Radiation cooling coating as well as preparation method and application thereof

A technology of coatings and reflective materials, applied in the direction of reflection/signal coatings, anti-fouling/underwater coatings, coatings, etc., can solve the problems of inability to maintain radiation cooling for a long time, achieve low cost, broad application prospects, and simple process effects

Active Publication Date: 2019-07-09
杭州瑞酷新材料有限公司
View PDF14 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no film-forming substance on the surface of the coating, and dust can easily penet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Radiation cooling coating as well as preparation method and application thereof
  • Radiation cooling coating as well as preparation method and application thereof
  • Radiation cooling coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] Add 95 parts of absolute ethanol, 5 parts of deionized water, 15 parts of polyvinyl butyral (Qingdao Haocheng Industry, SD-5) to the high-speed disperser, and stir for 120 minutes at a linear speed of 5m / s to obtain a slurry material. Then add 20 parts of zinc sodium phosphate (1~3μm), 30 parts of silicon dioxide (1~3μm), 2 parts of trimethoxysilane dispersant, 1 part of simethicone defoamer at a speed of 10m / s, 1 part of inorganic silver-based antibacterial agent (Beijing Aisier Technology Co., Ltd., MK-T-111), dispersed for 30 minutes, filtered through a 100-mesh sieve to obtain the radiation cooling coating of the present invention.

Example Embodiment

[0033] Example 2

[0034] Add 60 parts of cyclohexane, 30 parts of isopropanol, 10 parts of deionized water, and 20 parts of ethylene-vinyl acetate copolymer (Yangzi BASF, V5110J) into the high-speed disperser, and stir at a linear speed of 8m / s 20min to obtain slurry. Then add 30 parts of zirconia (1~3μm), 10 parts of silicon dioxide (1~3μm), 2 parts of trimethoxysilane dispersant and 2 parts of simethicone defoamer at a speed of 5m / s, and disperse 15 minutes, filtered through an 80-mesh screen to obtain the radiation cooling paint of the present invention.

Example Embodiment

[0035] Example 3

[0036] Add 95 parts of methyl ethyl ketone, 5 parts of ethylene glycol, and 20 parts of polyvinyl acetate (Xiamen Zhonghuayuan, PVAc-H) to the high-speed disperser, and stir for 60 min at a linear speed of 10 m / s to obtain a slurry. Then add 10 parts of sodium aluminum silicate (1~3μm), 50 parts of alumina (1~3μm), 3 parts of trimethoxysilane dispersant and 2 parts of dimethyl silicone oil defoamer at a speed of 20m / s. Disperse for 45 minutes and filter through an 80 mesh screen to obtain the radiation cooling paint of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a radiation cooling coating as well as a preparation method and application thereof. The method comprises the following steps: adding 15-30 parts by weight of polymer film-forming resin, 30-60 parts by weight of an ultraviolet reflective material and 1-5 parts by weight of an auxiliary agent into 60-100 parts by weight of a mixed solvent, performing dispersion uniform mixing, and performing filtration by using a filter screen to obtain the radiation cooling coating. The radiation cooling coating coats a substrate according to a thickness of 200-1500 [mu]m, the coating layer formed after drying contains micropores with a volume fraction of 0.05-0.5, the micropores and the ultraviolet reflective material synergistically generate solar reflectance of 0.92-0.96, so thatthe coating has a radiation cooling function. The radiation cooling coating provided by the invention has a simple process and low costs, is suitable for different shapes and planes, and suitable forplaces such as residential buildings, commercial buildings and industrial plants, and has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of energy-saving coatings, in particular to a radiation cooling coating and its preparation method and application. Background technique [0002] Radiation cooling materials achieve a cooling effect lower than atmospheric temperature under solar irradiation, and can replace air conditioning, spraying, etc. under certain conditions, with remarkable energy-saving effects and great application value. However, the existing radiation cooling materials often contain metal coating materials, the process is complex, the price is expensive, and it is only suitable for flat surfaces. [0003] Invention patent 201810238449.X (publication number CN 108250873A) discloses an outdoor all-weather solar reflection and infrared radiation cooling coating, by adding micron-scale spherical microbeads, micron-scale metal-plated flakes, and / or micron-scale plated Metal spheres are used in the coating system, through the method of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D129/14C09D131/04C09D123/08C09D133/04C09D5/33C09D5/14C09D7/61C09D7/65
CPCC08K2003/2227C08K2003/2244C08K2003/265C08K2003/3045C09D5/004C09D5/14C09D123/0853C09D129/14C09D131/04C09D133/04C09D7/61C09D7/65C08L83/04C08K3/32C08K3/36C08K3/22C08K3/34C08K3/30C08K3/26C08K3/346F28F13/185
Inventor 盛艳
Owner 杭州瑞酷新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap