Preparation method for brazed aluminum honeycomb board

A honeycomb panel and brazing technology, which is applied in the field of preparation of brazed aluminum honeycomb panels, can solve the problems of slow thermal conductivity, the mechanical properties of honeycomb panels need to be improved, and high energy consumption, so as to achieve reliable and simple production and solve aluminum brazing Risk Effects of Honeycomb Panels

Active Publication Date: 2020-01-31
佛山市桐立新材料科技有限公司
View PDF14 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the shortcomings of brazing honeycomb panels are: slow thermal conductivity, high energy consumption, desoldering due to high oxygen content in the furnace, difficulty in large-scale production, and the mechanical properties of honeycomb panels need to be improved due to the influence of welding quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for brazed aluminum honeycomb board
  • Preparation method for brazed aluminum honeycomb board
  • Preparation method for brazed aluminum honeycomb board

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] In order to solve the above problems, the invention provides a preparation method of brazing aluminum honeycomb panels, comprising the following steps:

[0034] S1. Select upper skin, lower skin and edge banding profiles;

[0035] S2. making brazing honeycomb core;

[0036] S3. Coating the upper skin and the lower skin in step S1 with the first brazing flux respectively; coating the edge sealing profile in step S1 with the first brazing paste;

[0037] S4. Put the upper skin, the lower skin, the edge banding profile in the step S3, and the brazing honeycomb core in the step S2 on the special tooling in the form of a sandwich, and flatten to obtain a semi-finished product;

[0038] S5. Welding the semi-finished product obtained in step S4 in a brazing furnace.

[0039] Step S1

[0040] In the present application, the upper skin is located on the upper surface of the brazed honeycomb core, and the lower skin is located on the lower surface of the brazed honeycomb cor...

Embodiment approach

[0043] As an embodiment, the composite aluminum alloy plate is selected from 4343-3003 double-composite aluminum alloy plate, 4343-3003-6 series four-composite aluminum alloy plate, 5 series-3003 four-composite aluminum alloy plate, 7 series-3003 quadruple At least one of the composite aluminum alloy plates.

[0044] In the 4343-3003 double composite plate, the thickness of the 4343 aluminum alloy is 8-15% of the total thickness of the double composite aluminum alloy plate, and the rest is 3003 aluminum alloy.

[0045] The 4343 aluminum alloy refers to an alloy whose main chemical composition is Si (6.8-8.2wt%) and the rest is Al. It has a low melting point and good fluidity, and it will become solder after soldering.

[0046] The 3003 aluminum alloy refers to an Al-Mn alloy, and its chemical composition is mainly: 0.6wt% silicon, 0.7wt% iron, 0.05-0.2wt% copper, 1.0-1.5wt% manganese, 0.1wt% zinc, and 0.15wt% others , Aluminum allowance.

[0047] The "5 series" refers to 5 ...

Embodiment 1

[0158] A preparation method for brazing aluminum honeycomb panels, comprising the following steps:

[0159] S1. Select upper skin, lower skin and edge banding profiles;

[0160] S2. making brazing honeycomb core;

[0161] S3. Spray the first brazing flux on the upper and lower skins in step S1 by electrostatic spraying; scrape and coat the first brazing paste on the edge sealing profile in step S1;

[0162] S4. Place the upper skin, lower skin, edge banding profile in step S3, and the brazing honeycomb core in step S2 on the graphite plate in the form of a sandwich, and flatten to obtain a semi-finished product;

[0163] S5. Welding the semi-finished product obtained in step S4 in a brazing furnace.

[0164] In step S1, the materials of the upper skin and the lower skin are independently 4343-3003 double-composite aluminum alloy plates; the thickness of the 4343 aluminum alloy is 10% of the total thickness of the double-composite aluminum alloy plates, and the rest is 3003 a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of manufacturing of honeycomb boards, and in particular relates to a preparation method for a brazed aluminum honeycomb board. The preparation method of the brazed aluminum honeycomb board comprises the following steps: S1, selecting upper skin, lower skin and an edge sealing profile; S2, manufacturing a brazed honeycomb core; S3, separately coating first brazing flux to the upper skin and the lower skin in the S1 separately, and coating first soldering paste to the edge cutting profile in the S1; S4, putting the upper skin, the lower skin and the edge sealing profile in the S3 and the brazed honeycomb core in the S2 on a special tool in a form of a sandwich, and planishing the same to obtain a semi-finished product; and S5, welding the semi-finished product obtained in the S4 in a brazing furnace to obtain the brazed aluminum honeycomb board. The preparation method solves the problems that the welding strength is low, the heat conductivityis low, the mechanical property of the honeycomb board is poor and the like in the welding process. By transforming the brazing furnace, the risk of the brazed aluminum honeycomb board which is weldedtightly in a large area is solved fully, so that the brazed aluminum honeycomb board is manufactured more reliably and simply, and the brazed aluminum honeycomb board can be produced on a large scale.

Description

technical field [0001] The invention belongs to the technical field of honeycomb panel production, and in particular relates to a preparation method of a brazed aluminum honeycomb panel. Background technique [0002] Aluminum honeycomb panel refers to the aluminum honeycomb core or circular aluminum honeycomb core made of aluminum foil into a regular hexagonal honeycomb shape. Large airports, ceilings of subway and high-speed rail stations, rail transit interiors, aerospace and other fields. [0003] Advantages of aluminum honeycomb panel composite materials: light weight, high flat compressive strength, high flat tensile strength, light weight, excellent compression and earthquake resistance, and high flatness of the plane. [0004] The aluminum honeycomb panels currently on the market are all bonded with polymer adhesives, such as the invention patent application number 201810211802.5, the manufacturing method of which is to prepare the honeycomb core is: 1) Use ultrasoni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B23K1/008
CPCB23K1/008B23P15/00
Inventor 欧阳伟李鹏钟永佳任碧野
Owner 佛山市桐立新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com