A kind of cerium-zirconium composite oxide with high specific surface area and its preparation method and application

A composite oxide and oxide technology, which is applied in the field of cerium-zirconium solid solution with high specific surface area and its preparation, can solve the problems that the performance cannot meet the requirements of emission regulations, the grain size of cerium-zirconium composite oxide is large, and the anti-aging ability is weak. Achieve the effects of large pore volume, good low-temperature catalytic activity, and high oxygen storage capacity

Active Publication Date: 2021-11-19
SHANDONG SINOCERA FUNCTIONAL MATERIAL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the crystal grains of the cerium-zirconium composite oxide prepared by the co-precipitation method are larger, and the specific surface area is lower. The anti-aging ability is weak, and its performance cannot meet the requirements of increasingly stringent emission regulations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cerium-zirconium composite oxide with high specific surface area and its preparation method and application
  • A kind of cerium-zirconium composite oxide with high specific surface area and its preparation method and application
  • A kind of cerium-zirconium composite oxide with high specific surface area and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Example 1 provides a composition comprising CeO 2 40%, ZrO 2 50%, La 2 o 3 5%, Pr 6 o 11 5% cerium-zirconium composite oxide, prepared by the following method:

[0054] Take 629g zirconium oxychloride and 62g ammonium cerium nitrate and add it into 1500mL ultrapure water, and add ammonia water dropwise to the solution to adjust the pH to 6.5 to obtain the sol of the first precipitate; , 65g of lanthanum nitrate and 58g of praseodymium nitrate were dissolved and mixed with ammonia water and added dropwise to the above-mentioned first precipitate, and the pH was adjusted to 10 to obtain the second precipitate of cerium hydroxide-zirconium hydroxide-lanthanum hydroxide-praseodymium hydroxide thing.

[0055] Filter and wash the above precipitate for at least 3 times, then add it to a 10L reaction kettle, heat at 210°C for 36 hours to obtain a composite oxide of ceria-zirconia-lanthanum oxide-praseodymium oxide, then add 22-300g of lauric acid, and oxidize at 850°C...

Embodiment 2

[0061] Example 2 provides a composition comprising CeO 2 20%, ZrO 2 73%, La 2 o 3 2%, Nd 2 o 3 5% cerium-zirconium composite oxide, prepared by the following method:

[0062] Take 918g of zirconium oxychloride and 31g of cerium ammonium nitrate and add them to 1500mL of ultrapure water, and add ammonia water dropwise to the solution to adjust the pH value to 6.5 to obtain the sol of the first precipitate; take 280g of cerium ammonium nitrate, 102g of oxychloride Zirconium, 26g of lanthanum nitrate and 65g of neodymium nitrate are dissolved and mixed with aqueous ammonia and added dropwise to the above-mentioned first precipitate, and the pH is adjusted to 11 to obtain the second product of cerium hydroxide-zirconium hydroxide-lanthanum hydroxide-neodymium hydroxide Precipitate.

[0063] Filter and wash the above precipitate for at least 3 times, then add it to a 10L reaction kettle, heat at 210°C for 36 hours to obtain a composite oxide of ceria-zirconia-lanthanum ox...

Embodiment 3

[0066] Example 3 provides a composition comprising CeO 2 25%, ZrO 2 60%, La 2 o 3 3%, Y 2 o 3 12% cerium-zirconium composite oxide, prepared by the following method:

[0067] Take 754g of zirconium oxychloride and 39g of cerium ammonium nitrate and add them to 1500mL of ultrapure water, and add ammonia water dropwise to the solution to adjust the pH to 6.5 to obtain the sol of the first precipitate; take 350g of cerium ammonium nitrate, 84g of cerium oxychloride , 26g of lanthanum nitrate and 35g of yttrium nitrate were dissolved and mixed with ammonia water and added dropwise to the above-mentioned precipitate to adjust the pH=11 to obtain the second precipitate of cerium hydroxide-zirconium hydroxide-lanthanum hydroxide-yttrium hydroxide.

[0068] Filter and wash the above precipitate for at least 3 times, then add it to a 10L reaction kettle, heat at 210°C for 36h to obtain a composite oxide of ceria-zirconia-lanthanum oxide-yttrium oxide, then add 22-300g of lauri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The present invention provides a high specific surface area cerium-zirconium composite oxide, comprising cerium oxide, zirconium oxide and at least one oxide of rare earth metal elements other than cerium, and the composite oxide is heat-treated at 850°C for 4-8 hours After, having at least 80m 2 / g specific surface area, 0.50~0.60mL / g pore volume, 500~1200μmol O 2 Oxygen storage capacity per gram, and the pore diameter showing a distribution of two pore groups, wherein the diameter of the first pore group is concentrated in the range of 1-8nm, and the diameter of the second pore group is concentrated in the range of 20-60nm. The cerium-zirconium composite oxide provided by the invention has a higher specific surface area and pore volume distribution than the composite oxide prepared by the existing method, shows better low-temperature catalytic activity, and can be used to catalyze hydrocarbons, Carbon oxides and / or nitrogen oxides. The present invention also provides a method for preparing cerium-zirconium composite oxides, which can prepare and obtain composite oxides with more uniform element lattice doping distribution and no phase separation. Research is of great significance.

Description

technical field [0001] The invention relates to the technical field of tail gas purification catalyst materials, in particular to a high specific surface area cerium-zirconium solid solution and its preparation method and application. Background technique [0002] Cerium-zirconium solid solution is used as an oxygen storage material, and its performance determines the catalytic effect of the three-way catalyst. A higher specific surface area is not only related to oxygen storage capacity and anti-aging ability, but also improves the utilization rate of precious metals and reduces the cost of three-way catalysts. [0003] At present, the methods used to prepare cerium-zirconium composite oxides at home and abroad mainly include high-energy ball milling method, co-precipitation method, sol-gel method and hydrothermal method, among which co-precipitation method and hydrothermal method are the main methods of industrial production. However, the crystal grains of the cerium-zirc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/10B01J35/10B01D53/86B01D53/62B01D53/56B01D53/72
CPCB01D53/62B01D53/86B01D53/8628B01D53/8668B01D2257/702B01J23/002B01J23/10B01J35/1014B01J35/1042B01J35/1061B01J2523/00B01J2523/3706B01J2523/3712B01J2523/48B01J2523/3718B01J2523/3725B01J2523/36
Inventor 宋锡滨朱国强潘光军焦英训
Owner SHANDONG SINOCERA FUNCTIONAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com