Weldable electrical signal copper platinum wire transmission wire
A technology for transmission lines and electrical signals, applied in circuits, conductive materials, conductive materials, etc., can solve problems such as poor tensile and thermal insulation performance, and increased economic costs.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] S1. Preparation of the first mixture: put 8 parts of lubricant, 8 parts of silane coupling agent, 8 parts of antistatic agent and 7 parts of flame retardant into the disperser, stir for 20 minutes, add 5 parts of plasticizer for soaking, After fully soaked, put it into a grinder, grind it for 30 minutes, take it out and put it in a reaction kettle, take it out after heating up to 100°C, and obtain a stabilizer. Mix 10 parts of PVC resin, 10 parts of PVC plastic particles, 15 parts of composite rubber and 7 Add one part of nitrile rubber into the high-speed mixer and stir at a low speed at 300rpm, then add the stabilizer, stir at a high speed at 600rpm, heat up and mix together for 20min at 100°C, take it out, and cool at room temperature reserve;
[0029]S2, the preparation of the second mixture: put 10 parts of oxidized polyvinyl alcohol, 12 parts of anti-ultraviolet powder, 11 parts of alumina and 10 parts of light calcium carbonate into the high-speed mixer, uniforml...
Embodiment 2
[0033] S1, the preparation of the first mixture: put 9 parts of lubricant, 9 parts of silane coupling agent, 9 parts of antistatic agent and 8 parts of flame retardant into the dispersing machine, after stirring for 25min, add 7 parts of plasticizer for soaking, After soaking fully, put it into the grinder, grind it for 30 minutes, take it out and put it into the reaction kettle, heat it up to 100°C, take it out for use, and obtain the stabilizer. Mix 12 parts of PVC resin, 12 parts of PVC plastic particles, 18 parts of composite rubber and 8 The nitrile rubber was added to the high-speed mixer, and stirred at a low speed at a stirring speed of 350 rpm. Then, the stabilizer was added, and the high-speed stirring was carried out at a rotating speed of 650 rpm. use;
[0034] S2, the preparation of the second mixture: put 11 parts of oxidized polyvinyl alcohol, 13 parts of anti-ultraviolet powder, 12 parts of alumina and 13 parts of light calcium carbonate into the high-speed mix...
Embodiment 3
[0038] S1, the preparation of the first mixture: put 10 parts of lubricant, 10 parts of silane coupling agent, 12 parts of antistatic agent and 9 parts of flame retardant into the disperser, stir for 30min, add 8 parts of plasticizer for soaking, After soaking fully, put it into the grinder, grind it for 45 minutes, take it out and put it into the reaction kettle, heat it up to 120°C, and take it out for use to obtain a stabilizer. Mix 15 parts of PVC resin, 15 parts of PVC plastic particles, 20 parts of composite rubber and 9 parts of A portion of nitrile rubber was added to the high-speed mixer, stirred at a low speed, the stirring speed was 400 rpm, then the stabilizer was added, and the high-speed stirring was carried out at a rotating speed of 700 rpm, and the temperature was raised at 120 ℃. backup;
[0039] S2, the preparation of the second mixture: put 12 parts of oxidized polyvinyl alcohol, 15 parts of anti-ultraviolet powder, 13 parts of alumina and 15 parts of light...