A kind of ternary modified biochar for removing fluorine in water and preparation method thereof

A biochar modification technology, which is applied to water pollutants, chemical instruments and methods, and other chemical processes, can solve problems such as the unsatisfactory defluorination efficiency of loaded lanthanum-aluminum modified biochar, and the inability to fully meet application requirements. , to achieve the effects of broadening the scope of application, improving the performance of fluoride removal, and increasing the anion exchange capacity

Active Publication Date: 2022-05-17
NANTONG UNIVERSITY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the modified liquid of lanthanum and aluminum salt is used to modify the biochar. The commonly used modification method is the impregnation-drying-sintering method. The fluoride removal efficiency of the modified biochar loaded with lanthanum and aluminum is still not ideal. Moreover, due to the low isoelectric point and anion exchange capacity, the applicable pH range of this material is in acidic water bodies, and its use is still limited, which cannot fully meet the needs of practical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) The rice straw is subjected to high-temperature carbonization treatment to obtain rice straw biochar.

[0022] (2) Dissolve 2.16g of lanthanum nitrate, 1.62g of ferric chloride and 2g of aluminum chloride in 100mL of deionized water to prepare a ternary modifier mixture, then add 1g of rice straw biochar and stir to obtain biochar - A mixed stock solution of modifiers.

[0023] (3) Use a peristaltic pump to drop a sodium hydroxide solution with a concentration of 3 mol / L to the obtained mixed stock solution containing biochar-modifier at a speed of 0.2 mL / min until the pH is 7.5, and continue stirring for 12 hours to obtain Modified product liquid.

[0024] (4) The obtained modified product liquid is subjected to centrifugation, and the precipitate obtained by the centrifugation is washed and then dried at a temperature of 105° C. to obtain a three-component modified biochar of rice straw.

[0025] (5) Fluorine adsorption experiment was carried out on the obtained...

Embodiment 2

[0028] (1) The rice straw is subjected to high-temperature carbonization treatment to obtain rice straw biochar.

[0029] (2) Dissolve 4.33g of lanthanum nitrate, 3.24g of ferric chloride and 4g of aluminum chloride in 100mL of deionized water to prepare a ternary modifier mixture, then add 1g of rice straw biochar for stirring to obtain biochar - A mixed stock solution of modifiers.

[0030] (3) Use a peristaltic pump to drop a sodium hydroxide solution with a concentration of 4mol / L to the obtained mixed stock solution containing biochar-modifier at a speed of 0.05mL / min until the pH is 7.5, and continue stirring for 12h to obtain Modified product liquid.

[0031] (4) Centrifuge the obtained modified product liquid, wash the precipitate obtained by the centrifugal separation, and then dry it at a temperature of 100° C. to obtain a three-component modified biochar of rice straw.

[0032] (5) Fluorine adsorption experiment was carried out on the obtained three-component modi...

Embodiment 3

[0035] (1) The rice straw is subjected to high-temperature carbonization treatment to obtain rice straw biochar.

[0036] (2) Dissolve 8.66g of lanthanum nitrate, 6.49g of ferric chloride and 8g of aluminum chloride in 100mL of deionized water to prepare a ternary modifier mixture, then add 1g of rice straw biochar for stirring to obtain biochar - A mixed stock solution of modifiers.

[0037] (3) Use a peristaltic pump to drop a sodium hydroxide solution with a concentration of 2 mol / L to the obtained mixed stock solution containing biochar-modifier at a speed of 0.5 mL / min until the pH is 7.5, and continue stirring for 12 hours to obtain Modified product liquid.

[0038] (4) Centrifuge the obtained modified product liquid, wash the precipitate obtained by the centrifugal separation, and then dry it at a temperature of 110° C. to obtain a three-component modified biochar of rice straw.

[0039] (5) Fluorine adsorption experiment was carried out on the obtained three-componen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of wastewater treatment, and discloses a ternary modified biochar for removing fluorine in water and a preparation method thereof. Biochar, and then strengthen and modify the biochar by slowly adding alkali, so that the surface of the biochar forms high-charge and high-polymerization aluminum forms, iron forms, and multi-metal layered double hydroxide colloids, and its acid-base stability The properties, surface hydroxyl groups, anion exchange capacity and isoelectric point are all improved, which not only improves the fluorine performance of the modified biochar, but also broadens its application range to alkaline, and its pH application range reaches 4-10. When fluorine is adsorbed, the fluorine removal rate can reach more than 90%.

Description

technical field [0001] The invention relates to the technical field of wastewater treatment, in particular to a ternary modified biochar used for removing fluorine in water and a preparation method thereof. Background technique [0002] Long-term drinking of water containing excessive fluoride will have adverse effects on human health. In today's field of fluoride removal technology, adsorption is considered to be a low-cost, simple and effective method for fluoride removal. When biochar is directly used as an adsorption material, the effect of removing fluorine is not ideal. In the prior art, metals are used to modify biochar to improve the adsorption capacity of fluorine. [0003] In the design of adsorption materials, according to the characteristics of fluoride ions, it is often necessary to consider increasing the porosity and reducing the particle size, preferably mesoporous, large specific surface area, more positive charges, itself or doping elements have fluorine-f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F101/14
CPCB01J20/20C02F1/281C02F1/283C02F2101/14B01J2220/4825
Inventor 叶长青周楠严玲周清稳杨玉环
Owner NANTONG UNIVERSITY
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com