Mildew-proof and moisture-proof optical film and preparation method thereof

An optical film, anti-mildew technology, applied in optics, optical components, ion implantation and plating, etc., can solve the problem of lack of effective solutions, and achieve the improvement of moisture-proof and mildew-proof performance, compactness, and compactness. Effect

Active Publication Date: 2019-11-22
HUBEI JIUZHIYANG INFRARED SYST CO LTD
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many methods reported in the literature for moisture-proof and mildew-proof photoelectric equipment and a complete range of related organic reagents. However, there are no effective solutions for the moisture-proof and mildew-proof of optical protection windows at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mildew-proof and moisture-proof optical film and preparation method thereof
  • Mildew-proof and moisture-proof optical film and preparation method thereof
  • Mildew-proof and moisture-proof optical film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The moisture-proof and mildew-proof optical film involved in the present invention is realized on a Leybold SYRUSpro1110 vacuum coating machine; the equipment is equipped with an APSII plasma source, an electron beam evaporation system, and an IC5 film thickness monitor.

[0038] refer to Figure 1 to Figure 3 As shown, the present invention discloses a moisture-proof and mildew-proof optical film with high transmittance, including a substrate 1, a high-density anti-reflection film system main body 2 and a hard wear-resistant protective layer 3 evaporated on the substrate 1 in sequence , the first hydrophobic film layer 4 and the second hydrophobic film layer 5; the substrate 1 is glass, sapphire, zinc sulfide or silicon wafer of the same material as the optical window, so the substrate 1 of the present invention can be Lay on the optical window and form an integral body with it, and the optical window can also be used as the substrate 1 to evaporate other film layers seq...

Embodiment 2

[0044] A high-efficiency anti-reflection film with moisture-proof and mildew-proof functions coated on a K9 glass light window, the size . The technical requirements are as follows: , incident angle 0-30 0 . The coating sample passed the high and low temperature, constant humidity, adhesion and severe friction tests specified in GJB2485-1995 at one time. At the same time, it can also withstand the mold test specified in GJB150.10A-2009.

[0045] First of all, according to the above technical requirements, the optimal design of the film structure is carried out, and the results are as follows:

[0046]

[0047] Among them, the material of the hard wear-resistant protective layer 3 is selected as SiO 2 , a-f are the physical thickness of the film layer, respectively, M1 and M2 are both fluorine-silicon-based organic hydrophobic film layers, and their physical thickness is 6.0nm. The physical thickness of other film layers is as follows:

[0048] a-70.25nm; b-82.66nm;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a moisture-proof and mildew-proof optical film. The mildew-proof and moisture-proof optical film comprises a substrate, a high-density antireflection film system main body, a hard wear-resistant protective layer, a first hydrophobic film layer and a second hydrophobic film layer, wherein the high-density antireflection film system main body, the hard wear-resistant protective layer, the first hydrophobic film layer and the second hydrophobic film layer are sequentially evaporated on the substrate in a vacuum environment. The invention further discloses a preparation process method of the mildew-proof and moisture-proof optical film. The mildew-proof and moisture-proof optical film and the preparation method thereof have the typical characteristics that the transmittance of a coated optical window is high, the surface is smooth and wear-resistant, the moisture-proof performance and the mildew-proof performance are good, and the preparation process is easy to transplant. The mildew-proof and moisture-proof optical film and the preparation method thereof can effectively solve the moisture-proof and mildew-proof problems in the actual application process of optical lens, and can be widely applied to military optoelectronic equipment, precision optical instruments, outdoor monitoring cameras and other military and civilian optoelectronic technology fields ina high-humidity environment.

Description

technical field [0001] The invention belongs to the technical field of optical films, and in particular relates to a moisture-proof and mildew-proof optical film with high transmittance applied to protective windows such as glass and optical crystals, and a preparation method thereof. Background technique [0002] In a variety of harsh environmental conditions, the growth of mold and the erosion of moisture are one of the important factors that cause the protection window of optoelectronic equipment to be corroded and damaged. In fact, mildew on the surface of the optical window is essentially the result of destructive chemical corrosion. Once dense mildew spots are formed, they cannot be removed. Over time, it will directly affect the optical performance of the system and the service life of the optical window. [0003] Studies have shown that molds will continue to secrete corrosive toxins during the growth of glass or optical crystals. However, conventional AR coatings c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/30C23C14/08C23C14/10C23C14/12C23C14/02C23C14/58G02B1/14G02B1/18
CPCC23C14/022C23C14/083C23C14/10C23C14/12C23C14/30C23C14/5833G02B1/14G02B1/18
Inventor 姚细林王航张天行何光宗薛俊
Owner HUBEI JIUZHIYANG INFRARED SYST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka