Fireproof material taking gypsum as base material and construction method thereof

A fireproof material and gypsum technology, applied in the field of building materials, can solve the problems of labor and time consumption, affect production efficiency, and take a long time, and achieve the effects of reducing labor amount, improving production efficiency, and long fire resistance time.

Inactive Publication Date: 2020-05-29
河南中柏防火涂料科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Fireproof materials are materials that play an absolute role in modern fire prevention, and fireproof materials are divided into non-combustible materials and flame-retardant materials.
At present, in fireproof materials, the base material is sprayed multiple times to meet the fireproof requirements, and after each spraying, it is necessary to wait for 4-8 hours before the next spraying, which takes a long time and requires multiple sprayings. It takes a lot of labor and time for workers, which delays the construction period and affects production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof material taking gypsum as base material and construction method thereof
  • Fireproof material taking gypsum as base material and construction method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026]Preferably, the expandable graphite is modified expandable graphite, and the preparation method of the modified expandable graphite comprises the following steps: nano-scale montmorillonite, expandable graphite, γ-( Add methacryloyloxy)propyltrimethoxysilane into water, stir evenly, heat to 100°C and react for 2 hours, then filter, wash, and dry. The mass ratio of -(methacryloyloxy)propyltrimethoxysilane is 5:1:0.5.

[0027] The sodium α-olefin sulfonate used in the present invention is not particularly limited, and the sodium α-olefin sulfonate used in the present invention is commercially available.

[0028] Gypsum retarder, the gypsum retarder used in the present invention is not particularly limited, and is commercially available.

[0029] As a preferred embodiment, the gypsum retarder in the present invention is selected from one or more mixtures of sodium citrate, tartaric acid, potassium tartrate, acrylic acid, sodium acrylate and borax.

[0030] Filler, the fil...

Embodiment 1

[0043] A fireproof material based on gypsum, comprising component A and component B, component A includes the following materials in parts by weight:

[0044] 40 parts of gypsum;

[0045] Fiber 10 parts;

[0046] 50 parts of sodium carbonate;

[0047] 5 parts of graphite;

[0048] 1 part of sodium α-olefin sulfonate;

[0049] 10 parts of gypsum retarder;

[0050] 1 part filler;

[0051] 1 part of dicalcium silicate;

[0052] Component B is modified aluminum hydroxide, and component B accounts for 6% of the weight of component A.

[0053] Described sodium carbonate is commercially available, purchased from Henan Qifeng Chemical Co., Ltd.

[0054] The graphite described is expandable graphite, and the expandable graphite is purchased from Qingdao Risheng Graphite Co., Ltd., model number 9580300.

[0055] The sodium α-olefin sulfonate was purchased from Jinan Beyate Chemical Technology Co., Ltd.

[0056] The gypsum retarder is sodium citrate.

[0057] The filler is calc...

Embodiment 2

[0060] A fireproof material based on gypsum, comprising component A and component B, component A includes the following materials in parts by weight:

[0061] 30 parts of gypsum;

[0062] 1 part of polystyrene pellets;

[0063] 1 part fiber;

[0064] 100 parts of sodium carbonate;

[0065] 5 parts of graphite;

[0066] 5 parts of sodium α-olefin sulfonate;

[0067] 1 part of gypsum retarder;

[0068] 3 parts of filler;

[0069] 1.5 parts of dicalcium silicate;

[0070] Component B is modified aluminum hydroxide, and component B accounts for 5% of the weight of component A.

[0071] Described sodium carbonate is commercially available, purchased from Henan Qifeng Chemical Co., Ltd.

[0072] The graphite described is expandable graphite, and the expandable graphite is purchased from Qingdao Risheng Graphite Co., Ltd., model number 9580300.

[0073] The sodium α-olefin sulfonate was purchased from Jinan Beyate Chemical Technology Co., Ltd.

[0074] The gypsum retarder i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
barrier rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fireproof material taking gypsum as a base material and a construction method thereof, and belongs to the technical field of building materials. The fireproof material taking gypsum as a base material is a two-component system, wherein the component A is prepared from the following materials in parts by weight: 30-80 parts of gypsum, 0-30 parts of polystyrene particles,0-30 parts of vermiculite, 1-15 parts of fiber, 50-100 parts of sodium carbonate, 1-5 parts of graphite, 1-5 parts of alpha-olefin sodium sulfonate, 1-10 parts of gypsum retarder, 1-3 parts of fillerand 1-3 parts of dicalcium silicate; and the component B is modified aluminum hydroxide and accounts for 5-30% of the weight of the component A. By means of the fireproof material, the one-time spraying thickness of a base material can reach 50 mm, and the problem caused by the fact that the thickness requirement is met only when workers conduct spraying on the base material many times is avoided.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a fireproof material with gypsum as a base material and a construction method thereof. Background technique [0002] Fireproof materials are widely used in various technical fields such as industry and construction, and their quality directly affects human property safety and personal safety, so the selection of fireproof materials is very important. Fireproof materials are materials that play an absolute role in modern fire prevention. Fireproof materials are divided into non-combustible materials and flame-retardant materials. Non-combustible materials will not burn, and flame-retardant materials can burn, but they have certain flame resistance. At present, in fireproof materials, the base material is sprayed multiple times to meet the fireproof requirements, and after each spraying, it is necessary to wait for 4-8 hours before the next spraying, which takes a long t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B22/16C04B22/02C04B22/06C04B24/00C04B111/28C04B111/52C04B103/63
CPCC04B20/1066C04B28/14C04B2111/00155C04B2111/28C04B2111/52C04B16/08C04B20/0048C04B22/10C04B14/024C04B24/16C04B24/06C04B14/106C04B14/043C04B2103/63C04B14/042C04B14/20C04B24/04C04B14/40
Inventor 唐立
Owner 河南中柏防火涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com