A colored glaze carved glass vase and its manufacturing method

A glass and vase technology, applied in glass manufacturing equipment, manufacturing tools, glass blowing, etc., can solve the problems of insufficient strength and general texture, etc., and achieve the improvement of ultraviolet and infrared absorption capacity, saving manufacturing cost, and good absorption capacity Effect

Active Publication Date: 2019-09-13
XINYI XINAODE GLASS PROD LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with this glass vase is that the texture is average and the strength is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A colored glaze carved glass vase and its manufacturing method
  • A colored glaze carved glass vase and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The glazed carved glass vase is made of glass and glaze. The glass is made of the following raw materials in parts by weight: 41 parts of lead-free cullet, 42 parts of quartz sand, 5 parts of sodium carbonate, 6 parts of albite, 3 parts of calcite, 0.5 parts of sodium sulfate, 2.5 parts of sodium fluorosilicate, 0.5 parts of gadolinium-dysprosium composite sulfide coated with silica, and 0.5 parts of vanadium oxide.

[0030] The manufacturing method of the present embodiment comprises the following steps:

[0031] A1. Mix gadolinium sulfide, dysprosium chloride, water, and citric acid, stir evenly to obtain a paste, dry it, grind it and put it into a crucible, place the crucible in a microwave oven, and react for 25 minutes under the condition of microwave power of 700W. Obtain gadolinium-dysprosium composite sulfide after taking out, the weight ratio of gadolinium sulfide, dysprosium chloride, water, citric acid is 3:2:50:20;

[0032] A2. Add gadolinium-dysprosium com...

Embodiment 2

[0039] The glazed carved glass vase is made of glass and glaze. The glass is made of the following raw materials in parts by weight: 40 parts of lead-free cullet, 43 parts of quartz sand, 5 parts of sodium carbonate, 6 parts of albite, 3 parts of calcite, 0.5 parts of sodium sulfate, 2.5 parts of sodium fluorosilicate, 0.5 parts of gadolinium-dysprosium composite sulfide coated with silica, and 0.5 parts of vanadium oxide.

[0040] The manufacturing method of the present embodiment comprises the following steps:

[0041] A1. Mix gadolinium sulfide, dysprosium chloride, water, and citric acid, stir evenly to obtain a paste, dry it, grind it and put it into a crucible, place the crucible in a microwave oven, and react for 25 minutes under the microwave power of 700W. Obtain gadolinium-dysprosium composite sulfide after taking out, the weight ratio of gadolinium sulfide, dysprosium chloride, water, citric acid is 3:2:50:20;

[0042] A2. Add gadolinium-dysprosium complex sulfide ...

Embodiment 3

[0049] The glazed carved glass vase is made of glass and glaze. The glass is made of the following raw materials in parts by weight: 42 parts of lead-free cullet, 41 parts of quartz sand, 5 parts of sodium carbonate, 6 parts of albite, 3 parts of calcite, 0.5 parts of sodium sulfate, 2.5 parts of sodium fluorosilicate, 0.5 parts of gadolinium-dysprosium composite sulfide coated with silica, and 0.5 parts of vanadium oxide.

[0050] The manufacturing method of the present embodiment comprises the following steps:

[0051] A1. Mix gadolinium sulfide, dysprosium chloride, water, and citric acid, stir evenly to obtain a paste, dry it, grind it and put it into a crucible, place the crucible in a microwave oven, and react for 25 minutes under the condition of microwave power of 700W. Obtain gadolinium-dysprosium composite sulfide after taking out, the weight ratio of gadolinium sulfide, dysprosium chloride, water, citric acid is 3:2:50:20;

[0052] A2. Add gadolinium-dysprosium com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a colored glaze engraved glass vase, which is prepared from glass and colored glaze, wherein the glass is prepared from the following raw materials in parts by weight: 40 to 42parts of lead-free broken glass, 41 to 43 parts of quartz sand, 5 parts of sodium carbonate, 6 parts of sodium feldspar, 3 parts of calcite, 0.5 part of sodium sulfate, 2.5 parts of sodium fluosilicate, 0.5 part of silicon dioxide coated gadolinium dysprosium composite sulfides and 0.5 part of vanadium oxide. The invention also provides a manufacturing method of the colored glaze engraved glass vase. The colored glaze engraved glass vase provided by the invention integrates the pattern engraving and the colored glaze, and the texture and the intensity are both good.

Description

technical field [0001] The invention relates to a glass vase, in particular to a colored glaze carved glass vase and a manufacturing method thereof. Background technique [0002] Glass products are a general term for daily necessities and industrial products processed with glass as the main raw material. Glass products are widely used in construction, daily use, medical treatment, chemistry, home furnishing, electronics, instrumentation, nuclear engineering and other fields. Glass vases are an important part of life A very common glass product. Traditional glass vases have a single format, smooth outer surface, and poor aesthetics. Although the current glass vases are carved with various patterns on the surface, glass vases with carved patterns can be seen everywhere, and most of their styles are similar. , the attractiveness is gradually reduced, unable to meet people's needs. [0003] The patent application number CN 201610240589.1 discloses "a glass vase with spots", whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C3/112C03B5/02C03B9/00C03B25/02C03C17/02
CPCY02P40/50
Inventor 孙鸿志
Owner XINYI XINAODE GLASS PROD LTD