A kind of ABS edge banding and preparation method thereof

A technology of edge banding and body, applied in the direction of film/sheet release coating, heat-activated film/sheet, film/sheet adhesive, etc., can solve the problem of not well considering the use of edge banding and other issues, to achieve the effect of providing overall stability, good aging resistance, and good adhesion

Active Publication Date: 2021-08-27
SINOWOLF PLASTIC DEKOR
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Of course, there is also an existing technology for improving hot-melt adhesives, but its improved guidance does not take into account the use of edge banding well, so there is no more effective solution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ABS edge banding and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] An ABS edge banding, comprising an edge banding body, the back of the edge banding body is sequentially compounded with a primer layer and a hot melt adhesive layer, and the edge banding body is made of the following raw materials in parts by weight:

[0055] ABS resin 60 parts

[0056] Nano calcium carbonate 25 parts

[0057] Acrylic Elastomer Emulsion 35 parts

[0058] Impact modifier 5 parts

[0059] Antioxidant 1.5 parts

[0060] 1.5 parts of ultraviolet absorber;

[0061]The primer layer is formed by UV curing of acrylic paint, and the acrylic paint includes the following raw materials in parts by weight:

[0062] Acrylate prepolymer 50 parts

[0063] Dilute monomer 25 parts

[0064] Nano carbon black 12 parts

[0065] Emulsifier 6 parts

[0066] Photoinitiator 0.6 parts

[0067] 70 parts of deionized water.

[0068] Wherein, the acrylic elastomer emulsion includes the following raw materials in parts by weight:

[0069] Styrene 10 parts

[0070] Methyl...

Embodiment 2

[0097] An ABS edge banding, comprising an edge banding body, the back of the edge banding body is sequentially compounded with a primer layer and a hot melt adhesive layer, and the edge banding body is made of the following raw materials in parts by weight:

[0098] ABS resin 50 parts

[0099] Nano calcium carbonate 20 parts

[0100] Acrylic Elastomer Emulsion 30 parts

[0101] Impact modifier 4 parts

[0102] Antioxidant 1 part

[0103] 1 part UV absorber;

[0104] The primer layer is formed by UV curing of acrylic paint, and the acrylic paint includes the following raw materials in parts by weight:

[0105] Acrylate prepolymer 40 parts

[0106] Dilute monomer 20 parts

[0107] Nano carbon black 10 parts

[0108] Emulsifier 5 parts

[0109] Photoinitiator 0.2 part

[0110] 60 parts of deionized water.

[0111] Wherein, the acrylic elastomer emulsion includes the following raw materials in parts by weight:

[0112] 8 parts styrene

[0113] Methyl methacrylate 10 pa...

Embodiment 3

[0140] An ABS edge banding, comprising an edge banding body, the back of the edge banding body is sequentially compounded with a primer layer and a hot-melt adhesive layer, and the edge banding body is made of the following raw materials in parts by weight:

[0141] ABS resin 70 parts

[0142] Nano calcium carbonate 30 parts

[0143] Acrylic elastomer emulsion 40 parts

[0144] Impact modifier 6 parts

[0145] Antioxidant 2 parts

[0146] 2 parts of UV absorber;

[0147] The primer layer is formed by UV curing of acrylic paint, and the acrylic paint includes the following raw materials in parts by weight:

[0148] Acrylate prepolymer 60 parts

[0149] Dilute monomer 30 parts

[0150] Nano carbon black 14 parts

[0151] Emulsifier 7 parts

[0152] Photoinitiator 1 part

[0153] 80 parts of deionized water.

[0154] Wherein, the acrylic elastomer emulsion includes the following raw materials in parts by weight:

[0155] Styrene 12 parts

[0156] Methyl methacrylate 12 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of edge banding, in particular to an ABS edge banding and a preparation method thereof. The edge banding includes an edge banding body, and the back of the edge banding body is sequentially compounded with a primer layer and a hot melt adhesive layer , the edge banding body is made of raw materials such as ABS resin, nano-calcium carbonate, and acrylic elastomer emulsion, and the primer layer is made of raw materials such as acrylate prepolymer, diluted monomer, and nano-carbon black. The present invention uses the primer layer as the transition layer to realize the stable bonding of the edge strip body and the hot melt adhesive, and has excellent stability, which can well overcome the problem of aging and degumming.

Description

technical field [0001] The invention relates to the technical field of edge banding, in particular to an ABS edge banding and a preparation method thereof. Background technique [0002] Edge banding is one of the commonly used accessories in furniture decoration. It is mostly used to seal the cross-section of furniture panels, so as to protect the panels from adverse effects such as moisture and light in the environment, and prevent formaldehyde volatilization inside the panels. For decoration and beautification. [0003] The ABS edge banding is easy to age during long-term use, and the phenomenon of degumming and warping occurs. Therefore, to improve the structural stability of the edge banding, the material of the edge banding is generally improved to improve the weather resistance, impact resistance and toughness of the edge banding. For example, CN105906988A discloses an ABS edge banding, which uses non-toxic plasticizers, does not contain phthalates, heavy metals and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L33/12C08L51/04C08K13/02C08K3/26C08K5/134C08K5/526C09D4/02C09D4/06C09D7/61C09J7/50C09J7/24C09J123/08C09J7/35
CPCC08K2003/265C08K2201/011C08L55/02C08L2205/03C09D4/06C09J123/0853C09D7/61C09J7/24C09J7/35C09J7/50C08L33/066C08L51/04C08K13/02C08K3/26C08K5/1345C08K5/526
Inventor 朱振伟曾庆景刘培义刘振宇张元桂
Owner SINOWOLF PLASTIC DEKOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap