Bamboo carbon fiber reinforced resin material

A technology of bamboo carbon fiber and reinforced resin, applied in the field of resin materials, can solve the problems of poor compatibility between bamboo carbon fiber and resin, poor material performance, etc., and achieves improvement of agglomeration behavior, improvement of interface properties, and improvement of transverse tensile strength. Effect

Inactive Publication Date: 2019-03-29
安徽省科晟生态木装饰材料有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, bamboo carbon fiber is often used to enhance the performance of resin materials, but due to the poor compatibility between bamboo carbon fiber and resin, the performance of the material is not good, and it is difficult to meet the market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A bamboo carbon fiber reinforced resin material, its raw materials include by weight: 70 parts of polyvinyl chloride resin, 55 parts of light calcium carbonate, 10 parts of modified bamboo carbon fiber, 15 parts of bamboo fiber, 3 parts of calcium zinc stabilizer, AC hair 2.5 parts of foaming agent, 5 parts of PVC foam regulator, 2 parts of polyethylene wax, 0.2 parts of stearic acid, 1.3 parts of environmental toughening agent, 1 part of rutile titanium dioxide, 4.5 parts of wood fiber.

Embodiment 2

[0020] A bamboo carbon fiber reinforced resin material, its raw materials include by weight: 85 parts of polyvinyl chloride resin, 45 parts of light calcium carbonate, 20 parts of modified bamboo carbon fiber, 5 parts of bamboo fiber, 8 parts of calcium zinc stabilizer, AC hair 1 part of foaming agent, 13 parts of PVC foam regulator, 0.5 parts of polyethylene wax, 1.5 parts of stearic acid, 0.2 parts of environmental toughening agent, 2.5 parts of rutile titanium dioxide, 2 parts of wood fiber;

[0021] Wherein, the preparation method of the modified bamboo carbon fiber is: taking carboxylated carbon nanotubes, bamboo carbon fiber and silica sol, mixing, ultrasonically stirring, vacuum drying, and grinding to obtain the modified bamboo carbon fiber.

Embodiment 3

[0023] A bamboo carbon fiber reinforced resin material, its raw materials include by weight: 75 parts of polyvinyl chloride resin, 50 parts of light calcium carbonate, 15 parts of modified bamboo carbon fiber, 10 parts of bamboo fiber, 5.5 parts of calcium zinc stabilizer, AC hair 1.8 parts of foaming agent, 6.3 parts of PVC foam regulator, 0.8 parts of polyethylene wax, 0.6 parts of stearic acid, 0.6 parts of environmental toughening agent, 1.8 parts of rutile titanium dioxide, 3.7 parts of wood fiber;

[0024] Wherein, the preparation method of the modified bamboo carbon fiber is: take carboxylated carbon nanotubes, bamboo carbon fiber and silica sol, mix, ultrasonically stir, vacuum dry, grind, obtain modified bamboo carbon fiber;

[0025] The mass ratio of the carboxylated carbon nanotubes, bamboo carbon fibers and silica sol is 0.5:1.3:2.5;

[0026] The power of the ultrasonic stirring is 140W, and the time is 2h;

[0027] The temperature of the vacuum drying is 130° C.,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of resin materials, in particular to a bamboo carbon fiber reinforced resin material. The bamboo carbon fiber reinforced resin material comprises the following raw materials by weight: 70-85 parts of polyvinyl chloride resin, 45-55 parts of light calcium carbonate, 10-20 parts of modified bamboo carbon fiber, 5-15 parts of bamboo fiber, 3-8 parts of a calcium-zinc stabilizer, 1-2.5 parts of an AC foaming agent, 5-13 parts of a PVC foaming regulator, 0.5-2 parts of polyethylene wax, 0.2-1.5 parts of stearic acid, 0.2-1.3 parts of an environment-friendly toughening agent, 1-2.5 parts of rutile titanium dioxide, and 2-4.5 parts of wood fiber. The bamboo carbon fiber reinforced resin material provided by the invention has excellent mechanical properties.

Description

technical field [0001] The invention relates to the technical field of resin materials, in particular to a bamboo carbon fiber reinforced resin material. Background technique [0002] Bamboo carbon fiber is made of moso bamboo as raw material, and adopts a new calcination process and new technology of pure oxygen high temperature and nitrogen barrier delay, which makes the micropores inherent in bamboo charcoal more refined and honeycombed, and then combined with the trend of honeycomb microporous structure It is made by melt spinning polyester modified chips. This unique fiber structure design has the characteristics of moisture absorption and breathability, antibacterial and antibacterial, warm in winter and cool in summer, green and environmentally friendly. [0003] At present, bamboo carbon fiber is often used to enhance the performance of resin materials, but due to the poor compatibility of bamboo carbon fiber and resin, the performance of the material is not good, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L67/00C08L97/02C08K13/06C08K3/04C08K7/24C08K3/26C08K5/09C08K3/22C08K3/36C08J9/10C08J5/06
CPCC08J5/06C08J9/103C08J2203/04C08J2327/06C08J2467/00C08J2497/02C08K3/041C08K3/36C08K5/09C08K7/24C08K13/06C08K2003/2241C08K2003/265C08K2201/011
Inventor 吴万水
Owner 安徽省科晟生态木装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com