Preparation method and application of a carbon nanotube assembled capsaicin repellent biological antifouling marine paint

A carbon nanotube and biological anti-fouling technology, which is applied in the direction of biocide-containing paint, anti-fouling/underwater paint, anti-corrosion paint, etc. low problems, to achieve the effect of superior comprehensive antifouling performance, good environmental protection and good anti-corrosion

Inactive Publication Date: 2021-06-08
浙江轩爱能源科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the problems of short antifouling time, low antifouling efficiency, and harm to marine organisms and sea body ecology, new types of antifouling coatings such as tin-free self-polishing antifouling coatings, low surface energy antifouling coatings, biological antifouling coatings, and nano antifouling coatings Antifouling coatings have emerged as the times require, and their excellent antifouling performance is highly anticipated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method for assembling capsaicin repellent biological antifouling marine paint by carbon nanotubes, comprising the following steps:

[0023] (1) Take carbon nanotubes, add them to a nitric acid solution with a concentration of 96-99%, ultrasonicate for 5 hours, filter, mix the precipitate with stearic acid, raise the temperature to 200°C, and keep stirring for 36 minutes to obtain activated carbon nanotube;

[0024] (2) Take octylisothiazolinone, add it to 88 times its weight in 71% ethanol solution, stir evenly, add trifluoroethyl methacrylate, stir evenly, and obtain monomer solution;

[0025] (3) get ammonium persulfate, join in the deionized water of 58 times of its weight, stir, obtain initiator solution;

[0026] (4) Get capsaicin, join in the acetone of its weight 9 times, stir well, add polysorbate, stir well, get acetone dispersion liquid;

[0027] (5) Obtain the monomer solution, mix the activated carbon nanotubes, stir evenly, send it into the ...

Embodiment 2

[0035] A preparation method for assembling capsaicin repellent biological antifouling marine paint by carbon nanotubes, comprising the following steps:

[0036] (1) Take carbon nanotubes, add them to a nitric acid solution with a concentration of 99%, ultrasonicate for 7 hours, filter, mix the precipitate with stearic acid, raise the temperature to 210°C, and keep stirring for 40 minutes to obtain activated carbon nanotubes ;

[0037] (2) Take octylisothiazolinone, add it to a 75% ethanol solution of 100 times its weight, stir evenly, add trifluoroethyl methacrylate, stir evenly, and obtain a monomer solution;

[0038] (3) get ammonium persulfate, join in the deionized water of 60 times of its weight, stir, obtain initiator solution;

[0039] (4) Get capsaicin, join in the acetone of its weight 12 times, stir well, add polysorbate, stir well, get acetone dispersion liquid;

[0040] (5) Obtain the monomer solution, mix the activated carbon nanotubes, stir evenly, send it into...

Embodiment 3

[0048] A preparation method for assembling capsaicin repellent biological antifouling marine paint by carbon nanotubes, comprising the following steps:

[0049] (1) Take carbon nanotubes, add them to a nitric acid solution with a concentration of 96%, ultrasonicate for 5 hours, filter, mix the precipitate with stearic acid, raise the temperature to 180°C, and keep stirring for 30-40 minutes to obtain activated carbon nanotube;

[0050] (2) Take octylisothiazolinone, add it to a 70% ethanol solution that is 80 times its weight, stir evenly, add trifluoroethyl methacrylate, stir evenly, and obtain a monomer solution;

[0051] (3) get ammonium persulfate, join in the deionized water of 50 times of its weight, stir, obtain initiator solution;

[0052] (4) Get capsaicin, join in the acetone of its weight 8 times, stir well, add polysorbate, stir well, get acetone dispersion liquid;

[0053] (5) Obtain the monomer solution, mix the activated carbon nanotubes, stir evenly, send it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of carbon nanotubes assembled capsaicin repellent biological antifouling marine paint. The invention first activates carbon nanotubes with nitric acid and stearic acid, and uses trifluoroethyl methacrylate as a monomer, Polymerization under the action of an initiator to obtain a polyester emulsion doped with carbon nanotubes, and then dispersing the acetone solution of capsaicin into the polyester emulsion to realize the intercalation and assembly of capsaicin between carbon nanotubes, sustained release and The affinity with the ship bottom steel plate improves the fastness and slow release service life of the ship bottom coating. In the invention, the modified capsaicin is assembled with carbon nanotubes as an effective component, and the biological repelling and anti-corrosion effects of using capsaicin in a long life can be achieved.

Description

technical field [0001] The invention belongs to the field of marine anticorrosion, and in particular relates to a preparation method and an application of a capsaicin repellent biological antifouling marine paint assembled with carbon nanotubes (multi-wall). Background technique [0002] As we all know, the attachment of marine organisms to the surface of a ship will not only significantly increase the mass of the hull, increase navigation resistance, reduce the speed of the ship, thereby increasing fuel consumption, but also accelerate the corrosion of the ship's bottom and shorten the service life. In order to reduce the harm of marine organisms and prevent marine organisms from fouling ships, people have studied a variety of antifouling technologies. In the past few decades, compounds such as mercury and arsenic were used to formulate antifouling coatings in the early stage, but they were eliminated due to the toxicity of these substances and polluted the marine environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/16C09D5/08
CPCC08L2205/03C09D5/08C09D5/1618C09D5/1625C09D163/00C08L83/04C08L33/16C08K9/02C08K9/04C08K3/041C08K5/20
Inventor 关君正张孝彬程继鹏关君安范骏
Owner 浙江轩爱能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products