Antibacterial TPU and PVC blended composite film and preparation method thereof

A composite film and blending technology, applied in the field of film, can solve the problems of easy falling off, easy water absorption and deterioration, poor environmental protection performance, etc., and achieve the effect of improving impact strength, good sterilization and antivirus effect, and improving weather resistance.

Inactive Publication Date: 2019-03-15
宁波鼎峰新材料科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the existing film has antibacterial properties, but the antibacterial time is short, it is easy to oxidize and lose, and it is easy to be stained with dust, easy to absorb water and deteriorate, low hardness, easy to damage, easy to fall off, and poor environmental protection performance
Traditional fungicides often contain toxic substances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The invention provides the following technical solutions: a composite film blended with antibacterial TPU and PVC, and the composite film blended with antibacterial TPU and PVC is prepared from the following raw materials in parts by weight:

[0037] TPU 300 parts

[0038] PVC 300 parts

[0039] Polylactic acid 20 parts

[0040] Hydroxypropyl Acrylate 50 parts

[0041] 15 parts of trifluoropropylmethyldichlorosilane

[0042] Vinyl triisopropoxysilane 15 parts

[0043] 8 parts hydroxypropyl methylcellulose

[0044] Chitosan 8 parts

[0045] 5 parts acetic acid

[0046] Eugenol 3 parts

[0047] 5 parts polyvinyl alcohol

[0048] Specifically, the raw materials also include emulsifiers, defoamers, initiators, deionized water and plasticizers.

[0049] Specifically, the plasticizer is an epoxy plasticizer.

[0050] Specifically, the initiator is potassium sulfate.

[0051] Specifically, the emulsifier is tristyrylphenol polyoxyethylene ether.

[0052] Specifical...

Embodiment 2

[0061] The invention provides the following technical solutions: a composite film blended with antibacterial TPU and PVC, and the composite film blended with antibacterial TPU and PVC is prepared from the following raw materials in parts by weight:

[0062] TPU 250 parts

[0063] PVC 250 parts

[0064] Polylactic acid 18 parts

[0065] 40 parts of hydroxypropyl acrylate

[0066] 10 parts of trifluoropropylmethyldichlorosilane

[0067] Vinyltriisopropoxysilane 10 parts

[0068] 2-8 parts of hydroxypropyl methylcellulose

[0069] Chitosan 6 parts

[0070] 2 parts acetic acid

[0071] Eugenol 2 parts

[0072] 3 parts polyvinyl alcohol

[0073] Specifically, the raw materials also include emulsifiers, defoamers, initiators, deionized water and plasticizers.

[0074] Specifically, the plasticizer is an epoxy plasticizer.

[0075] Specifically, the initiator is potassium sulfate.

[0076] Specifically, the emulsifier is tristyrylphenol polyoxyethylene ether.

[0077] Speci...

Embodiment 3

[0086] The invention provides the following technical solutions: a composite film blended with antibacterial TPU and PVC, and the composite film blended with antibacterial TPU and PVC is prepared from the following raw materials in parts by weight:

[0087] TPU 100 parts

[0088] PVC 100 parts

[0089] Polylactic acid 10 parts

[0090] 20 parts of hydroxypropyl acrylate

[0091] Trifluoropropylmethyldichlorosilane 2 parts

[0092] Vinyltriisopropoxysilane 3 parts

[0093] 2 parts hydroxypropyl methylcellulose

[0094] Chitosan 3 parts

[0095] 2 parts acetic acid

[0096] Eugenol 1 part

[0097] 2 parts polyvinyl alcohol

[0098] Specifically, the raw materials also include emulsifiers, defoamers, initiators, deionized water and plasticizers.

[0099] Specifically, the plasticizer is an epoxy plasticizer.

[0100] Specifically, the initiator is potassium sulfate.

[0101] Specifically, the emulsifier is tristyrylphenol polyoxyethylene ether.

[0102] Specifically, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of thin films and particularly discloses an antibacterial TPU (Thermoplastic Polyurethane) and PVC (Polyvinyl Chloride) blended composite film. The antibacterial TPU and PVC blended composite film is prepared from raw materials of the TPU, the PVC, polylactic acid, hydroxypropyl methacrylate, trifluoropropylmethyldichlorosilane and the like. A preparation method of the antibacterial TPU and PVC blended composite film comprises the following steps: firstly, mixing the TPU with the PVC and mixing; secondly, heating the molten mixture obtained in the first step and plasticizing until complete plasticizing is finished; thirdly, filtering the completely-plasticized mixture, removing impurities and the like. The antibacterial TPU and PVC blended composite film prepared with the preparation method disclosed by the invention has better sterilization and antibacterial effects and longer service life; by using TPU and PVC blended modified composite fabric, the two substance are blended to fully realize respective characteristics. The weather resistance, wear resistance, oil resistance, chemical resistance, low temperature resistance and bonding characteristics with other resin of the PVC can be improved by using the TPU to modify the PVC, and further the impact strength of the PVC is improved.

Description

technical field [0001] The invention belongs to the technical field of thin films, and in particular relates to a composite film blended with antibacterial TPU and PVC and a preparation method thereof. Background technique [0002] TPU film is a film made by special processes such as calendering, casting, film blowing and coating on the basis of TPU pellets. Thickness 0.01 to 2mm. [0003] TPU, thermoplastic TPU elastomer, due to its good elasticity, good physical properties, and various mechanical strengths, it is widely used in processing methods such as injection, extrusion, calendering, and dissolving into solution resins. It is often used by plastic processing industry Plastic materials, the products made of which cover the range of industrial applications and civil necessities. [0004] PVC film. The main ingredient is polyvinyl chloride, and other ingredients are added to enhance its heat resistance, toughness, ductility, etc. The top layer of this surface film is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/04C08L27/06C08L67/04C08L33/14C08L1/28C08L5/08C08K5/09C08K5/13C08J5/18C08F220/20C08F230/08C08F2/30
CPCC08F2/30C08F220/20C08J5/18C08J2327/06C08J2375/04C08J2401/28C08J2405/08C08J2427/06C08J2443/04C08J2467/04C08J2475/04C08K5/09C08K5/13C08F230/08
Inventor 惠建平
Owner 宁波鼎峰新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com