Aramid fiber reinforced carbon fiber resin prepreg and preparation method thereof

A technology of aramid fiber and carbon fiber, which is applied in the field of aramid fiber reinforced carbon fiber resin prepreg and its preparation, can solve the problems of delamination damage, affecting the stability and safety of the overall structure, and low interlayer bonding strength, and achieve improvement High brittleness, low cost of improvement, and simple preparation method

Active Publication Date: 2020-04-03
浙江宝旌炭材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the CFRP material is prepared by a multi-layer prepreg through a hot-pressing process, there is a brittle pure epoxy resin connection layer in its structure, resulting in a low interlayer bonding strength and easy delamination of the CFRP structure. Defects such as damage seriously affect the stability and safety of the overall structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aramid fiber reinforced carbon fiber resin prepreg and preparation method thereof
  • Aramid fiber reinforced carbon fiber resin prepreg and preparation method thereof
  • Aramid fiber reinforced carbon fiber resin prepreg and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Preparation of aramid pulp reinforced unidirectional carbon fiber resin prepreg.

[0041] Raw materials: The carbon fiber used is 12K T700 industrial-grade unidirectional carbon fiber filament produced by Toray, Japan. The carbon fiber spreading width is 1m, and the fiber distribution surface density is 150g / m 2 The epoxy resin used is MT3 type epoxy resin produced by Jinggong (Shaoxing) Composite Materials Co., Ltd., the curing temperature is 130°C, and the designed resin distribution surface density is about 80g / m 2 ;The aramid fiber used is Kevlar aramid pulp produced by Dupont in the United States, the fiber length is ≤1mm, and the fiber diameter is ≤1μm; the mass ratio of the components of the prepreg is designed to be: aramid Fiber: 1.25 parts; Epoxy resin: 100 parts; Carbon fiber: 200 parts.

[0042] Preparation method: Take 10wt% epoxy resin component A, mix the same amount of acetone and stir until the resin is completely dissolved, then pour the solution into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an aramid fiber reinforced carbon fiber resin prepreg and a preparation method thereof. The main components of the product are carbon fibers, epoxy resin and aramid fibers; firstly acetone is used as an organic solvent, the aramid fibers are uniformly dispersed in the epoxy resin, then the epoxy resin added with the aramid fibers is combined with the carbon fibers by a prepreg machine, and the aramid fiber reinforced carbon fiber resin prepreg is prepared by a roll forming process. Compared with a common carbon fiber prepreg, the aramid fiber reinforced carbon fiber resin prepreg has the advantages that a plurality of mechanical properties such as strength and modulus of a carbon fiber reinforced plastic (CFRP) product formed after the product is laminated and cured are greatly improved; meanwhile, the structural stability and the impact resistance of the CFRP can be enhanced, and important significance is provided for overcoming the defects that interlayer resin of the CFRP material is high in brittleness and prone to layering, breaking and damaging.

Description

technical field [0001] The invention relates to the technical field of carbon fiber composites, in particular to an aramid fiber reinforced carbon fiber resin prepreg and a preparation method thereof. Background technique [0002] Carbon fiber reinforced resin matrix composites (CFRP) is a layered composite material prepared by a suitable molding process with carbon fiber or carbon fiber fabric as reinforcement, thermosetting or thermoplastic resin as matrix. It combines the high strength of carbon fiber and the low specific gravity of resin, thus showing excellent comprehensive performance, and is currently one of the most advanced composite materials in the world. [0003] Under the same quality conditions, the strength of CFRP is 10 times that of steel, but its density is 50% lower than steel and 30% lower than aluminum, so its lightweight effect is very obvious. In addition, compared with traditional metal materials, CFRP composite materials also have the advantages of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L77/10C08K7/06C08J5/24C08J5/04
CPCC08J5/24C08J5/047C08J5/046C08J5/042C08J2363/00C08J2477/10C08K7/06
Inventor 胡晓智谭波孙兴祥夏建明杨小兵
Owner 浙江宝旌炭材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap