Reflective heat-insulating stone-like coating and preparation process thereof

A preparation process, a technology of real stone paint, applied in the field of building materials and coatings, can solve the problems of poor overall application effect and good overall applicability, and achieve the effect of improving application effect, improving applicability, and good reflection effect

Inactive Publication Date: 2019-10-01
HUBAO NEW MATERIAL TECH SHANGHAI CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the problem in the prior art that the coating film of real stone paint cannot effectively reflect the visible light and near-infrared light in sunlight back into the atmosphere, resulting in poor overall application effect, the first purpose of the present invention is to provide a By adding water-based polyurethane paint with reflective heat-insulating titanium dioxide to dye white quartz sand at high temperature to solve the above technical problems, the coating film formed after use is sensitive to visible light and near sunlight in sunlight. Infrared light has a good reflection effect, and the overall applicability is good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reflective heat-insulating stone-like coating and preparation process thereof
  • Reflective heat-insulating stone-like coating and preparation process thereof
  • Reflective heat-insulating stone-like coating and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Example 1: A reflective and heat-insulating real stone paint, the components and their corresponding parts by weight are shown in Table 1, and are prepared through the following steps:

[0050] Step 1, prepare the color paint, remove the corresponding weight percentage of dyed sand, mix and stir evenly with polyurethane water-based paint and curing agent, and obtain the special color paint for dyed sand;

[0051] Step 2, sand dyeing production, first turn on the sand dyeing equipment to preheat for 1-2 hours, add the white quartz sand of the corresponding weight percentage into the dispersion tank, stir continuously, then slowly add the special color paint for sand dyeing, and disperse for 5- After 10 minutes, high-temperature baking is carried out for 12-15 minutes to obtain dyed sand in corresponding parts by weight;

[0052] Step 3, mixing the paint material, the pure acrylic acid emulsion, 4040 dispersant, propylene glycol butyl ether, ethylene glycol, cellulose, tr...

Embodiment 2-8

[0055] Example 2-8: A reflective heat-insulating real stone paint, the difference from Example 1 is that the components and their corresponding parts by weight are shown in Table 1.

[0056] Each component and parts by weight thereof in table 1 embodiment 1-8

[0057]

Embodiment 9

[0058] Embodiment 9: A reflective and heat-insulating real stone paint. The difference from Embodiment 1 is that the dyed sand in the above steps includes the following components in weight percentage: 75% of white quartz sand; 20% of polyurethane water-based paint for dyed sand ; Curing agent 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a reflective heat-insulating stone-like coating and a preparation process thereof, relates to the technical field of building material coatings, and solves the problem of pooroverall application effect due to the fact that a coating film of the stone-like coating cannot effectively reflect visible light and near infrared light in solar light back into the atmosphere. The reflective heat-insulating stone-like coating comprises the following components in parts by weight: 12-14 parts of pure acrylic emulsion, 1.2-1.5 parts of 4040 dispersant, 0.6-0.8 part of a film forming additive, 0.3-0.7 part of ethylene glycol, 0.12-0.15 part of cellulose, 0.1-0.125 part of a pH regulator, 0.075-0.08 part of a preservative, 0.025-0.05 part of a defoaming agent and 70-75 parts ofdyed sand, wherein the dyed sand comprises the following components in percentage by weight: 75-80% of white quartz sand, 16-20% of polyurethane aqueous color paint for the dyed sand and 4-5% of a curing agent. A coating film formed by the reflective heat-insulating stone-like coating has a good reflection effect on THE visible light and near infrared light in solar light, can maintain good stability in the use process, and has a good application effect.

Description

technical field [0001] The invention relates to the technical field of building material coatings, more specifically, it relates to a reflective heat-insulating real stone paint and a preparation process thereof. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly formulated with natural stone powder of various colors. It is applied to the imitation stone effect of building exterior walls. It has the texture of natural stone, so it is also called liquid stone. [0003] In the Chinese invention patent application document with the publication number CN105348962A, a natural stone paint for exterior walls is disclosed, which is composed of the following raw materials in parts by weight: 20-45 parts of soap-free polymerized pure acrylic emulsion, 15-45 parts of natural colored sand 25 parts, 5-18 parts of organic zinc complex inhibitors, 6-12 parts of silicone defoamers, 1-5 parts of quaternary am...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/06C04B20/10
CPCC04B20/10C04B20/1096C04B26/06C04B2111/00482C04B2103/408C04B24/023C04B24/02C04B24/383C04B14/06C04B24/122C04B24/008C04B24/42C04B24/045
Inventor 孟奎孟运
Owner HUBAO NEW MATERIAL TECH SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products