Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of nanometer cerium zirconium composite oxide and its catalytic no x Application in Reduction Reaction

A composite oxide, zirconium oxide technology, applied in the direction of metal/metal oxide/metal hydroxide catalyst, zirconium compound, catalyst activation/preparation, etc., can solve the problem of affecting the conversion efficiency of catalyst pollutants, low surface activity energy, The problem of high surface activity, to achieve the effect of excellent low temperature catalytic activity and high temperature stability, excellent catalytic advantage, good catalytic effect

Active Publication Date: 2021-11-02
SHANDONG SINOCERA FUNCTIONAL MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the size is too small, the surface activity is too high, and it is easy to agglomerate, which will lead to a sharp drop in the specific surface area after high temperature aging; if the size is too large, the initial specific surface area is too low, and there are fewer active sites. At the same time, the surface activity energy is low. The above two factors will affect the conversion efficiency of the catalyst to pollutants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nanometer cerium zirconium composite oxide and its catalytic no <sub>x</sub> Application in Reduction Reaction
  • A kind of nanometer cerium zirconium composite oxide and its catalytic no <sub>x</sub> Application in Reduction Reaction
  • A kind of nanometer cerium zirconium composite oxide and its catalytic no <sub>x</sub> Application in Reduction Reaction

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The embodiment of the present invention provides a preparation method of nano-cerium-zirconium composite oxide, the specific steps include:

[0052] S1, dissolve the salts of cerium, zirconium, lanthanum and praseodymium or yttrium respectively, set the volume to a total concentration of 40-140g / L, stir until clear, and continue to stir at a low speed for 0.5h;

[0053] S2, drop an alkaline precipitant into the above solution, the alkaline precipitant is one or more of ammonia, sodium hydroxide, amines, preferably ammonia, and then adjust the pH of the solution to 1.5- 2;

[0054] S3, introducing the above solution into a high-pressure reactor, and hydrolyzing it at 150° C. for 10-20 hours;

[0055] S4, adding an alkaline precipitant dropwise to the precursor slurry obtained in S3 to adjust the pH to 8-10;

[0056] S5, introducing the precursor slurry obtained in S4 into an autoclave, and performing a hydrothermal reaction at 150° C. for 6-10 hours;

[0057] S6, beat...

Embodiment 1

[0060] Embodiment 1 provides a composition based on cerium oxide, zirconia, lanthanum oxide, and yttrium oxide, and the composition is CeO in proportion by weight of the oxide 2 28%, ZrO 2 62%, La 2 o 3 5%, Y 2 o 3 5%.

[0061] The equipment used in this embodiment is a 10L polytetrafluoro-lined high-pressure reactor, the solution filling degree is 80%, and the total concentration of oxides is 40g / l. Its preparation method is as follows:

[0062] Get 574g of zirconium oxynitrate, 54.2g of yttrium nitrate, dissolve with 2000ml of deionized water until clear to obtain solution A;

[0063] Take 278.5g of ammonium cerium nitrate and 42.7g of lanthanum nitrate into solution A, stir until clear, adjust the pH of solution A to 1.5-1.6 with ammonia water in a water bath at 50°C, set the volume to 8000ml, and introduce In the vinyl fluoride-lined pressure melting bomb, hydrothermal hydrolysis reaction at 150°C for 20 hours, lowered to room temperature and adjusted pH to 9.5-9...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a nano-cerium-zirconium composite oxide, which comprises cerium oxide, zirconium oxide and at least one oxide of a rare earth metal element other than cerium, and the mass fraction of the cerium oxide contained in the composite oxide is the same as The ratio of the mass fraction of zirconium oxide is less than 1; the composite oxide has a particle size of 5-20nm and an oxygen storage capacity of at least 1.10mmol[O] / g after heat treatment at 750°C for 4-8 hours. The nano-cerium-zirconium composite oxide obtained by the invention has appropriate micro-nano particle size and high oxygen storage capacity. Experiments have shown that the T 50 , T 90 They are about 150°C and 200°C respectively, and the T after aging at 1100°C for 4 hours 50 and T 90 At about 170°C and 220°C, respectively, it shows excellent low-temperature catalytic activity and anti-aging activity.

Description

technical field [0001] The invention relates to the technical field of mobile source tail gas purification catalysis, in particular to a nano-cerium-zirconium composite oxide and its catalytic performance in NO X Applications in reduction reactions. Background technique [0002] Mobile source is the abbreviation of mobile air pollution source, which can produce a large amount of pollutants, for example, the cold start phase of the engine can emit a large amount of nitrogen-containing compounds, such as nitrogen monoxide (NO), nitrogen dioxide (NO 2 ) and other nitrogen oxides (NO X ) and ammonia (NH 3 )Wait. At present, the main means to solve the cold start exhaust problem is to install a purifier with a built-in catalyst at the exhaust emission of the vehicle. [0003] Cerium-zirconium composite oxides are widely used in the field of automobile exhaust catalysis. In addition to participating in the catalytic reaction, the cerium-zirconium composite oxide also has the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G25/00B82Y40/00B82Y30/00B01J23/63B01J37/10B01J37/02B01J37/03B01D53/94B01D53/56B01D53/86
CPCB01D53/8628B01D53/9413B01D2258/012B01J23/002B01J23/63B01J37/0201B01J37/031B01J37/10B01J2523/00B82Y30/00B82Y40/00C01G25/006C01P2004/04C01P2004/64C01P2004/82B01J2523/36B01J2523/3706B01J2523/3712B01J2523/48
Inventor 宋锡滨邢晶刘洪升潘光军
Owner SHANDONG SINOCERA FUNCTIONAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com