Modified ABS material for automobiles

An ABS material and modification technology, applied in glass molding, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of chalking, loss of mechanical properties, discoloration, etc., achieve high hollowness, improve heat resistance, and improve resistance The effect of heat and strength

Pending Publication Date: 2020-05-12
苏州润佳高分子材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to the double bond contained in the chemical structure of the existing ABS material, it is easy to degrade under the action of sunlight and hot oxygen, resulting in pulverization, discoloration and loss of some mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Modified ABS material for automobiles, including the following raw materials in parts by weight: 100 parts of ABS, 20 parts of rubber, 20 parts of PC, 10 parts of hollow microspheres, 10 parts of ethylene oxide, 1 part of silane coupling agent, and 1 part of carbon black 1 part and antioxidant BHT 1 part.

[0023] The hollow microspheres are obtained through the following steps: wet ball milling of glass to obtain glass slurry, adding aluminum oxide and starch aqueous solution to the glass slurry under ultrasonic conditions, fully mixing, drying in an oven, and pulverizing , to obtain granules, and spheroidize the granules in a spheroidizing furnace to obtain hollow microspheres.

[0024] Wherein, glass wet ball milling is to put glass and ethanol in a ball mill for ball milling, the weight ratio of the glass, ethanol and steel balls is 1:2:4, and the speed range of the ball mill is 100rpm-300rpm.

[0025] Based on 10 parts by weight of glass, the parts by weight of th...

Embodiment 2

[0030] The modified ABS material for automobiles comprises the following raw materials in parts by weight: 120 parts of ABS, 30 parts of rubber, 30 parts of PC, 15 parts of hollow microspheres, 15 parts of ethylene oxide, 3 parts of silane coupling agent, and 2 parts of titanium dioxide And antioxidant 1076 2 parts.

[0031] The hollow microspheres are obtained through the following steps: wet ball milling of glass to obtain glass slurry, adding aluminum oxide and starch aqueous solution to the glass slurry under ultrasonic conditions, fully mixing, drying in an oven, and pulverizing , to obtain granules, and spheroidize the granules in a spheroidizing furnace to obtain hollow microspheres.

[0032] Wherein, glass wet ball milling is to place glass and ethanol in a ball mill for ball milling, the weight ratio of the glass, ethanol and steel balls is 1: 3: 5, and the speed range of the ball mill is 100rpm-300rpm.

[0033] Based on 10 parts by weight of glass, the parts by weig...

Embodiment 3

[0038] Modified ABS material for automobiles, including the following raw materials in parts by weight: 110 parts of ABS, 26 parts of rubber, 25 parts of PC, 12 parts of hollow microspheres, 12 parts of ethylene oxide, 2 parts of silane coupling agent, 1 part of carbon black 1 part and 164 parts of antioxidant.

[0039] The hollow microspheres are obtained through the following steps: wet ball milling of glass to obtain glass slurry, adding aluminum oxide and starch aqueous solution to the glass slurry under ultrasonic conditions, fully mixing, drying in an oven, and pulverizing , to obtain granules, and spheroidize the granules in a spheroidizing furnace to obtain hollow microspheres.

[0040] Wherein, the glass wet ball milling is to place glass and ethanol in a ball mill for ball milling, the weight ratio of the glass, ethanol and steel balls is 1:2-3:4-5, and the speed range of the ball mill is 100rpm-300rpm .

[0041] Based on 10 parts by weight of the glass, the parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified ABS material for automobiles. The modified ABS material is prepared from, by weight, 100 to 120 parts of ABS, 20 to 30 parts of rubber, 20 to 30 parts of PC, 10 to 15 parts of hollow microspheres, 10 to 15 parts of ethylene oxide, 1 to 3 parts of a silane coupling agent, 1 to 2 parts of a light stabilizer and 1 to 2 parts of an antioxidant. The modified ABS material is good in heat resistance and light resistance and suitable for automobiles, the heat resistance and the strength of the material are improved through the hollow microspheres and the rubber respectively, and the light stability of the material is improved through the light stabilizer and the antioxidant.

Description

technical field [0001] The invention relates to a modified ABS material for automobiles, belonging to the technical field of composite materials. Background technique [0002] Due to the superior characteristics of plastics, a large number of plastics are used in automobile design, which can not only realize the lightweight design of automobile structures, but also comprehensively reflect the requirements for automobile design performance, namely lightweight, safety, anti-corrosion, shape and comfort. In addition, it is also beneficial to reduce costs and save material resources. [0003] ABS (acrylonitrile-butadiene-styrene copolymer) has many varieties, good surface treatment effect and low price. Therefore, it has always been popular in body materials and plays an important role in the production of auto parts. Although PP (polypropylene) has come from behind in the production of auto parts, the aristocratic status of ABS in high-end auto parts cannot be shaken and comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L21/00C08L69/00C08K13/04C08K7/28C08K3/04C08K3/22C03B19/10C03C11/00
CPCC08L55/02C03B19/107C03C11/002C08L2205/03C08L2201/08C08K2003/2241
Inventor 翁永华汪理文邱晓雁李凯旋王绍庆
Owner 苏州润佳高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com