Waterproof flame-retardant paint used for corrugated paperboard and production method of waterproof flame-retardant paint used for corrugated paperboard

A technology of flame-retardant coating and corrugated cardboard, which is applied in the field of corrugated cardboard, can solve the problems of restricting the use of flame-retardant corrugated cardboard, great influence on the strength of corrugated cardboard, and human injury, etc., and achieve the effects of enhanced mechanical properties, convenient operation, and not easy to lose

Active Publication Date: 2019-10-08
台州市黄岩华印纸业有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the existing flame retardants for corrugated cardboard can achieve a certain flame-retardant effect, there are the following defects: one is the use of halogen-containing flame retardants, which will produce harmful gases such as hydrogen halides when a fire occurs, causing harm to the human body and causing damage to the human body. Environmental damage; the second is inorganic flame retardants such as Al(OH) 3 , Mg(OH) 2 There are problems such as easy loss, large dosage, and great influence on the strength of corrugated cardboard, which seriously restrict the use of flame-retardant corrugated cardboard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof flame-retardant paint used for corrugated paperboard and production method of waterproof flame-retardant paint used for corrugated paperboard

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The waterproof and flame-retardant coating for corrugated cardboard of the present embodiment includes the following components in weight percent: 50% of silicone modified polyurethane aqueous dispersion, 10% of ammonium polyphosphate, 6.0% of melamine phosphate, 6.0% of pentaerythritol, iso 4.0% propanol, 3.0% isopropanol silica sol, 1.5% methyltrimethoxysilane, 0.2% nonylphenol polyoxyethylene ether, 0.5% additive, and the balance is water.

[0045] The preparation method of the waterproof flame retardant coating for corrugated cardboard of the present embodiment, comprises the following steps:

[0046] 1) Take the formula quantity of isopropanol silica sol, add 15% water of the mass of isopropanol silica sol and 1 / 3 formula quantity of methyltrimethoxysilane, stir and react at 50°C for 60min, then cool to room temperature , to obtain modified silica sol;

[0047] 2) Mix ammonium polyphosphate, melamine phosphate, and pentaerythritol with 2 / 3 of the formula amount of...

Embodiment 2

[0054] The waterproof and flame-retardant coating for corrugated cardboard of the present embodiment includes the following components in weight percent: 50% of silicone modified polyurethane water dispersion, 12% of ammonium polyphosphate, 5.0% of melamine phosphate, 5.0% of pentaerythritol, iso 4.5% propanol, 3.2% isopropanol silica sol, 1.8% methyltrimethoxysilane, 0.15% nonylphenol polyoxyethylene ether, 0.5% additive, and the balance is water.

[0055] The preparation method of the waterproof flame retardant coating for corrugated cardboard of the present embodiment, comprises the following steps:

[0056] 1) Take the isopropanol silica sol of the formula, add 12% of the mass of isopropanol silica sol and 1 / 3 of the formula of methyltrimethoxysilane, stir and react at 60°C for 50min, and then cool to room temperature to obtain Modified silica sol;

[0057] 2) Mix ammonium polyphosphate, melamine phosphate, and pentaerythritol with 2 / 3 of the formula amount of methyltrime...

Embodiment 3

[0064] The waterproof and flame-retardant coating for corrugated cardboard of the present embodiment includes the following components in weight percent: 50% of silicone modified polyurethane aqueous dispersion, 11% of ammonium polyphosphate, 5.0% of melamine phosphate, 6.0% of pentaerythritol, iso 5.0% propanol, 3.5% isopropanol silica sol, 1.8% methyltrimethoxysilane, 0.1% nonylphenol polyoxyethylene ether, 0.5% additive, and the balance is water.

[0065] The preparation method of the waterproof flame retardant coating for corrugated cardboard of the present embodiment, comprises the following steps:

[0066] 1) Take the isopropanol silica sol of the formulation amount, add 10% of the mass of the isopropanol silica sol and 1 / 3 of the formulation amount of methyltrimethoxysilane, stir and react at 55°C for 55min, and then cool to room temperature to obtain Modified silica sol;

[0067] 2) Mix ammonium polyphosphate, melamine phosphate, and pentaerythritol with 2 / 3 of the fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
edge compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to waterproof flame-retardant paint used for corrugated paperboard and a production method of the waterproof flame-retardant paint used for the corrugated paperboard. The waterproof flame-retardant paint comprises water and the following components in percentage by weight: 48%-52% of organosilicone-modified polyurethane aqueous dispersion, 10%-12% of ammonium polyphosphate, 5.0%-6.0% of a melamine phosphate, 5.0%-6.0% of pentaerythritol, 4.0%-5.0% of isopropanol, 3.0%-3.5% of isopropanol silica sol, 1.5%-1.8% of methyltrimethoxysilane, 0.1%-0.2% of nonylphenol polyoxyethylene ether and 0.5%-1.0% of assistants. Under situations of a thin coating and low coating weight, the waterproof flame-retardant paint improves the mechanical strength and the mechanical performanceof the corrugated paperboard; the corrugated paperboard can reach a flame-retardant grade, and fire-proofing and flame-retardant effects are obvious; and a water contact angle of the surface of a filmreaches 120 degrees or above, so that the corrugated paperboard has good dampproof and waterproof properties.

Description

technical field [0001] The invention belongs to the technical field of corrugated cardboard, specifically relates to a waterproof and flame-retardant coating for corrugated cardboard, and also relates to a preparation method of the above-mentioned waterproof and flame-retardant coating for corrugated cardboard. Background technique [0002] With the rise and explosive development of e-commerce, logistics and express delivery industries, the amount of corrugated cardboard used as packaging materials has also shown a substantial increase, and the corrugated cardboard industry has entered a period of rapid development and growth. Corrugated cardboard, also known as corrugated cardboard, is a multi-layer cardboard formed by processing corrugated base paper into a corrugated shape and bonding it with boxboard in a certain way. It is made of at least one layer of corrugated paper and a layer of boxboard. Good strength, elasticity and stiffness. [0003] The use of corrugated card...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/34D21H19/24D21H19/14
CPCD21H21/34D21H19/24D21H19/14
Inventor 魏晓峰
Owner 台州市黄岩华印纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com