Charged ceramic membrane and preparation method thereof

A ceramic membrane and charging technology, applied in the field of ceramic materials, can solve the problems of harsh preparation process and high cost, and achieve the effect of reducing sintering temperature and energy consumption

Active Publication Date: 2021-10-29
萍乡市普天高科实业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of charged ceramic membrane still has problems such as high cost and harsh preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The invention provides a charged ceramic membrane, which composition includes the following components in parts by weight: 50 parts of cordierite (wherein 10 wt% is nano cordierite), 10 parts of silicon carbide, 3 parts of α-alumina, 1 part of neodymium oxide parts, 3 parts of titanium oxide, 5 parts of polyethyleneimine, 20 parts of polyvinyl alcohol, 0.1 part of chitosan, and the film thickness is 5 μm.

[0026] The preparation method of the above-mentioned charged ceramic membrane comprises the following steps:

[0027] S1. In addition to preparing all the film layer slurry of the charging agent, 90wt% (mass percentage) of the above raw materials is used to prepare the ceramic membrane support body slurry, and 10wt% is used to prepare the film layer slurry;

[0028] S2. Preparation of ceramic membrane support slurry: take cordierite, silicon carbide, α-alumina, neodymium oxide, and titanium oxide and mix them in proportion and put them into a ball mill for ball milli...

Embodiment 2

[0036] The invention provides a charged ceramic membrane, which composition includes the following components in parts by weight: 70 parts of cordierite (20 wt% of which is nano cordierite), 15 parts of silicon carbide, 6 parts of α-alumina, 3 parts of neodymium oxide 1 part, 5 parts of titanium oxide, 10 parts of polyethyleneimine, 30 parts of polyvinyl alcohol, 1 part of yeast dextran, and the thickness of the film layer is 8 μm.

[0037] The preparation method of the above-mentioned charged ceramic membrane comprises the following steps:

[0038] S1. In addition to preparing all the film layer slurry of the charging agent, 90wt% (mass percentage) of the above raw materials is used to prepare the ceramic membrane support body slurry, and 10wt% is used to prepare the film layer slurry;

[0039]S2. Preparation of ceramic membrane support slurry: take cordierite, silicon carbide, α-alumina, neodymium oxide, and titanium oxide and mix them in proportion, put them into a ball mil...

Embodiment 3

[0047] The invention provides a charged ceramic membrane, which composition includes the following components in parts by weight: 60 parts of cordierite (15 wt% of which is nano cordierite), 12 parts of silicon carbide, 5 parts of α-alumina, 2 parts of neodymium oxide parts, 4 parts of titanium oxide, 8 parts of polyethyleneimine, 25 parts of polyvinyl alcohol, 0.5 parts of zirconia, and the film thickness is 3 μm.

[0048] The preparation method of the above-mentioned charged ceramic membrane comprises the following steps:

[0049] S1. In addition to preparing all the film layer slurry of the charging agent, 90wt% (mass percentage) of the above raw materials is used to prepare the ceramic membrane support body slurry, and 10wt% is used to prepare the film layer slurry;

[0050] S2. Preparation of ceramic membrane support slurry: take cordierite, silicon carbide, α-alumina, neodymium oxide, and titanium oxide in proportion and mix them in a ball mill for 28 hours, then add pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
strengthaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a charged ceramic membrane, which comprises the following components in parts by weight: 50-70 parts of cordierite, 10-15 parts of silicon carbide, 3-6 parts of α-alumina, and 1-3 parts of neodymium oxide 3-5 parts of titanium oxide, 5-10 parts of polyethyleneimine, 20-30 parts of polyvinyl alcohol, and 0.1-1 part of charging agent. The above-mentioned charged ceramic membrane is prepared by isostatic pressing method and dipping method. Through the proportion of each component and the temperature control at each stage of sintering, and by adding α-alumina, neodymium oxide, titanium oxide, etc. to reduce the sintering temperature, improve the bonding strength of cordierite and silicon carbide, and form a double-layer pore structure to obtain high Strong support body and membrane layer, the porosity of the prepared charged ceramic membrane can reach 45%, and the strength can reach 20MPa.

Description

technical field [0001] The invention relates to a ceramic material, in particular to a charged ceramic membrane and a preparation method thereof. Background technique [0002] Ceramic membrane is a kind of inorganic membrane, which belongs to the solid membrane material in membrane separation technology. Fired. The ceramic membrane for separation usually has a three-layer structure: a support body (also known as a carrier layer), a transition layer (also known as an intermediate layer), and a membrane layer (also known as a separation layer). The function of the support layer is to increase the mechanical strength of the membrane; the intermediate layer The pore diameter of the layer is smaller than that of the support layer, and its function is to prevent the particles from penetrating into the porous support layer during the preparation of the membrane layer; the membrane layer has a separation function. The pore size distribution of the entire membrane gradually decreas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/195C04B35/622C04B35/64
CPCC04B35/195C04B35/62218C04B35/64C04B2235/3217C04B2235/3224C04B2235/3225C04B2235/3232C04B2235/3244C04B2235/3826C04B2235/6562C04B2235/6567C04B2235/661C04B2235/96
Inventor 刘绍辉黄乃乔袁明辉
Owner 萍乡市普天高科实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More