Unsaturated polyester material electrostatically sprayed at high temperature of 38 DEG C and gelatinized for 80 minutes

An electrostatic spraying, unsaturated technology, applied in the field of coatings, can solve the problems of short construction exchange time, poor adhesion, poor fullness, etc., and achieve the effects of long gelation time, easy sanding, and high fullness

Inactive Publication Date: 2019-03-08
CHENGDU ZHANCHEN PAINT
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of electrostatic spraying unsaturated polyester gelling material at a high temperature of 38°C for 80 minutes to solve the problem o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Formula: 38 parts of air-drying unsaturated polyester resin, 5 parts of adhesion promoter, 0.5 parts of anti-greening dispersant, polymerization inhibitor: 5% hydroquinone 0.5 parts, hardening agent: 2 parts, grinding aid: hardening agent 3 parts of zinc fatty acid, solvent: 3 parts of styrene, 1 part of ethanol, inorganic filler: 7 parts of transparent powder, 15 parts of titanium dioxide, 18 parts of calcium carbonate, 5 parts of talcum powder, anti-settling agent: 0.8 part of fumed silica, disinfectant Foaming agent: 0.1 part of acrylate polymer, leveling agent: 0.5 part of polyacrylate compound, rheological additive: 0.3 part, and 0.1 part of additive for increasing coating conductivity.

[0038] Production process: put air-drying unsaturated polyester resin into it → add adhesion promoter → add styrene, ethanol → stir evenly at low speed → add anti-greening dispersant, polymerization inhibitor, defoamer and leveling agent in sequence → middle Disperse at high speed...

Embodiment 2

[0041] Formula: 40 parts of air-drying unsaturated polyester resin, 4 parts of adhesion promoter, 0.5 parts of anti-greening dispersant, polymerization inhibitor: 5% hydroquinone 0.5 parts, hardening agent: 2 parts, grinding aid: hardening agent 2 parts of zinc fatty acid, solvent: 3 parts of styrene, 1 part of ethanol, inorganic filler: 6 parts of transparent powder, 14 parts of titanium dioxide, 22 parts of calcium carbonate, 5 parts of talcum powder, anti-settling agent: 0.8 part of fumed silica, disinfectant Foaming agent: 0.1 part of acrylate polymer, leveling agent: 0.5 part of polyacrylate compound, rheological additive: 0.3 part, and 0.1 part of additive for increasing coating conductivity.

[0042] Production process: put air-drying unsaturated polyester resin into it → add adhesion promoter → add styrene, ethanol → stir evenly at low speed → add anti-greening dispersant, polymerization inhibitor, defoamer and leveling agent in sequence → middle Disperse at high speed...

Embodiment 3

[0045] Formula: 4,3 parts of air-drying unsaturated polyester resin, 3 parts of adhesion promoter, 0.5 parts of anti-greening dispersant, polymerization inhibitor: 5% hydroquinone 0.5 parts, hardening agent: 2 parts, grinding aid : 2 parts of zinc stearate, solvent: 3 parts of styrene, 1 part of ethanol, inorganic filler: 3 parts of transparent powder, 15 parts of titanium dioxide, 22 parts of calcium carbonate, 2 parts of talcum powder, anti-settling agent: 0.8 part of fumed silica, Defoaming agent: 0.1 part of acrylate polymer, leveling agent: 0.5 part of polyacrylate compound, rheological additive: 0.3 part, and 0.1 part of additive for increasing coating conductivity.

[0046]Production process: put air-drying unsaturated polyester resin into it → add adhesion promoter → add styrene, ethanol → stir evenly at low speed → add anti-greening dispersant, polymerization inhibitor, defoamer and leveling agent in sequence → middle Disperse at high speed for 10 minutes → add fumed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface dry timeaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an unsaturated polyester material electrostatically sprayed at the high temperature of 38 DEG C and gelatinized for 80 minutes. The material comprises, by weight, 38-48 parts of unsaturated polyester resin, 1-3 parts of polishing aids, 35-55 parts of inorganic fillers, 3-6 parts of solvents, 1-2 parts of anti-settling agents, 1-2 parts of enhanced anti-settling rheologicalagents, 1-3 parts of hardening agents, 0.1-0.5 part of defoaming agent, 0.2-0.5 part of leveling agent, 0.1-0.2 part of conducting assistants, 0.5-0.7 part of polymerization inhibitor, 3-5 parts of adhesion promoters and 0.5-0.7 part of slow-drying anti-greening dispersing agent. The unsaturated polyester material has the advantages that the material is suitable for rotary-cup-type electrostatic spraying, and the paint utilization rate is increased; the gelatinization time reaches 80 minutes in an environment with the temperature of 38 DEG C, and performance and environmental protection requirements are met at the same time.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to an unsaturated polyester material which is electrostatically sprayed at a high temperature of 38°C and has a gelation time of 80 minutes. Background technique [0002] With the continuous advancement of science and technology, people pay more and more attention to environmental protection. The traditional manual spraying operation is gradually replaced by mechanical spraying, and electrostatic spraying has gradually become the mainstream. Because the rotating cup electrostatic spraying adopts cyclic operation to improve the utilization rate of paint, it has a high requirement for the gelation time of unsaturated polyester materials, which needs to reach 80 minutes at 38 ° C. The gelation time of ordinary unsaturated polyester materials Only about 30 minutes. [0003] Therefore, there is an urgent need in this field for a construction tolerance that can broaden the unsaturated...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/06C09D5/46C09D7/45C09D7/61C09D7/63
CPCC09D7/63C09D7/70C09D167/06C09D7/45C09D7/61C08K2201/011C08K2003/2227C08K2003/2241C08K2003/265C08K13/04C08K3/22C08K3/26C08K3/34C08K7/26
Inventor 兰春风麦冬李华君
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap