Reaction-bonding wet-laid polymer waterproofing membrane and preparation method thereof

A technology of polymer waterproofing and wet laying, which is applied in the direction of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., and can solve the problems that affect the waterproof and sealing performance of the coil, cracks in the coil, stretching of the coil, etc. problems, to achieve good elongation, improve low temperature flexibility, and high tensile strength

Active Publication Date: 2019-11-05
GUANGXI YUJIE WATERPROOF & ANTICORROSION MATERIAL CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current reaction-bonded wet-laid polymer waterproof membrane has the following defects in use: if cracks occur on the laying surface, the membrane will be stretched, such as the base layer of the membrane cannot relieve the tension formed during stretching. stress, it is easy to cause cracks or even breakage of the coiled material, which affects the waterproof and sealing performance of the coiled material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reaction-bonding wet-laid polymer waterproofing membrane and preparation method thereof
  • Reaction-bonding wet-laid polymer waterproofing membrane and preparation method thereof
  • Reaction-bonding wet-laid polymer waterproofing membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A reaction-bonded wet-laid polymer waterproofing membrane, comprising a polyolefin thermoplastic elastomer base layer located on the upper layer, a modified asphalt binder layer located in the middle, and an isolation film protective layer located on the lower layer, specifically:

[0028] The adhesive layer is made of the following raw materials: 55 kg of petroleum pitch, 7 kg of coumarone resin as a tackifier, 5 kg of dibutyl phthalate as a plasticizer, and antioxidant tris(2,4-di-tert-butyl benzene) (Base) ester 0.5kg, crosslinking agent vinyl triethoxysilane, 0.5kg, crosslinking accelerator 3-aminopropyltriethoxysilane 0.2kg, filler 20kg;

[0029] Polyolefin thermoplastic elastomer is made of the following raw materials: 5kg of polyisobutylene with a molecular weight of 10,000-100,000, 20kg of copolymer of ethylene and octene with a molecular weight of 1000-3500, 3kg of ethylene-propylene rubber, 10kg of modified polypropylene, antioxidant 1.2kg of bis(dodecanol) thiodip...

Embodiment 2

[0038] A reaction-bonded wet-laid polymer waterproofing membrane, comprising a polyolefin thermoplastic elastomer base layer located on the upper layer, a modified asphalt binder layer located in the middle, and an isolation film protective layer located on the lower layer, specifically:

[0039] The adhesive layer is made of the following raw materials: 58kg petroleum pitch, 8kg coumarone resin as a tackifier, 8kg trimellitate as a plasticizer, and tris(2,4-di-tert-butylphenyl) phosphite as an antioxidant Ester 0.7kg, crosslinking agent vinyl tris (β-methoxyethoxy) silane 1.2kg, crosslinking accelerator 3-aminopropyl triethoxy silane 0.5kg, filler 25kg;

[0040] Polyolefin thermoplastic elastomer is made of the following raw materials: 8kg of polyisobutylene with a molecular weight of 10,000 to 100,000, 25kg of copolymer of ethylene and octene with a molecular weight of 1,000 to 3,500, 4.5kg of ethylene-propylene rubber, 18kg of modified polypropylene, antioxidant 1.6kg of di(dode...

Embodiment 3

[0049] A reaction-bonded wet-laid polymer waterproofing membrane, comprising a polyolefin thermoplastic elastomer base layer located on the upper layer, a modified asphalt binder layer located in the middle, and an isolation film protective layer located on the lower layer, specifically:

[0050] The binder layer is made of the following raw materials: 59kg petroleum pitch, 9kg coumarone resin as a tackifier, 7kg epoxy soybean oil as a plasticizer, and antioxidant tris(2,4-di-tert-butylphenyl) phosphite 0.5~1kg, crosslinking agent tri-tert-butoxyvinylsilane 1.0kg, crosslinking accelerator 3-aminopropyltriethoxysilane 0.5kg, filler 26kg;

[0051] Polyolefin thermoplastic elastomer is made of the following raw materials: 7kg of polyisobutylene with a molecular weight of 10,000-100,000, 22kg of copolymer of ethylene and octene with a molecular weight of 1,000-3500, 4kg of ethylene-propylene rubber, 18kg of modified polypropylene, antioxidant Di(octadecyl thiodipropionate) 1.8kg, anti-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a reaction-bonding wet-laid polymer waterproofing membrane and a preparation method thereof, and belongs to the technical field of waterproofing materials. The waterproofing membrane comprises a polyolefin thermoplastic elastomer base layer located at the upper layer, a modified asphalt adhesive layer located at the middle layer and a separator film protection layer locatedat the lower layer, and the polyolefin thermoplastic elastomer is mainly made from polyisobutylene, an ethylene-octene copolymer, ethylene-propylene rubber, modified polypropylene, an antioxidant, anti-aging agent, a softener and a filler. The preparation method comprises the following steps: respectively preparing a modified asphalt adhesive and a polyolefin thermoplastic elastomer, performing thermocompression bonding, performing thickness-controlled shaping, covering the shaped product with the separator film protection layer, and winding the covered product to obtain the waterproofing membrane. A tire base layer with a good adapting performance to the modified asphalt adhesive is manufactured, and the crack resistance of the tire base layer and the adhesion between the modified asphaltadhesive and the tire base layer are increased to avoid the membrane from cracking, so the waterproof sealing effect of the membrane is ensured.

Description

【Technical Field】 [0001] The invention relates to the technical field of waterproof coiled materials, in particular to a reaction-bonded wet-laid polymer waterproof coiled material and a preparation method thereof. 【Background technique】 [0002] Waterproof coiled material is mainly used in building walls, roofs, tunnels, highways, subways, landfills, etc., to resist external rainwater and groundwater leakage, a flexible building material product that can be rolled into a roll. There is no leakage connection between the project foundation and the building. It is the first barrier for the entire project’s waterproofing and plays a vital role in the entire project. According to its main waterproof components, it can be divided into asphalt waterproof materials and polymer modified materials. There are three types of waterproof membranes and synthetic polymer waterproof membranes. Asphalt waterproof membrane is a rollable sheet-like waterproof material made by impregnating the base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/30C09J7/24C09J195/00C09J11/04C09J11/08C09J11/06C08L23/08C08L23/20C08L23/16C08L23/12C08L23/28C08K9/04C08K3/26C08K3/34C08K5/13C08K13/06E04B1/66E04D5/10E02D31/02
CPCC09J7/30C09J7/243C09J195/00C09J11/04C09J11/08C09J11/06C08L23/0815E04B1/66E04D5/10E02D31/02C08K2003/265C08L2205/035C09J2423/046C09J2495/00C08L45/00C08K5/12C08K9/08C08K3/26C08K3/346C08K5/13C08K13/06C08L23/22C08L23/16C08L23/12C08L23/28
Inventor 孙浩孙向东
Owner GUANGXI YUJIE WATERPROOF & ANTICORROSION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com