Stranded wire for high-strength steel and preparation process thereof

A preparation process, high-strength steel technology, applied in the direction of manufacturing tools, welding equipment, welding media, etc., can solve the problems of insufficient strength, achieve the effect of not affecting strength and toughness, beautiful shape, and improving impact toughness

Inactive Publication Date: 2020-03-31
河北联之捷焊业科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of lightweight technology for car bodies, when the strength of the steel plate is 1000MPa, the heat input to the steel plate during the welding process of the solid welding material is larger than that of the flux-cored wire, and the strength of the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stranded wire for high-strength steel and preparation process thereof
  • Stranded wire for high-strength steel and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A stranded welding wire for high-strength steel comprises a flux core and an outer skin covered on the outside of the flux core, and the weight ratio of the flux core to the skin is 2.5:10; the flux core comprises by weight percentage: graphite powder 4%, nano-titanium dioxide 0.2% , rutile 20%, calcium oxide 2%, tungsten powder 3%, metal chromium 0.8%, sodium fluoride 4.2%, lithium fluoride 0.12%, yttrium trioxide 0.4%, metal manganese 1%, potassium titanate 2%, Nickel powder is 4%, Ti-Nb-V-Fe alloy is 2%, and the balance is iron powder.

[0020] Among them, in the Ti-Nb-V-Fe alloy, titanium element accounts for 2% by mass, niobium element accounts for 18% by mass, and vanadium element accounts for 8% by mass.

[0021] The above-mentioned preparation process of stranded welding wire for high-strength steel includes rolling the outer skin into a U-shaped groove, placing the flux core in the U-shaped groove, and extruding and rolling into an O-shaped ...

Example Embodiment

[0022] Example 2

[0023] A stranded welding wire for high-strength steel, comprising a flux core and a sheath wrapped on the outside of the flux core, the weight ratio of the flux core to the sheath is 3.5:10; the flux core comprises by weight percentage: graphite powder 2%, nano-titanium dioxide 1% , rutile 10%, calcium oxide 5%, tungsten powder 1%, metal chromium 1.8%, sodium fluoride 2.5%, lithium fluoride 0.2%, yttrium trioxide 0.1%, metal manganese 2%, potassium titanate 1%, The nickel powder is 10%, the Ti-Nb-V-Fe alloy is 1.2%, and the balance is iron powder.

[0024] Among them, in the Ti-Nb-V-Fe alloy, the titanium element accounts for 4% by mass, the niobium element accounts for 14% by mass, and the vanadium element accounts for 12% by mass.

[0025] The above-mentioned preparation process of stranded welding wire for high-strength steel includes rolling the outer skin into a U-shaped groove, placing the flux core in the U-shaped groove, and extruding and rolling i...

Example Embodiment

[0026] Example 3

[0027] A stranded welding wire for high-strength steel comprises a flux core and a sheath wrapped on the outer side of the flux core, the weight ratio of the flux core and the sheath is 2.8:10; the flux core comprises, by weight percentage: graphite powder 3.5%, nano-titanium dioxide 0.4% , rutile 18%, calcium oxide 3%, tungsten powder 2.5%, metal chromium 1%, sodium fluoride 4%, lithium fluoride 0.14%, yttrium trioxide 0.3%, metal manganese 1.3%, potassium titanate 1.6%, The nickel powder is 6%, the Ti-Nb-V-Fe alloy is 1.8%, and the balance is iron powder.

[0028] Among them, in the Ti-Nb-V-Fe alloy, the titanium element accounts for 2.5% by mass, the niobium element accounts for 17% by mass, and the vanadium element accounts for 9% by mass.

[0029] The above-mentioned preparation process of stranded welding wire for high-strength steel includes rolling the outer skin into a U-shaped groove, placing the flux core in the U-shaped groove, and extruding and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stranded wire for high-strength steel. The stranded wire comprises a medicine core and a sheath coated on the outer side of the medicine core, wherein the medicine core comprises the following components in percentage by weight, 2% to 4% of graphite powder, 0.2% to 1% of nano titanium dioxide, 10% to 20% of Rutile, 2% to 5% of calcium oxide, 1% to 3% of Tungsten Powder, 0.8% to 1.8% of Metal Chromium, 2.5% to 4.2% of sodium fluoride, 0.12% to 0.2% of lithium fluoride, 0.1% to 0.4% of Yttria, 1% to 2% of Metal Manganese, 1% to 2% of potassium titanate, 4% to 10% of Nickel Powder, 1.2% to 2% of Ti-Nb-V-Fe Alloy, and the balance is iron powder. The preparation process comprises the following steps of rolling a sheath into a U-shaped groove, placing the medicine corein the U-shaped groove, and extruding and rolling to form an O-shaped closed tube containing a medicine core; and welding the O-shaped closed tube by contact welding, rolling into a disk, carrying outsurface acidification treatment, carrying out rough drawing, carrying out surface acidification treatment, and carrying out fine drawing, and removing grease to obtain the stranded welding wire for high-strength steel.

Description

technical field [0001] The invention relates to the technical field of flux-cored welding wire, in particular to a stranded welding wire for high-strength steel and a preparation process thereof. Background technique [0002] With the continuous development of my country's heavy-duty vehicle industry, steel is still the main material for the manufacture of heavy-duty vehicles, but its connotation has undergone major changes, from the previous mild steel to high-strength steel plates, combined with advanced steel processing technology , the strength of steel materials continues to increase. While realizing the lightweight of the car body, it also puts forward strict requirements on the matching high-strength and high-toughness welding consumables. [0003] With the development of lightweight technology for the body, when the strength of the steel plate is 1000MPa, the heat input to the steel plate during the welding process of the solid welding consumables is greater than that...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/02B23K35/30B23K35/40
CPCB23K35/0266B23K35/0283B23K35/3053B23K35/40
Inventor 梁裕
Owner 河北联之捷焊业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap