Bio-based asphalt modifier and preparation method thereof

An asphalt modifier, bio-based technology, applied in building structures, building components, building thermal insulation materials, etc., to achieve the effects of good compatibility, wide sources and good compatibility

Active Publication Date: 2020-01-14
SHANDONG JIANZHU UNIV
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention proposes a bio-based asphalt modifier and its preparation method, which overcomes the shortcomings and deficiencies of existing asphalt modifiers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bio-based asphalt modifier and preparation method thereof
  • Bio-based asphalt modifier and preparation method thereof
  • Bio-based asphalt modifier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The raw materials used in the bio-based asphalt modifier are as follows: 70wt% of biomass-based matrix material, 15wt% of olefin-based rigid polyester modifier, 1wt% of auxiliary agent, 12wt% of interface enhancer, and 2wt% of nano inorganic filler.

[0030] Wherein, include coupling agent and initiator in the auxiliary agent, coupling agent is made up of silane coupling agent and titanate coupling agent, and its mass ratio is 1:1; Initiator is benzoyl peroxide tert-butyl ester initiation agent, the mass ratio of silane coupling agent, titanate coupling agent and benzoyl tert-butyl peroxide initiator is 1:1:1; the interface enhancer is a carbon nanotube interface enhancer with a mesh number of 3nm; The inorganic filler can be nanometer zinc oxide with a mesh number of 15nm.

[0031] The preparation method of the bio-based asphalt modifier is as follows: ①Weigh the biomass-based matrix material according to the above ratio, add the polyester modifier and additives in seque...

Embodiment 2

[0054] The raw materials used in the bio-based asphalt modifier are as follows: 65wt% of biomass-based matrix material, 18wt% of polyester modifier, 1wt% of auxiliary agent, 14wt% of interface enhancer, and 2wt% of nano inorganic filler.

[0055] The specific composition and parameters of each component are consistent with Example 1, and the preparation method, preparation process and performance test are consistent with Example 1.

Embodiment 3

[0057] Bio-based asphalt modifier components are consistent with Example 2. The polyester modifier is an olefin-based rigid polyester modifier. Among them, the auxiliary agent includes a coupling agent and an initiator, the coupling agent is composed of a silane coupling agent and a titanate coupling agent, and its mass ratio is 1:1; the initiator is a methyl ethyl ketone peroxide initiator; the interface enhancer It is nano-graphene with an average particle size of 3nm and a height of 0.7nm; the nano-inorganic filler can be nano-calcium carbonate with a mesh size of 30nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a bio-based asphalt modifier and a preparation method thereof, wherein the bio-based asphalt modifier comprises, by mass, 60-80 wt% of a biomass-based matrix material, 10-20 wt%of a polyester modifier, 0.5-2 wt% of an auxiliary agent, 10-15 wt% of an interface enhancer and 2-10 wt% of a nanometer inorganic filler. According to the invention, the novel biomass-based organic-inorganic composite high-modulus additive is prepared by adopting simple one-step high-temperature melt blending modification; the novel biomass-based high-modulus additive has the outstanding advantages of excellent performance, low cost, good compatibility with asphalt and the like, and a series of products can be developed according to different engineering requirements; and the high-modulus asphalt has the outstanding advantages of high complex shear modulus, large anti-rut factor, good anti-fatigue performance, strong elastic recovery capability and the like.

Description

technical field [0001] The invention relates to the technical field of modified asphalt, in particular to a bio-based asphalt modifier and a preparation method thereof. Background technique [0002] With the development of my country's national economy, the traffic volume has increased rapidly, and the mileage of my country's highways has reached the first place in the world. Because asphalt pavement has the characteristics of good driving comfort, fast construction speed, and convenient maintenance, it is more and more widely used in pavement structures. At the same time, heavy and overloaded road traffic is becoming more and more common. In addition, the frequency of extreme and continuous high-temperature climates in many places is increasing, and the rutting disease of asphalt pavement is becoming more and more serious. It has become the first of several major diseases, directly affecting driving comfort and performance. safety. According to incomplete statistics, amon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/00C08L67/00C08L95/00C08K3/22C08K3/26
CPCC08K2003/2296C08K2003/265C08K2201/011C08L91/00C08L95/00C08L2201/08C08L2205/03C08L67/00C08K3/22C08K3/26
Inventor 任瑞波赵品晖孟伟坤徐强耿立涛王立志周浩李志刚
Owner SHANDONG JIANZHU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More