Zirconium alloy coating with high burnup and long service life and preparation method of zirconium alloy coating

A zirconium alloy and coating technology is applied in the field of preparation of high fuel consumption and long-life zirconium alloy coatings, which can solve the problems of not being able to meet comprehensive performance requirements at the same time, and achieve the effects of saving preparation costs, improving compactness and achieving remarkable effects.

Active Publication Date: 2019-05-28
NUCLEAR POWER INSTITUTE OF CHINA
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a zirconium alloy coating for high fuel consumption and long service life and its preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium alloy coating with high burnup and long service life and preparation method of zirconium alloy coating
  • Zirconium alloy coating with high burnup and long service life and preparation method of zirconium alloy coating
  • Zirconium alloy coating with high burnup and long service life and preparation method of zirconium alloy coating

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0053] Example 1

[0054] A preparation method of a zirconium alloy coating with high burn-up and long-life period, including:

[0055] (1) Pre-treatment: Place the obtained zirconium alloy matrix material in an ultrasonic container and wash with carbon tetrachloride and acetone for 10-20 minutes respectively, then ultrasonically clean with deionized water for more than 10 minutes, and use deionized water in the final stage rinse. The cleaned pipe samples are dried in a vacuum drying oven, and the drying temperature does not exceed 50°C. Clamp the pre-processed sample on the turntable of the coating equipment.

[0056] (2) Ion cleaning: vacuum the vacuum chamber of the coating equipment, and the vacuum degree reaches 1×10 -3 After Pa is above, a certain flow of argon is then filled to maintain the pressure in the vacuum chamber at 0.1-5 Pa. The bias voltage is adjusted to above -1000V for about 10-20 minutes, and the surface of the zirconium alloy pipe is bombarded by a high-speed...

Example Embodiment

[0066] Example 2

[0067] A preparation method of a zirconium alloy coating with high burn-up and long-life period, including:

[0068] (1) Pre-treatment: Place the obtained zirconium alloy matrix material in an ultrasonic container and wash with carbon tetrachloride and acetone for 10-20 minutes respectively, then ultrasonically clean with deionized water for more than 10 minutes, and use deionized water in the final stage rinse. The cleaned pipe samples are dried in a vacuum drying oven, and the drying temperature does not exceed 50°C. Clamp the pre-processed sample on the turntable of the coating equipment.

[0069] (2) Ion cleaning: vacuum the vacuum chamber of the coating equipment, and the vacuum degree reaches 1×10 -3 After Pa is above, a certain flow of argon is then filled to maintain the pressure in the vacuum chamber at 0.1-5 Pa. The bias voltage is adjusted to above -1000V for about 10-20 minutes, and the surface of the zirconium alloy pipe is bombarded by a high-speed...

Example Embodiment

[0079] Example 3

[0080] A preparation method of a zirconium alloy coating with high burn-up and long-life period, including:

[0081] (1) Pre-treatment: Place the obtained zirconium alloy matrix material in an ultrasonic container and wash with carbon tetrachloride and acetone for 10-20 minutes respectively, then ultrasonically clean with deionized water for more than 10 minutes, and use deionized water in the final stage rinse. The cleaned pipe samples are dried in a vacuum drying oven, and the drying temperature does not exceed 50°C. Clamp the pre-processed sample on the turntable of the coating equipment.

[0082] (2) Ion cleaning: vacuum the vacuum chamber of the coating equipment, and the vacuum degree reaches 1×10 -3 After Pa is above, a certain flow of argon is then filled to maintain the pressure in the vacuum chamber at 0.1-5 Pa. The bias voltage is adjusted to above -1000V for about 10-20 minutes, and the surface of the zirconium alloy pipe is bombarded by a high-speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a zirconium alloy coating with high burnup and long service life and a preparation method of the zirconium alloy coating. Zirconium alloy is a fuel element cladding material,the coating is a metal Cr coating, the purity of metal Cr is 99.95%, and the thickness of the coating is 1-10 microns. The zirconium alloy coating is mainly used for improving the corrosion resistanceand high temperature oxidation resistance of a zirconium alloy cladding so as to improve the inherent safety of a fuel element and prolong the refuelling cycle. The invention also provides the preparation method of the zirconium alloy coating. By optimizing the method, better coating binding force and a fine coating surface structure are obtained.

Description

technical field [0001] The invention relates to the field of high-temperature protective coatings, in particular to a preparation method of a zirconium alloy coating with high fuel consumption and long service life. Background technique [0002] Zirconium alloys have long been used as fuel cladding materials for water-cooled reactors due to their low thermal neutron absorption cross section, moderate mechanical properties, good corrosion resistance and processability. But after the Fukushima nuclear accident in 2011, international efforts were made to research accident-tolerant fuel (ATF) to replace the existing UO 2 -Zr fuel system to improve the ability of nuclear fuel elements to maintain structural integrity under severe accidents, thereby improving the safety and reliability of nuclear reactors under accident conditions. [0003] From the perspective of nuclear fuel cladding, ATF accident-resistant fuel cladding mainly considers corrosion resistance in high temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/32C23C14/35C23C14/16C23C14/02C23C14/58
Inventor 韦天国张瑞谦杨红艳陈寰杜沛南何琨邱绍宇
Owner NUCLEAR POWER INSTITUTE OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap