Anti-wear electrical ternary fluororubber nonmetal compensator and preparation method thereof

A non-metallic compensator and ternary fluororubber technology, which is applied to expansion compensation devices for pipelines, pipe components, mechanical equipment, etc., can solve the problems of reduced material strength, shortened service life, and poor adhesion, and achieve improved Effects of bonding strength, leakage prevention, improvement of toughness and wear resistance

Inactive Publication Date: 2017-04-19
当涂县金龙凤科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The adhesion between rubber and glass fiber is poor. Although the article "Research and Development of Ternary Fluorine Rubber Non-metallic Compensator" uses silane coupling agent to treat the surface of glass fiber, it can be used in high temperature, high pressure, highly corrosive gas, liquid and solid mixed media. Among them, the silane coupling agent is easy to decompose, which makes the glass fiber and rubber separate, reduces the strength of the material, causes leakage, shortens the service life, needs to be improved, and also needs to improve the wear resistance of the non-metallic compensator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] An anti-grinding ternary fluororubber non-metallic compensator, made of the following raw materials in parts by weight (kg): appropriate amount of ternary fluororubber, 100% alkali-free bulked yarn glass fiber fabric, vinylidene fluoride-hexafluoropropylene copolymer 50, acetone 200, benzyltriethylammonium chloride 2, 5wt% potassium hydroxide aqueous solution 80, 30wt% hydrogen peroxide aqueous solution 110, 36wt% hydrochloric acid aqueous solution, zinc oxide whisker 3, zirconium oxychloride 0.5, polyphenylene Sulfide micron powder 2.5, trifluoroethyl acrylate 0.3.

[0016] The preparation method of the anti-wear ternary fluororubber non-metallic compensator comprises the following steps:

[0017] (1) Mix and stir vinylidene fluoride-hexafluoropropylene copolymer and acetone until dissolved, add benzyltriethylammonium chloride and zinc oxide whiskers, stir well, then add 5wt% potassium hydroxide aqueous solution and stir well, then Add 30wt% hydrogen peroxide aqueous ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant electrical ternary fluororubber nonmetal compensator, which is prepared from the following raw materials in parts by weight: a proper amount of ternary fluorubber, 100-110 of alkali-free bulked yarn fiberglass fabric, 50-55 of vinylidene fluoride-hexafluoropropylene copolymer, 200-220 of acetone, 2-2.5 of TEBA, 80-85 of 5-5.5 wt% potassium hydroxide aqueous solution, 110-120 of 30-31 wt% hydrogen peroxide aqueous solution, a proper amount of 36-38 wt% hydrochloric acid aqueous solution, 3-3.5 of zinc oxide crystal whiskers, 0.5-0.7 of zirconium oxychloride, 2.5-3 of PPS micron powder, and 0.3-0.5 of trifluoroethyl acrylate. According to the technical scheme of the invention, the compatibility and the heat resistance of PPS micron powder and rubber are improved. Meanwhile, the PPS micron powder can improve the toughness and the wear resistance of the rubber. Therefore, the toughness and the wear resistance of the compensator are improved.

Description

technical field [0001] The invention relates to the technical field of non-metallic compensators, in particular to an anti-friction ternary fluorine rubber non-metallic compensator and a preparation method thereof. Background technique [0002] Non-metallic compensators are also called fabric compensators, non-metallic expansion joints or non-metallic soft connections. Corrosion, wear resistance, small mass, low cost, convenient installation and maintenance, etc. As a flexible connecting element, non-metallic compensators are widely used in fluid conveying pipelines and equipment in mining, metallurgy, electric power, cement, building materials, nuclear energy, petrochemical and other industries. [0003] In recent years, the material, structure, production process and application fields of non-metallic compensators in my country have been developing continuously. Now the applicable medium of the non-metallic compensator has developed from the initial flue gas in the low t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/12C08L81/02C08K13/06C08K9/04C08K7/00C08K7/14C08K7/08C08K3/18C08K5/101B29C35/02F16L51/00
CPCB29C35/02C08L27/12C08L2201/08F16L51/00C08L81/02C08K13/06C08K9/08C08K7/00C08K7/14C08K7/08C08K3/18C08K5/101
Inventor 张万宝
Owner 当涂县金龙凤科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products