A kind of high thermal conductivity ultraviolet curing adhesive for optical fiber coil potting and preparation method thereof
An optical fiber coil, high thermal conductivity technology, used in adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of large temperature gradient and poor thermal conductivity, so as to improve thermal conductivity and improve thermal conductivity. , Improve the effect of full temperature stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0038] A method for preparing a high thermal conductivity ultraviolet light curing adhesive for potting an optical fiber coil, comprising the following steps:
[0039]Step 1: Mix epoxy acrylate prepolymer, urethane acrylate prepolymer, and acrylic reactive diluent, add to the reaction kettle, mix evenly at a certain speed, raise the temperature to 80°C, and keep it warm for 1.5 to 2.5 hours. Obtain a mixed prepolymer;
[0040] Step 2: Cool down the mixed prepolymer obtained in step 1 to 45°C, add thermally conductive fillers and additives, stir and mix evenly at a constant temperature of 45°C, and keep warm for 0.5-1.5h to obtain a doped prepolymer;
[0041] Step 3: Heat the doped prepolymer obtained in step 2 to 65°C, add a photoinitiator, a sensitizer and an adhesion promoter under the condition of avoiding light, stir and mix evenly at a constant temperature of 65°C, and cool down at 0.5°C / min Cool down to room temperature at a high rate to obtain a high thermal conductivi...
Embodiment 1
[0044] A method for preparing a high thermal conductivity UV-curable adhesive for optical fiber coil potting, which is specifically completed according to the following steps:
[0045] 1. By weight percentage, take respectively 28% of epoxy acrylate prepolymer, 40% of polyurethane acrylate prepolymer, 15% of acrylic reactive diluent, 3.9% of photoinitiator, 0.1% of sensitizer, and Concentration accelerator 7%, thermal conductivity filler 5%, auxiliary agent 1%;
[0046] The epoxy acrylate prepolymer described in step 1 is Corning 3215;
[0047] The polyurethane acrylate prepolymer described in step 1 is Cytec EB210;
[0048] The acrylic reactive diluent described in step 1 is triethoxylated trimethylolpropane triacrylate;
[0049] The photoinitiator described in step 1 is 2,4,6-trimethylbenzoyl-ethoxyl-phenylphosphine oxide;
[0050] The sensitizer described in step 1 is Doublecure EPD;
[0051] The adhesion promoter described in step 1 is gamma-(methacryloyloxy) propyltri...
Embodiment 2
[0058] A method for preparing a high thermal conductivity UV-curable adhesive for optical fiber coil potting, which is specifically completed according to the following steps:
[0059] 1. By weight percentage, respectively weigh 30% of epoxy acrylate prepolymer, 20% of polyurethane acrylate prepolymer, 26% of acrylic reactive diluent, 0.5% of photoinitiator, 0.5% of sensitizer, and Concentration accelerator 1%, thermal conductivity filler 20%, auxiliary agent 2%;
[0060] The epoxy acrylate prepolymer described in step 1 is Cytec EB6040;
[0061] The polyurethane acrylate prepolymer described in step 1 is Sartomer CN972;
[0062] The acrylic reactive diluent described in step 1 is glycidyl methacrylate;
[0063] The photoinitiator described in step 1 is α, α-diethoxyacetophenone;
[0064] The sensitizer described in step 1 is Doublecure 225;
[0065] The adhesion promoter described in step 1 is 2,3-epoxypropyl propyl trimethoxysilane;
[0066] The thermally conductive fil...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More