Anti-tensile composite steel adhesive

A steel-adhesive and tensile-resistant technology, which is applied in the field of building structural adhesives, can solve problems such as poor mechanical properties of steel-bonded adhesives, and achieve the effects of improved mechanical properties, improved permeability, and increased double bond content

Inactive Publication Date: 2019-07-12
许水仙
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is: aiming at the problem of poor mechanical properties of traditional steel glue, a kind of anti-stretch composite steel glue is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-tensile composite steel adhesive

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0034] In parts by weight, 30 parts of cork powder, 5 parts of carbomer 934, 3 parts of biogas slurry, 2 parts of sucrose, and 30 parts of water are placed in a fermentation tank at a temperature of 35°C and a speed of 200r / min. , stirred and mixed and fermented for 5 days, then dripped ammonia water with a mass fraction of 30% in the fermentation tank to adjust the pH to 8.3 to obtain a fermentation mixture, then filtered the fermentation mixture to obtain a filter cake, and then placed the filter cake in an oven , dried to constant weight at a temperature of 110°C to obtain a dry filter cake, then put the dry filter cake in a carbonization furnace, and fill the furnace with nitrogen at a rate of 90mL / min, and at a temperature of 850°C, After carbonization for 3 hours, lower the temperature to 160°C to obtain the carbonized material. At a temperature of 160°C, put the carbonized material and the low-melting point alloy in a ball mill at a mass ratio of 1:10 and mix and ball mi...

example 2

[0036] In parts by weight, 30 parts of cork powder, 5 parts of carbomer 934, 3 parts of biogas slurry, 2 parts of sucrose, and 30 parts of water are placed in a fermentation tank at a temperature of 35°C and a speed of 200r / min. , stirred and mixed and fermented for 5 days, then dripped ammonia water with a mass fraction of 30% in the fermentation tank to adjust the pH to 8.3 to obtain a fermentation mixture, then filtered the fermentation mixture to obtain a filter cake, and then placed the filter cake in an oven , dried to constant weight at a temperature of 110°C to obtain a dry filter cake, then put the dry filter cake in a carbonization furnace, and fill the furnace with nitrogen at a rate of 90mL / min, and at a temperature of 850°C, After carbonization for 3 hours, lower the temperature to 160°C to obtain the carbonized material. At a temperature of 160°C, put the carbonized material and the low-melting point alloy in a ball mill at a mass ratio of 1:10 and mix and ball mi...

example 3

[0038] In parts by weight, 30 parts of cork powder, 5 parts of carbomer 934, 3 parts of biogas slurry, 2 parts of sucrose, and 30 parts of water are placed in a fermentation tank at a temperature of 35°C and a speed of 200r / min. , stirred and mixed and fermented for 5 days, then dripped ammonia water with a mass fraction of 30% in the fermentation tank to adjust the pH to 8.3 to obtain a fermentation mixture, then filtered the fermentation mixture to obtain a filter cake, and then placed the filter cake in an oven , dried to constant weight at a temperature of 110°C to obtain a dry filter cake, then put the dry filter cake in a carbonization furnace, and fill the furnace with nitrogen at a rate of 90mL / min, and at a temperature of 850°C, After carbonization for 3 hours, lower the temperature to 160°C to obtain the carbonized material. At a temperature of 160°C, put the carbonized material and the low-melting point alloy in a ball mill at a mass ratio of 1:10 and mix and ball mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-tensile composite steel adhesive and belongs to the technical field of building structure adhesives. Zeolite is subjected to ball milling and sieved, and refined zeolite is obtained; the refined zeolite and a gelatin liquid are subjected to ultrasonic mixing, filtering and drying, a dried filter cake is obtained, the dried filter cake and tetraethoxysilane are mixedand subjected to vacuum impregnation and filtration, filtered residues are obtained, carbonized and cooled, and a modified auxiliary material is obtained; cork powder, carbomer 934, biogas slurry, saccharose and water are mixed and fermented, ammonia water is dropwise added to adjust pH, filtration, drying and carbonization are performed, a carbonized material is obtained and mixed with a low-melting-point alloy, the mixture is subjected to ball milling, and a modified additive is obtained; epoxy resin, a diluent, unsaturated polyester resin, drying oil, the modified additive, a plasticizer,the modified auxiliary material, the curing agent and a coupling agent are mixed and stirred, and the anti-tensile composite steel adhesive is obtained. The provided anti-tensile composite steel adhesive has excellent mechanical performance.

Description

technical field [0001] The invention discloses a stretch-resistant composite steel adhesive, which belongs to the technical field of building structural adhesives. Background technique [0002] Engineering structure reinforcement is an emerging industry, which refers to the necessary structural transformation and reinforcement when the structural system of a building or structure cannot meet the requirements of use. In engineering structure reinforcement, bonded steel reinforcement is a common engineering reinforcement technology. In bonded steel reinforcement, concrete is a common base to be reinforced. In concrete reinforcement, structural adhesives are needed to bond the concrete base and steel to be reinforced. , so that it becomes a unified whole, and then bear the force together to play a role in structural reinforcement. In the reinforcement of bonded steel with concrete as the base material, GB50728-2011 puts forward clear requirements for the basic performance of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J11/04C09J11/06C09J11/08
CPCC08K2003/0837C08K2201/011C08L2205/035C09J11/04C09J11/06C09J11/08C09J163/00C08L67/06C08L91/005C08L97/02C08L95/00C08K13/06C08K9/08C08K9/00C08K9/04C08K7/26C08K3/04C08K3/08C08K5/12C08K3/36
Inventor 许水仙
Owner 许水仙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap