Method for preparing rare-earth-doped manganese-zinc ferrite material

A manganese zinc ferrite, rare earth doping technology, applied in the field of magnetic materials, can solve the problem of unsatisfactory magnetic permeability

Inactive Publication Date: 2019-04-02
ZHONGDE ELECTRONICS
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The magnetic permeability of the soft ferrite in the prior art cannot meet the needs of the prior art, so it is urgent to design a soft ferrite material with high magnetic permeability to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing rare-earth-doped manganese-zinc ferrite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method of a rare earth-doped manganese-zinc ferrite material, comprising the steps of:

[0023] S1, adding the main components of manganese oxide, zinc oxide, and iron oxide into a ball mill for ball milling to obtain a mixture A; wherein the molar ratio of manganese oxide, zinc oxide, and iron oxide is 35:55:9;

[0024] S2, pre-calcining the mixture A, and then cooling to room temperature to obtain a pre-calcined material;

[0025] S3. Add calcined material, vanadium oxide, niobium pentoxide, bismuth oxide, molybdenum oxide, phosphorus pentoxide, copper oxide, and composite rare earth additives into a ball mill for secondary ball milling, and dry to obtain mixture B; the composite rare earth The additive is composed of cerium oxide, yttrium oxide and lanthanum oxide;

[0026] S4, add polyvinyl alcohol solution to mixing granulation in mixture B, then pass through 40 mesh sieves, obtain granular material; The mass ratio of mixture B and polyvinyl alcohol ...

Embodiment 2

[0030] A preparation method of a rare earth-doped manganese-zinc ferrite material, comprising the steps of:

[0031] S1, adding the main components of manganese oxide, zinc oxide, and iron oxide into a ball mill for ball milling to obtain a mixture A; wherein the molar ratio of manganese oxide, zinc oxide, and iron oxide is 37:53:11;

[0032] S2, pre-calcining the mixture A, and then cooling to room temperature to obtain a pre-calcined material;

[0033] S3. Add calcined material, vanadium oxide, niobium pentoxide, bismuth oxide, molybdenum oxide, phosphorus pentoxide, copper oxide, and composite rare earth additives into a ball mill for secondary ball milling, and dry to obtain mixture B; the composite rare earth The additive is composed of cerium oxide, yttrium oxide and lanthanum oxide;

[0034] S4, add polyvinyl alcohol solution to mixing granulation in mixture B, then pass 80 mesh sieves, obtain granular material; The mass ratio of mixture B and polyvinyl alcohol solutio...

Embodiment 3

[0038] A preparation method of a rare earth-doped manganese-zinc ferrite material, comprising the steps of:

[0039] S1. Add the main components of manganese oxide, zinc oxide, and iron oxide into a ball mill for ball milling to obtain mixture A; wherein the molar ratio of manganese oxide, zinc oxide, and iron oxide is 35:55:9; the ball mill speed is 150r / min, and the ball milling time for 6h;

[0040] S2. Pre-calcining the mixture A, and then cooling to room temperature to obtain a pre-calcining material; the pre-calcining temperature is 860° C., and the pre-calcining time is 90 minutes;

[0041] S3. Add pre-fired material, vanadium oxide, niobium pentoxide, bismuth oxide, molybdenum oxide, phosphorus pentoxide, copper oxide, and composite rare earth additives into a ball mill for secondary ball milling, and dry to obtain mixture B; pre-fired material, The mass ratio of vanadium oxide, niobium pentoxide, bismuth oxide, molybdenum oxide, phosphorus pentoxide, copper oxide, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of magnetic materials, and discloses a method for preparing a rare-earth-doped manganese-zinc ferrite material, comprising the steps of adding manganese oxide, zinc oxide and iron oxide as main components to a ball mill and conducting ball milling to obtain a mixture A; pre-firing the mixture A, and then conducting cooling to room temperature to obtaina pre-fired material; adding the pre-sintered material, vanadium oxide, niobium oxide, bismuth trioxide, molybdenum oxide, phosphorus pentoxide, copper oxide and a composite rare earth additive into aball mill, and conducting secondary ball milling and drying to obtain a mixture B, wherein the composite rare earth additive is composed of cerium oxide, yttrium oxide and lanthanum oxide; adding a polyvinyl alcohol solution to the mixture B, conducting mixing and granulation, and then conducting sieving by a sieve of 40-80 mesh, so as to obtain pellets; adding the pellets into a molding machinefor pressing, so as to obtain a blank; and sintering the blank and conducting cooling. The rare-earth-doped manganese-zinc ferrite material prepared by the method of the invention has high initial magnetic conductivity and saturation magnetic flux density.

Description

technical field [0001] The invention relates to the technical field of magnetic materials, in particular to a preparation method of a rare earth-doped manganese-zinc ferrite material. Background technique [0002] The application of soft magnetic materials in industry began at the end of the 19th century, with the rise of electric power and telecommunication technology, and its application range is extremely wide. Soft magnetic materials are not only used in the fields of home appliances, information technology, automobiles and other supporting fields, but more importantly, soft magnetic materials, as the main raw materials for the production of electronic components, have brought a steady stream of demand for them. With the development of the electronics industry and the expansion of application fields, the requirements for magnetic materials are also getting higher and higher. The magnetic permeability of the soft ferrite in the prior art cannot meet the requirements of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/26C04B35/622C04B35/626C04B35/634
CPCC04B35/2658C04B35/622C04B35/62605C04B35/63416C04B2235/3225C04B2235/3227C04B2235/3229C04B2235/3239C04B2235/3251C04B2235/3256C04B2235/3281C04B2235/3298C04B2235/34
Inventor 瞿德林王久如李丛俊
Owner ZHONGDE ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com