Bamboo carbon fiber phenolic resin composite material

A technology of bamboo carbon fiber and phenolic resin, which is applied in the field of resin materials, can solve the problems of poor material performance, difficulty in improving enterprise benefits, poor compatibility between bamboo carbon fiber and resin, and achieve improved agglomeration behavior, improved interface performance, The effect of improving mechanical properties

Inactive Publication Date: 2019-03-12
安徽省科晟生态木装饰材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, bamboo carbon fiber is often used to enhance the performance of resin materials, but due to the poor compatibility between bamboo carbon fiber and resin, the performance of the material is not good, and it is difficult to improve the benefits of enterprises.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of bamboo carbon fiber phenolic resin composite material, its raw material comprises by weight: 75 parts of phenolic resin, 60 parts of polyamide curing agent T31, 15 parts of modified bamboo carbon fiber, 10 parts of hydroxymethyl cellulose, N methyl acetamide 1 3 parts, AC foaming agent 3 parts, PVC foam regulator 3 parts, brominated polyethylene 2.5 parts, stearic acid 0.3 parts, talcum powder 3.5 parts, potassium hexatitanate whisker 1.2 parts.

Embodiment 2

[0020] A kind of bamboo carbon fiber phenolic resin composite material, its raw material comprises by weight: 87 parts of phenolic resins, 40 parts of polyamide curing agent T31, 25 parts of modified bamboo carbon fibers, 2 parts of hydroxymethyl cellulose, 7 parts of N methyl acetamide 1.5 parts of AC foaming agent, 9 parts of PVC foaming regulator, 1 part of brominated polyethylene, 1.6 parts of stearic acid, 0.4 parts of talcum powder, 3 parts of potassium hexatitanate whiskers;

[0021] Wherein, the preparation method of the modified bamboo carbon fiber is: taking carboxylated carbon nanotubes, bamboo carbon fiber and silica sol, mixing, ultrasonically stirring, vacuum drying, and grinding to obtain the modified bamboo carbon fiber.

Embodiment 3

[0023] A kind of bamboo carbon fiber phenolic resin composite material, its raw material comprises by weight: 80 parts of phenolic resins, 50 parts of polyamide curing agent T31, 20 parts of modified bamboo carbon fibers, 5 parts of hydroxymethyl cellulose, 5 parts of N methyl acetamide 2 parts, AC foaming agent 2 parts, PVC foaming regulator 5 parts, brominated polyethylene 1.5 parts, stearic acid 1 part, talcum powder 2 parts, potassium hexatitanate whisker 2 parts;

[0024] Wherein, the preparation method of the modified bamboo carbon fiber is: mix carboxylated carbon nanotubes, bamboo carbon fiber and silica sol according to the mass ratio of 0.4:1.5:3, stir ultrasonically at 150W for 1.5h, and vacuum dry at 130°C for 55min , grind to obtain modified bamboo carbon fiber;

[0025] The preparation method of the carboxylated carbon nanotubes is as follows: placing the carbon nanotubes in a mixed solution of nitric acid and sulfuric acid, stirring under reflux, cooling the ref...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of resin materials, in particular to a bamboo carbon fiber phenolic resin composite material. The bamboo carbon fiber phenolic resin composite material isprepared from the following raw materials in parts by weight: 75 to 87 parts of phenolic resin, 40 to 60 parts of polyamide curing agent T31, 15 to 25 parts of modified bamboo carbon fibers, 2 to 10 parts of hydroxymethyl cellulose, 1 to 7 parts of N-methyl acetamide, 1.5 to 3 parts of AC foaming agent, 3 to 9 parts of PVC foaming regulator, 1 to 2.5 parts of brominated polyethylene, 0.3 to 1.6 parts of stearic acid, 0.4 to 3.5 parts of talcum powder, and 1.2 to 3 parts of potassium hexatitanate whisker. The bamboo carbon fiber phenolic resin composite material is excellent in mechanical performance.

Description

technical field [0001] The invention relates to the technical field of resin materials, in particular to a bamboo carbon fiber phenolic resin composite material. Background technique [0002] Bamboo carbon fiber is made of moso bamboo as raw material, and adopts a new calcination process and new technology of pure oxygen high temperature and nitrogen barrier delay, which makes the micropores inherent in bamboo charcoal more refined and honeycombed, and then combined with the trend of honeycomb microporous structure It is made by melt spinning polyester modified chips. At present, bamboo carbon fiber is often used to enhance the performance of resin materials, but due to the poor compatibility of bamboo carbon fiber and resin, the performance of the material is not good, and it is difficult to improve the benefits of enterprises. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a bamboo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/06C08L77/00C08K9/02C08K7/06C08K7/08C08K3/34C08K5/09C08J9/10
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0085C08J9/009C08J9/0095C08J9/103C08J2203/04C08J2361/06C08J2477/00C08K3/34C08K5/09C08K7/06C08K7/08C08K9/02
Inventor 吴万水
Owner 安徽省科晟生态木装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com