Free-cutting aluminum copper alloy extruded bar and preparation method thereof

An aluminum-copper alloy, easy-cutting technology, applied in the field of aluminum-copper alloy extruded bar and its preparation, can solve the problem of high temperature brittleness, the cutting performance of aluminum-copper alloy extruded bar is difficult to meet the requirements of high-speed cutting processing of CNC machine tools, and the Poor corrosion performance, etc.

Active Publication Date: 2019-08-23
GUANGDONG XINGFA ALUMINUM +1
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] (2) With the popularization and application of high-speed CNC machine tools such as CNC lathes, CNC milling machines, and CNC drilling machines, the cutting performance of existing easy-to-cut aluminum-copper alloy extruded bars has become increasingly difficult to meet the high-speed cutting requirements of CNC machine tools , there is an urgent need to develop alu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Free-cutting aluminum copper alloy extruded bar and preparation method thereof
  • Free-cutting aluminum copper alloy extruded bar and preparation method thereof
  • Free-cutting aluminum copper alloy extruded bar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] A free-machining aluminum-copper alloy extruded rod, consisting of the following components in mass percentage: Cu 4.1%, Mg 0.8%, Mn 0.9%, Cr 0.5%, Ce 0.2%, B 0.08%, Ti 0.015%, C 0.0006%, Sn 1.1%, Bi0.4%, Fe≤0.2%, Si≤0.1%, the balance is Al and other impurity elements, the individual content of other impurity elements≤0.05%, the total ≤0.15%;

[0064] Its preparation method is as figure 1 shown, including the following steps:

[0065] S001: According to the composition and mass percentage of aluminum-copper alloy extruded rods, select aluminum ingots with 99.7% aluminum content, magnesium ingots with 99.95% magnesium content, tin ingots with 99.99% tin content, bismuth ingots with 99.99% bismuth content, AlCu50 alloy, AlMn10 alloy, AlCr10 alloy, AlCe5 alloy, AlB3 alloy and AlTi5C0.2 alloy wire are used as raw materials for batching;

[0066]S002: Place the aluminum ingot in a furnace with a permanent magnetic stirring device at the bottom of the furnace and heat and m...

Embodiment 2

[0075] A free-machining aluminum-copper alloy extruded rod, composed of the following components in mass percentage: Cu 3.5%, Mg 0.9%, Mn 0.6%, Cr 0.6%, Ce 0.25%, B 0.06%, Ti 0.01%, C 0.0004%, Sn 1.2%, Bi0.3%, Fe≤0.2%, Si≤0.1%, the balance is Al and other impurity elements, the individual content of other impurity elements≤0.05%, the total ≤0.15%;

[0076] Its preparation method comprises the following steps:

[0077] S001: According to the composition and mass percentage of aluminum-copper alloy extruded rods, select aluminum ingots with 99.7% aluminum content, magnesium ingots with 99.95% magnesium content, tin ingots with 99.99% tin content, bismuth ingots with 99.99% bismuth content, AlCu50 alloy, AlMn10 alloy, AlCr10 alloy, AlCe5 alloy, AlB3 alloy and AlTi5C0.2 alloy wire are used as raw materials for batching;

[0078] S002: Place the aluminum ingot in a furnace with a permanent magnetic stirring device at the bottom of the furnace and heat and melt at 760°C, then add m...

Embodiment 3

[0087] A free-machining aluminum-copper alloy extruded rod, consisting of the following components in mass percentage: Cu 4.5%, Mg 0.6%, Mn 1.0%, Cr 0.4%, Ce 0.15%, B 0.1%, Ti 0.02%, C 0.0008%, Sn 0.8%, Bi0.5%, Fe≤0.2%, Si≤0.1%, the balance is Al and other impurity elements, the individual content of other impurity elements is ≤0.05%, and the total amount is ≤0.15%;

[0088] Its preparation method comprises the following steps:

[0089] S001: According to the composition and mass percentage of aluminum-copper alloy extruded rods, select aluminum ingots with 99.7% aluminum content, magnesium ingots with 99.95% magnesium content, tin ingots with 99.99% tin content, bismuth ingots with 99.99% bismuth content, AlCu50 alloy, AlMn10 alloy, AlCr10 alloy, AlCe5 alloy, AlB3 alloy and AlTi5C0.2 alloy wire are used as raw materials for batching;

[0090] S002: Place the aluminum ingot in a furnace with a permanent magnetic stirring device at the bottom of the furnace to heat and melt at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a free-cutting aluminum copper alloy extruded bar and a preparation method thereof. The aluminum copper alloy extruded bar comprises the following components of, in percentage by mass, 3.5%-4.5% of Cu, 0.6%-0.9% of Mg, 0.6%-1.0% of Mn, 0.4%-0.6% of Cr, 0.15%-0.25% of Ce, 0.06%-0.1% of B, 0.01%-0.02% of Ti, 0.0004%-0.0008% of C, 0.8%-1.2% of Sn, 0.3%-0.5% of Bi, less than orequal to 0.2% of Fe, less than or equal to 0.1% of Si, and the balance Al and other impurity elements. The preparation method of the bar sequentially comprises the steps of burdening, smelting an aluminum copper molten alloy, in-furnace blowing and refining treatment and degassing and impurity removing, on-line grain refining, on-line degassing filtering treatment, semi-continuous casting treatment, cast bar homogenizing, heating extruding treatment, on-line quenching and artificial aging treatment. The aluminum copper alloy extruded bar does not contain heavy metal element lead, meets the environment-friendly requirement, and has good mechanical properties and excellent cutting machining performance; cutting chips are easy to break, not prone to adhere to or twine around a cutter, the production efficiency of cutting machining is improved, and the surface smoothness and the size precision of products are improved.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy preparation, and in particular relates to an easy-cut aluminum-copper alloy extruded rod and a preparation method thereof. Background technique [0002] Easy-to-cut aluminum alloys usually refer to aluminum alloys that are easy to break chips, do not stick to the knife, do not wrap around the knife, and are easy to remove chips. Free-cutting aluminum alloys can be cut at a higher speed or with a larger feed rate, so the production efficiency of cutting can be significantly improved, and precision aluminum alloy parts with good surface finish and high dimensional accuracy can be obtained. [0003] The existing free-cutting aluminum alloys mainly improve the cutting performance of aluminum alloys by adding low-melting point metal elements. During high-speed cutting of aluminum alloys, the temperature of aluminum alloy chips increases due to frictional heat generation. When the temperature of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/16C22C21/14C22C1/03C22C1/06C22F1/057B21C23/00
CPCB21C23/002C22C1/026C22C1/03C22C1/06C22C21/14C22C21/16C22F1/057
Inventor 陈文泗罗铭强王顺成聂德键易鹏林丽荧金娜郑健全
Owner GUANGDONG XINGFA ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap