology of choline chloride and microcapsules, which is applied in the field of feed additives, can solve problems such as low active ingredients, difficulty in long-term storage, moisture absorption, etc., and achieve promotion, promotion of rumen passing rate and release rate, and increase of release rate Effect

Active Publication Date: 2022-04-05
HANGZHOU KINGTECHINA FEED CO LTD
View PDF15 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Although the above-mentioned documents provide a variety of processes for preparing rumen chloride choline granules / microcapsules, the rumen choline chloride granules / microcapsules produced by the above-mentioned process have low active ingredients, or the rumen choline The rumen rate is between 85% and 90% (24h), and the best release rate in the small intestine is within 95%; and there is moisture absorption when placed for a long time, and it is not easy to store for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rumen-passed choline chloride microcapsules and preparation method thereof
  • A kind of rumen-passed choline chloride microcapsules and preparation method thereof
  • A kind of rumen-passed choline chloride microcapsules and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A rumen-passed choline chloride microcapsule, the raw material composition is as follows: 25% choline chloride; 25% silicon dioxide; 30% carnauba wax; 10% rice bran wax; 5% glucose phthalate; zinc oxide powder 5%.

[0049] Concrete preparation process is as follows:

[0050] (1) Get 250kg choline chloride, after pulverizing, mix homogeneously with 250kg silicon dioxide, obtain mixture I;

[0051] (2) Take 300kg of carnauba wax and put it in the reactor to melt, and keep it warm at a temperature of 20°C higher than its melting point; then mix the melted carnauba wax with mixture I, stir well, and spray into the frozen Freeze-drying at low temperature (8°C) in a chamber to obtain primary coated particles;

[0052] (3) 100kg rice bran wax, 50kg phthalate glucose are dissolved in 500L of 75% (volume fraction) ethanol solution, then add 50kg zinc oxide powder, obtain mixed solution II; In the fluidized bed, spray mixed solution II at the same time, and after the product o...

Embodiment 2

[0066] A rumen-passed choline chloride microcapsule, the raw material composition is as follows: 50% choline chloride; 25% silicon dioxide; 15% carnauba wax; 5% rice bran wax; 2.5% glucose phthalate; zinc oxide powder 2.5%.

[0067] Concrete preparation process is as follows:

[0068] (1) Get 500kg choline chloride, after pulverizing, mix homogeneously with 250kg silicon dioxide, obtain mixture I;

[0069] (2) Take 150kg of carnauba wax and put it in the reactor to melt, and keep it warm at a temperature of 20°C higher than its melting point; then mix the melted carnauba wax with mixture I, stir well, and spray into the frozen Freeze-drying at low temperature (8°C) in a chamber to obtain primary coated particles;

[0070] (3) 50kg of rice bran wax and 25kg of glucose phthalate are dissolved in 500L of 75% (volume fraction) ethanol solution, and then 25kg of zinc oxide powder is added to obtain mixed solution II; In the fluidized bed, spray the mixed solution II simultaneous...

Embodiment 3

[0073] A rumen-passed choline chloride microcapsule, the raw material composition is as follows: 75% choline chloride; 10% silicon dioxide; 5% carnauba wax; 5% rice bran wax; 2.5% glucose phthalate; zinc oxide powder 2.5%.

[0074] Concrete preparation process is as follows:

[0075] (1) Get 750kg choline chloride, after pulverizing, mix homogeneously with 100kg silicon dioxide, obtain mixture I;

[0076] (2) Take 50kg of carnauba wax and put it in the reactor to melt, and keep it warm at a temperature of 20°C higher than its melting point; then mix the melted carnauba wax with mixture I, stir well, and spray into the frozen Freeze-drying at low temperature (8°C) in a chamber to obtain primary coated particles;

[0077] (3) 50kg of rice bran wax and 25kg of glucose phthalate are dissolved in 500L of 75% (volume fraction) ethanol solution, and then 25kg of zinc oxide powder is added to obtain mixed solution II; In the fluidized bed, spray mixed solution II at the same time, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rumen-passed choline chloride microcapsule and a preparation method thereof. The microcapsule comprises a core material composed of choline chloride and a carrier, an inner coating and an outer coating, and the inner coating The raw materials include one or more vegetable fats whose melting point is higher than 60°C; the raw materials of the outer coating include rice bran wax, zinc oxide powder and film-forming materials; the film-forming materials are glucose phthalate, poly Ethylene glycol or sodium alginate; the content of the rice bran wax is 5-10%, and the mass ratio of rice bran wax, zinc oxide powder and film-forming material is 1-5:0.1-1:0.1-1. The present invention adopts rice bran wax, zinc oxide powder and film-forming material as the raw materials of the outer coating, which not only significantly improves the rumen-passing rate of the rumen-passing choline chloride microcapsules in the rumen of ruminants and the release rate in the small intestine, It also reduces the hygroscopicity of the product during storage and use, thereby effectively improving the utilization efficiency of ruminants to choline chloride.

Description

technical field [0001] The invention relates to the technical field of feed additives, in particular to a rumen-passed choline chloride microcapsule and a preparation method thereof. Background technique [0002] Choline is a B vitamin with the chemical name hydroxyethyltrimethylamine. It has many biological functions, including: a component of phospholipids, which participates in the formation of lecithin and sphingomyelin, etc.; an unstable methyl group donor; plays an important role in regulating liver fat metabolism; and is the main component of the synthesis of acetylcholine. At present, choline has been used as a feed additive for pigs, poultry complete feed and ruminant concentrate. Enhance the physical fitness and disease resistance of livestock and poultry. [0003] Choline is a colorless liquid at room temperature, hygroscopic, alkaline and viscous. Choline chloride is the hydrochloride salt of choline. The molecule has a polar tendency, and it is easy to absorb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K9/50A61K31/14A23K20/10A23K20/105A23K20/158A23K20/163A23K20/20A23K40/35
CPCA23K20/10A23K20/105A23K20/158A23K20/163A23K20/30A23K40/35A23K50/10A23K10/30A23K40/10A23K20/28
Inventor 徐二华李浙烽张倩云
Owner HANGZHOU KINGTECHINA FEED CO LTD