A cationic polyester blended fabric with antibacterial function and its preparation process

A technology of cationic polyester and blended fabrics, applied in textiles, papermaking, knitting, plant fibers, etc., can solve the problems of small surface friction coefficient of chitosan fibers, poor mechanical properties of chitosan fibers, and poor bobbin forming effect, etc. , to achieve bright colors, improve wearability, and reduce the number of hairiness

Active Publication Date: 2020-12-22
苏州麦克成纺织有限公司 +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, chitosan fiber has poor mechanical properties and is not suitable for direct processing, which makes it difficult to prepare antibacterial fabrics by weaving chitosan fiber; in addition, due to the small friction coefficient of chitosan fiber surface, The fiber cohesion is low, so the hairiness increases greatly in the winding process, which may easily cause the problem of poor yarn forming effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A cationic polyester blended fabric with antibacterial function and its preparation process
  • A cationic polyester blended fabric with antibacterial function and its preparation process
  • A cationic polyester blended fabric with antibacterial function and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of preparation technology of cationic polyester blended fabric with antibacterial function, its specific steps are as follows:

[0052] (1) Preparation of cationic polyester raw slivers:

[0053] (1.1) carry out modification treatment to polyester fiber, adopt dimethyl isophthalate-5-sodium sulfonate (SIPM) and polyester copolymerization, obtain cationic polyester fiber;

[0054] (1.2) First of all, if image 3 The cationic polyester shown is soaked in absolute ethanol, and fully washed in an ultrasonic cleaner for 60 minutes, rinsed with deionized water and dried in an oven at 60°C, then spread the cationic polyester on the wire mesh, and then place it In the plasma processing chamber, the output power of the plasma machine power supply and the pressure of the vacuum chamber were adjusted to 150w and 10Pa respectively, and argon gas was passed through for 40s. Finally, the cationic polyester was washed with deionized water for several times and placed in 60 ℃ ...

Embodiment 2

[0074] A kind of preparation technology of cationic polyester blended fabric with antibacterial function, its specific steps are as follows:

[0075] (1) Preparation of cationic polyester raw slivers:

[0076] (1.1) carry out modification treatment to polyester fiber, adopt dimethyl isophthalate-5-sodium sulfonate (SIPM) and polyester copolymerization, obtain cationic polyester fiber;

[0077] (1.2) First, immerse the cationic polyester in absolute ethanol, and fully wash it in an ultrasonic scrubber for 20 minutes, rinse it with deionized water and dry it in an oven at 60°C, then spread the cationic polyester flat on the steel wire mesh, and then It is placed in the plasma processing chamber, and then the output power of the plasma machine power supply and the pressure of the vacuum chamber are adjusted to 200w and 20Pa respectively, and nitrogen is passed through for 100s. Finally, the cationic polyester is washed with deionized water several times and placed in the Dry in ...

Embodiment 3

[0097] A kind of preparation technology of cationic polyester blended fabric with antibacterial function, its specific steps are as follows:

[0098] (1) Preparation of cationic polyester raw slivers:

[0099] (1.1) carry out modification treatment to polyester fiber, adopt dimethyl isophthalate-5-sodium sulfonate (SIPM) and polyester copolymerization, obtain cationic polyester fiber;

[0100] (1.2) First, immerse the cationic polyester in absolute ethanol, and fully wash it in an ultrasonic scrubber for 40 minutes, rinse it with deionized water and dry it in an oven at 60°C, then lay the cationic polyester flat on the steel wire mesh, and then It is placed in the plasma treatment chamber, and then the output power of the plasma machine power supply and the pressure of the vacuum chamber are adjusted to 150w and 15Pa respectively, and oxygen is passed through for 100s. Finally, the cationic polyester is washed with deionized water for several times and placed in the Dry in an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial functional cationic polyester blended fabric and a preparation process thereof. The preparation process includes the step of weaving antibacterial functionalcationic polyester blended yarn to obtain the antibacterial functional cationic polyester blended fabric. The antibacterial functional cationic polyester blended yarn is prepared by carding cationic polyester fibers obtained after plasma treatment, cotton fibers and chitosan fibers separately, carrying out mixing, and then sequentially carrying out the procedures of drawing, roving, spinning and winding, wherein according to the parameters of the winding procedure, the winding speed is 850-1200 m / min, and the tension is 5-8 cN; the finally prepared antibacterial functional cationic polyester blended fabric is excellent in elasticity, soft and comfortable in hand feeling and good in moisture absorption and air permeability. The blended fabric solves the problems that cationic polyester fibers are poor in antibacterial property, chitosan fibers are low in breaking strength, high in rigidity and low in cohesive force, and thus the spinnability is poor. The obtained fabric has good antibacterial function, great mechanical performance, high moisture absorption and air permeability and low hairiness number.

Description

technical field [0001] The invention belongs to the technical field of textiles, and relates to an antibacterial functional cationic polyester blended fabric and a preparation process thereof. Background technique [0002] Cationic polyester, also known as cationic dye-dyeable polyester, is a modified polyester product. Modification of polyester can improve the color absorption performance of the fiber and reduce the crystallinity of the fiber, making the dye molecules easy to penetrate, facilitating the dyeing of the dye molecules, and the fiber absorbs moisture. The air permeability is also further improved, so the development and application of cationic polyester is very extensive. [0003] When developing and applying polyester, it is often necessary to modify polyester. The cationic polyester obtained after modification is dyed with cationic dyes. The dyed fabric is bright in color, has a high dye exhaustion rate, and greatly reduces the discharge of printing and dyeing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/14D02G3/04D06M10/02D06M15/03D06M11/155D06M15/285D06M101/32D06M101/06
CPCD02G3/04D04B1/14D06M10/02D06M11/155D06M15/03D06M15/285D06M16/00D06M2101/06D06M2101/32D10B2201/02D10B2331/04D10B2401/13
Inventor 潘志娟张明其张莉张鸿赵泽宇刘燕平李刚
Owner 苏州麦克成纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com