High-shielding UV treatment agent and treatment process thereof

A covering and treatment agent technology, applied in coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve the problems of uneven surface coating roughness, inconvenient construction, poor recoating effect, etc., and achieve improved Cross-link density and hiding properties, fast curing speed, and the effect of improving flexibility

Inactive Publication Date: 2019-05-28
陈建平
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a high-covering UV treatment agent and its treatment process, and the product processed by its formula and treatment process has high covering properties, high wear resistance, easy recoating, and surface-drying speed Fast, fast curing speed and fast film-forming speed, etc., the coating surface after recoating will not appear the problems of bottoming, bleeding and poor bonding force, and the coating surface after its treatment has high smoothness and gloss It solves the problems of uneven roughness, poor hiding, poor recoating effect, inconvenient construction and low yield rate of the surface coating of products treated with conventional UV treatment agents. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-shielding UV treatment agent and treatment process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] A high-covering UV treatment agent, which includes the following components by weight ratio:

[0070] Specially modified acrylate 17.2%,

[0071] Urethane acrylate 16%,

[0072] Polyester Acrylate 5%,

[0073] Modified silica 0.3%,

[0074] TMP3EOTA 2%,

[0075] HDDA 6%,

[0076] Ciba184 0.2%,

[0077] TPO 0.3%,

[0078] BASF819 0.2%,

[0079] Leveling agent 0.8%,

[0080] Ethylene glycol butyl ether 6%,

[0081] Toluene 7%,

[0082] Isopropanol 13%,

[0083] Ethyl acetate 17%,

[0084] Butyl acetate 7%,

[0085] Silicone leveling agent 2%.

[0086] In one embodiment, the TMP3EOTA is ethoxylated trimethylolpropane triacrylate.

[0087] In one embodiment, the HDDA is 1,6-hexanediol diacrylate.

[0088] In one embodiment, the Ciba184 is 1-hydroxycyclohexyl phenyl ketone.

[0089] In one embodiment, the TPO is 2, 4, 6 trimethylbenzoyl-diphenylphosphine oxide.

Embodiment 2

[0091] A high-covering UV treatment agent, which includes the following components by weight ratio:

[0092] Specially modified acrylate 20.8%,

[0093] Urethane acrylate 17%,

[0094] Polyester Acrylate 4%,

[0095] Modified silica 0.3%,

[0096] TMP3EOTA 3%,

[0097] HDDA 8%,

[0098] Ciba184 0.3%,

[0099] TPO 0.1%,

[0100] BASF819 0.4%,

[0101] Leveling agent 0.5%,

[0102] Ethylene glycol butyl ether 9%,

[0103] Toluene 6%,

[0104] Isopropanol 8%,

[0105] Ethyl acetate 16%,

[0106] Butyl acetate 6%,

[0107] Silicone leveling agent 0.6%.

[0108] In one embodiment, the TMP3EOTA is ethoxylated trimethylolpropane triacrylate.

[0109] In one embodiment, the HDDA is 1,6-hexanediol diacrylate.

[0110] In one embodiment, the Ciba184 is 1-hydroxycyclohexyl phenyl ketone.

[0111] In one embodiment, the TPO is 2, 4, 6 trimethylbenzoyl-diphenylphosphine oxide.

Embodiment 3

[0113] A high-covering UV treatment agent, which includes the following components by weight ratio:

[0114] Specially modified acrylate 15%,

[0115] Urethane acrylate 18%,

[0116] Polyester Acrylate 3%,

[0117] Modified silica 0.3%,

[0118] TMP3EOTA 4%,

[0119] HDDA 7%,

[0120] Ciba184 0.1%,

[0121] TPO 0.2%,

[0122] BASF819 0.3%,

[0123] Leveling agent 0.4%,

[0124] Ethylene glycol butyl ether 10%,

[0125] Toluene 6%,

[0126] Isopropanol 10%,

[0127] Ethyl acetate 18%,

[0128] Butyl acetate 7%,

[0129] Silicone leveling agent 0.7%.

[0130] In one embodiment, the TMP3EOTA is ethoxylated trimethylolpropane triacrylate.

[0131] In one embodiment, the HDDA is 1,6-hexanediol diacrylate.

[0132] In one embodiment, the Ciba184 is 1-hydroxycyclohexyl phenyl ketone.

[0133] In one embodiment, the TPO is 2, 4, 6 trimethylbenzoyl-diphenylphosphine oxide.

[0134] The high-coverage UV treatment agent prepared by the formula of the above-mentioned exampl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-shielding UV treatment agent and a treatment process thereof. The high-shielding UV treatment agent is prepared from special modified acrylic ester, urethane acrylate,polyester acrylate, modified silicon dioxide, TMP3EOTA, HDDA, Ciba184, TPO, BASF819, leveling agents, butyl cellosolve, methylbenzene, isopropanol, ethyl acetate, butyl acetate and organic silicon leveling agents. A product obtained by using the formula and being treated by the treatment process has the advantages of high shielding performance, high wear performance, easy re-coating, high surfacedrying speed, high curing speed, fast film forming and the like; the problems of bottom hinging, color seepage and poor combination power do not occur after the re-coating; the treated coating surfacehas high smoothness, high luster degree, good smoothness and high qualified product rate, and solves the problems of nonuniform roughness degree, poor shielding performance, poor re-coating effect, construction inconvenience, low qualification product rate and the like of the surface coating of a product treated by the existing conventional UV treatment agent.

Description

technical field [0001] The present invention relates to the field of coatings, in particular to a UV treatment agent suitable for covering mobile phone shells, automotive interior parts, and shells of some high-end cosmetics made of plastic substrates such as PC, ABS, and ABS+PC, and its UV treatment agent. Processing technology. Background technique [0002] With the increasing expansion of the mobile phone market, the application of mobile phone coatings is also increasing. However, the competition in all walks of life is becoming increasingly fierce. In addition to differences in functions, price has also become one of the main considerations. Therefore, PC, When plastic substrates such as ABS and ABS+PC are sprayed and processed, the yield rate becomes a key indicator that can reduce production costs. At present, the products molded by plastic substrates such as PC, ABS and ABS+PC have the disadvantages of uneven surface roughness, poor heat resistance and poor coating ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D167/06C09D7/63C09D7/62
Inventor 陈建平刘妍霞朱金辉
Owner 陈建平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap