Low-odor flame-retardant rubber floor and preparation method thereof

A technology for flame-retardant rubber and rubber flooring, applied in the field of rubber materials, can solve the problems of easy aging of rubber flooring, volatilize odor, odor, reduce odor, etc., and achieve the effect of reducing odor, increasing the rate of gel formation, and improving product stability

Inactive Publication Date: 2019-07-30
DALIAN GAOKE FLAME RETARDANT RUBBER
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Because the rubber floor is mostly used in a closed room, the rubber floor in the prior art is often due to the unreasonable proportion of light stabilizers and antioxidants, which causes the rubber floor to age easily and emit peculiar smell. The peculiar smell is caused by the volatilization of low mol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-odor flame-retardant rubber floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The embodiment of the present invention also discloses a preparation method for the above-mentioned low-odor flame-retardant rubber floor, which is a method of extruding, calendering and vulcanization after mixing with an internal mixer, specifically including:

[0031] A. Weigh 15-25 parts of high styrene resin, 40-55 parts of kaolin, 2-4 parts of light stabilizer, 5-8 parts of antioxidant, 40-60 parts of inorganic flame retardant, 60- 80 parts, 4-8 parts of silane coupling agent, 2-5 parts of accelerator, and 3-6 parts of vulcanizing agent are mixed to form a mixed drug;

[0032] B. Cool the internal mixer with water, control the temperature of the working room of the internal mixer to 100°C to 150°C, adjust the speed of the internal mixer to 35 rpm, adjust the pressure of the top bolt on the internal mixer to 0.38MPa, and start the mixer for internal mixing. After 10 seconds of internal mixing, weigh 80-100 parts of styrene-butadiene rubber and add it to the internal...

Embodiment 1

[0038] A. Weigh 15 parts of high styrene resin, 40 parts of kaolin, 2 parts of BASF Tinuvin770DF, 8 parts of BASF 1076, 40 parts of magnesium hydroxide, 60 parts of melamine cyanurate, 4 parts of silicon 69, and 2 parts of accelerator DM. mixed to form a mixture;

[0039]B. Cool the internal mixer with water, control the temperature of the working room of the internal mixer to 100°C to 150°C, adjust the speed of the internal mixer to 35 rpm, adjust the pressure of the top bolt on the internal mixer to 0.38MPa, and start the mixer for internal mixing. After 10 seconds of internal mixing, weigh 80-100 parts of styrene-butadiene rubber and add it to the internal mixer to form a mixture, and adjust the speed to 38 rpm;

[0040] C. After 30 seconds for banburying, add the mixed drug into the banbury mixer for banburying;

[0041] D. Add 45 parts of white carbon black at 200 seconds for banburying, control and keep the temperature of the glue at 160°C for banburying and discharging...

Embodiment 2

[0045] Compared with Example 1, the present embodiment only changes the formula: the rubber floor includes the following parts by weight: 90 parts of styrene-butadiene rubber, 20 parts of high styrene resin, 50 parts of white carbon black, 48 parts of kaolin 3 parts, 3 parts of BASF Tinuvin770DF, 6 parts of BASF 1076, 50 parts of aluminum hydroxide, 70 parts of melamine cyanurate, 6 parts of silicon 69, 4 parts of accelerator TBzTD, 5 parts of vulcanizing agent, the preparation method still adopts embodiment 1 Preparation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention relates to the technical field of rubber, in particular to a low-odor flame-retardant rubber floor and a preparation method thereof. The rubber floor is prepared from,by weight, 80-100 parts of styrene-butadiene rubber, 15-25 parts of high-styrene resin, 45-55 parts of white carbon black, 40-55 parts of kaolin, 2-4 parts of a light stabilizer, 5-8 parts of an antioxidant, 40-60 parts of an inorganic flame retardant, 60-80 parts of melamine cyanurate, 4-8 parts of a silane coupling agent, 2-5 parts of an accelerator and 3-6 parts of a vulcanizing agent. The low-odor flame-retardant rubber floor and the preparation method thereof have the advantages that the light stabilizer and the antioxidant are properly mixed, so that the generation of low-molecular-weight volatile substances after ageing caused by ultraviolet irradiation and oxidation reaction during use is relieved, thereby greatly reducing the odor and solving the problem of pollution.

Description

technical field [0001] The embodiment of the present invention relates to the technical field of rubber materials, in particular to a low-odor flame-retardant rubber floor and a preparation method thereof. Background technique [0002] Rubber flooring is a floor made of natural rubber, synthetic rubber and other polymer materials. SBR, high benzene, and butadiene rubber are synthetic rubbers, which are by-products of petroleum. Rubber flooring has a wide range of practical applications due to its high efficiency flame retardancy and mechanical properties. Match factory, fireworks factory, national defense ammunition depot, anti-slip deck of warship office, office building, pedestrian walkway in villa area, anti-slip walkway of ship, nursery school, kindergarten, activity center for the elderly, shopping in medium-sized children's playground, swimming pool, swimming pool, massage room, medical unit Boutique rooms in the center, tour walkways in counters, welcome corridors i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/06C08L25/10C08K13/02C08K3/36C08K3/34C08K5/3492C08K3/22C08K13/06C08K9/06
CPCC08K2003/2224C08K2003/2227C08L9/06C08L2201/02C08L2201/08C08L25/10C08K13/02C08K3/36C08K3/346C08K5/34928C08K3/22C08K13/06C08K9/06
Inventor 郭连龙戴宇
Owner DALIAN GAOKE FLAME RETARDANT RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap