Photo-catalytic composite filtration sheet with water quality purification function and preparation method thereof

A composite filtration and water purification technology, which is applied in chemical instruments and methods, filtration separation, filtration treatment, etc., can solve the problems of porous carrier water permeability, mechanical properties, catalyst adhesion strength, light-receiving performance, etc., so as to improve the strength of the matrix and surface erosion resistance, high compressive strength, and the effect of improving photocatalytic efficiency

Active Publication Date: 2020-01-14
HOHAI UNIV
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its wide application is limited due to the water permeability, mechanical properties, adhesion strength of catalysts on its surface, and light-receiving performance of porous supports.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photo-catalytic composite filtration sheet with water quality purification function and preparation method thereof
  • Photo-catalytic composite filtration sheet with water quality purification function and preparation method thereof
  • Photo-catalytic composite filtration sheet with water quality purification function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for preparing a photocatalytic composite filter with water purification function, comprising the following steps:

[0036] (1) Soak the quartz sand in water and wash it twice, drain the quartz sand and put it into NaOH solution to stir and soak, then drain the quartz sand and put it in an oven for drying for later use;

[0037] (2) Mix melamine and glass glaze powder and put them into a ball mill to evenly mix to form mixed powder 1, and sieve it for later use;

[0038] (3) Put the quartz sand, glass glaze powder and water into the mixer and mix evenly to form the mixed powder 2, take it out for later use;

[0039] (4) The mold cylinder 4 is sealed and fixed on the upper surface of the mold base 7, and the inner wall of the mold cylinder 4, the upper surface of the mold base 7 and the upper and lower sides of the separator 6 are all brushed with a layer of boron nitride release agent, and adhered to a layer graphite paper;

[0040](5) First, use a vibrating s...

Embodiment 2

[0056] The difference from Example 1 is that the particle size of the quartz sand in step (1) is changed to 5-10 mesh, and other preparation steps and material ratios remain unchanged, and a photocatalytic composite filter with high water permeability can be obtained , suitable for occasions with higher water passing requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a photo-catalytic composite filtration sheet with a water quality purification function and the photo-catalytic composite filtration sheet with the water quality purification function. A mold is divided into independent units by using a plurality of division sheets, each unit is filled according to a manner that a layer of a quartz sand and glass glaze powder mixed material is sandwiched between two layers of a melamine and glass glaze powder mixed material, the mold is placed in a vacuum hot-pressing furnace, heat preservation and pressure maintaining is performed for 120 min under conditions that a temperature is 550+ / -10 DEG C, a pressure is 4.5-5 MPa, and a vacuum degree is 10-15 Pa, and multiple composite filtration sheets can be obtained after cooling with the furnace. The prepared composite filtration sheet has integrated functions of photo-catalytic degradation and filtration adsorption, also has excellent water permeability, corrosion resistance and erosion resistance, and is suitable for purification treatment of high-concentration sewage.

Description

technical field [0001] The invention relates to a photocatalytic composite filter with water purification function and a preparation method of the photocatalytic composite filter with water purification function, and belongs to the technical field of composite material forming. Background technique [0002] The continuous progress of the human industrialization process has brought us economic benefits, but it has also caused serious damage to the environment. A large amount of industrial wastewater and agricultural sewage are discharged into rivers, lakes and oceans without treatment or incomplete treatment. These sewage It has the characteristics of many types of pollution, complex components, and poor biodegradability. Due to the stable physical and chemical properties of a large number of pollutants, it is difficult to degrade and remove them in a short time by ordinary chemical or biological treatment methods, so the treatment efficiency is low. Due to the existence of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D39/14C02F1/00C02F1/28C02F1/30C02F1/72
CPCB01D39/14C02F1/001C02F1/28C02F1/30C02F1/725
Inventor 饶磊王沛芳王平凡
Owner HOHAI UNIV