Aging-resistant rubber belt track

A rubber crawler and anti-aging technology, which is applied in the field of rubber materials and its preparation, can solve the problems of insufficient strength, aging and aging performance of the rubber crawler.

Inactive Publication Date: 2019-05-07
XCMG CONSTR MACHINERY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the rubber track currently used is prone to aging phenomenon earlier, resulting in insufficient strength of the track in the later use process, unable to meet the requirements of the carrying capacity and service life of construction machinery
[0003] At present, domestic research on the anti-aging performance of rubber tracks mainly improves the aging performance of rubber tracks by adding accelerators,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aging-resistant rubber belt track

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of described aging-resistant rubber track is as follows:

[0035] step one:

[0036] Preparation of ingredients: Prepare accelerators AZ and / or BZ, magnesium oxide, anti-scorch agent, silane coupling agent, stearic acid, low-density naphthenic oil and other compounding ingredients, crush and dry, sieve, weigh and put in according to the proportion Stir well in the container.

[0037] Step two:

[0038] Initial mixing: Set the speed ratio of the front and rear rollers of the open mill to 1:1.3, adjust the roll distance of the open mill to 1mm, add raw rubber for mastication, and add the ingredients in step 1 to continue mixing after the plasticization is completed.

[0039] Step three:

[0040] Mixing: Adjust the roller distance of the open mill to 0.8mm, and then mix the rubber after the initial mixing with calcium carbonate, flame retardant, and light stabilizer; after the mixing is completed, add carbon black, The ultra-fine activated clay i...

Embodiment 1

[0044] A kind of aging-resistant rubber track provided by the present embodiment, described aging-resistant rubber track comprises the following raw materials in parts by weight: 60 parts of EPDM rubber, 40 parts of neoprene rubber, 1 part each of accelerator BZ and TMTD, 3.5 parts of magnesium oxide, 4 parts of zinc oxide, 2 parts of antioxidant NBC, NMB, DFC-34, 40 parts of carbon black N550, 1 part of anti-scorch agent PVI, 1 part of silane coupling agent kh550, 1 part of stearic acid, 3 parts of low-density naphthenic oil, 15 parts of superfine activated clay, 4 parts of calcium carbonate, 1 part of light stabilizer PDS, 1 part of antimony trioxide, and 1 part of chlorinated paraffin.

[0045] step one:

[0046] Preparation of ingredients: Prepare accelerator BZ, magnesium oxide, anti-aging agent NBC, NMB, DFC-34, anti-scorch agent PVI, silane coupling agent kh550, stearic acid, low-density naphthenic oil and other compounding ingredients, crush and dry Sieve, weigh in pr...

Embodiment 2

[0054] A kind of aging-resistant rubber crawler provided by the present embodiment, described aging-resistant rubber crawler comprises the raw material of following parts by weight: EPDM rubber 60 parts, butadiene rubber 40 parts, accelerator AZ and TMTD each 1.5 parts, 4 parts of magnesium oxide, 4 parts of zinc oxide, 2.5 parts of antioxidant NMB, DFC-34, and CMA each, 50 parts of carbon black N770, 1.5 parts of anti-scorch agent PVI, 2 parts of silane coupling agent kh5502, 1.5 parts of stearic acid, low 3.5 parts of density naphthenic oil, 16 parts of superfine activated clay, 3.5 parts of calcium carbonate, 1.5 parts of light stabilizer PDS, 1.5 parts of antimony trioxide and 1.5 parts of decabromodiphenyl ether.

[0055] step one:

[0056] Preparation of ingredients: prepare accelerator AZ, magnesium oxide, anti-aging agent NMB, DFC-34, CMA, anti-scorch agent PVI, silane coupling agent kh550, stearic acid, low-density naphthenic oil and other compounding ingredients, cru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aging-resistant rubber belt track. Raw materials comprise rubber, accelerant, magnesium oxide, zinc oxide, an anti-aging agent, carbon black, a silane coupling agent kh550,scorch retarder PVI, stearic acid, low-density naphthenic oil, superfine active clay, calcium carbonate, a light stabilizer and a fire retardant, and the aging-resistant rubber belt track is producedthrough initial mixing, mixing, packing and batch-out. Through different rubber components, by adding the anti-aging agent, the scorch retarder, the fire retardant, the carbon black, the superfine active clay, the light stabilizer and the like, the aging-resistant performance and the intensity of the rubber are improved, and the service life of the rubber is prolonged; and the accelerant, the magnesium oxide, the zinc oxide, the silane coupling agent kh550 and the like are adopted for promoting a vulcanization process of the rubber, so that vulcanization of the rubber is fuller.

Description

technical field [0001] The invention relates to a rubber material and a preparation method thereof, in particular to an aging-resistant rubber track and a preparation method thereof. Background technique [0002] The rubber track is an endless belt made of rubber and metal or fiber materials. It has the characteristics of no damage to the road surface, small grounding specific pressure, good wet ground passability, small vibration, low noise, fast speed, reduced weight of the whole machine, and good corrosion resistance. Advantages, it has a very wide range of uses in tracked vehicles, and its application proportion in construction machinery, construction machinery, agricultural machinery, and garden machinery continues to increase. However, the rubber track currently used is prone to aging phenomenon earlier, which leads to insufficient strength of the track in the later use process, and cannot meet the requirements of the carrying capacity and service life of construction ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L11/00C08L9/00C08L91/00C08L91/06C08K13/06C08K9/06C08K3/22C08K3/04C08K5/09C08K3/34C08K3/26
Inventor 朱鹏霄李毅陈波
Owner XCMG CONSTR MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap