Matte PET film for decorative sheet and preparation method thereof

A film and matte technology, applied in coatings, polyurea/polyurethane coatings, etc., can solve the problem of poor light transmittance of matte coatings, achieve good matte effect, adjustable surface performance, and high yield Effect

Active Publication Date: 2020-06-05
佛山市菲锐表面科技有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a matte PET film for decorative sheets and a preparation method thereof, which solves the problem of poor light transmittance of the existing matte coating, can ensure the transparency of the product, and has a good matte finish. light effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matte PET film for decorative sheet and preparation method thereof
  • Matte PET film for decorative sheet and preparation method thereof
  • Matte PET film for decorative sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 5 g of butyl acrylate / ethylene glycol dimethacrylate copolymer with a crosslinking degree of 2%, 10 g of polymethyl methacrylate (polymerization degree is 100), 30 g of aliphatic polyurethane acrylate resin, 3-hydroxy- 2,2-Dimethylpropyl-3-hydroxyl-2,2-dimethylpropyl ester diacrylate (purchased from Changxing Company, model EM2202) 45g and photoinitiator TPO (2,4,6-trimethyl Benzoyl-diphenylphosphine oxide) 1.2g, the remaining additives: leveling agent, dispersant 8.8g in total, with ethyl acetate 300g and butyl acetate 600g as solvent, high-speed dispersion and stirring to obtain a uniform solution.

[0053] Wherein, the mass ratio of butyl acrylate (BA) to ethylene glycol dimethacrylate (EGDMA) is 50:1.

[0054] The above solution was coated onto the surface of a transparent PET film by roller coating, and then cured by UV radiation after being dried in a far-infrared heating oven. The light source was a UV mercury lamp with a center wavelength of 365nm.

[0055] Tab...

Embodiment 2

[0059] 10 g of butyl acrylate / ethylene glycol dimethacrylate copolymer, polymethyl methacrylate (polymerization degree 100) 10 g, aliphatic polyurethane acrylate resin 30 g, 3-hydroxy-2 , 2-dimethylpropyl-3-hydroxy-2,2-dimethylpropyl diacrylate (purchased from Changxing Company, model EM2202) 40g, photoinitiator TPO 1.2g, other additives: leveling agent 1. Dispersant 8.8g in total, with ethyl acetate 300g and butyl acetate 600g as solvent, high-speed dispersion and stirring to obtain a uniform solution.

[0060] Wherein, the mass ratio of butyl acrylate (BA) to ethylene glycol dimethacrylate (EGDMA) is 50:1.

[0061] The above solution was coated onto the surface of the transparent PET film by roller coating, and then cured by UV radiation after being dried in a far-infrared heating oven. The light source was a UV mercury lamp with a center wavelength of 365nm.

[0062] Surface properties of table 2 matte PET film

[0063]

Embodiment 3

[0065] 10g of butyl acrylate / ethylene glycol dimethacrylate copolymer, polymethyl methacrylate (polymerization degree 1000) 10g, aliphatic polyurethane acrylate resin 30g, 3-hydroxy-2 , 2-dimethylpropyl-3-hydroxy-2,2-dimethylpropyl diacrylate (purchased from Changxing Company, model EM2202) 40g, photoinitiator TPO 1.2g, other additives: leveling agent 1. Dispersant 8.8g in total, with ethyl acetate 300g and butyl acetate 600g as solvent, high-speed dispersion and stirring to obtain a uniform solution.

[0066] Wherein, the mass ratio of butyl acrylate (BA) to ethylene glycol dimethacrylate (EGDMA) is 50:1.

[0067] The above solution was coated onto the surface of the transparent PET film by roller coating, and then cured by UV radiation after being dried in a far-infrared heating oven. The light source was a UV mercury lamp with a center wavelength of 365nm.

[0068] Surface properties of table 3 matte PET film

[0069]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
hazeaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a matte PET (Polyethylene Terephthalate) film for a decorative sheet and a preparation method thereof. The matte PET film comprises a transparent PET film and a UV (Ultraviolet) light-cured coating coated on the transparent PET film, wherein the UV light-cured coating is used as a matte coating, and the UV light-cured coating is composed of a polyacrylate polymer with a crosslinking degree of 1-30%, a thermoplastic acrylate polymer with a molecular weight of 10000-200000, an acrylate monomer, acrylic resin, a photo initiator and an auxiliary agent, wherein the acrylatemonomer and the acrylic resin are UV crosslinkable. The provided matte PET film can ensure the transparency of a product and has a good matte effect.

Description

technical field [0001] The invention relates to a matte film, in particular to a matte PET film used for decorative sheets and a preparation method thereof. Background technique [0002] Plastic sheet occupies a dominant position in the new surface decoration material market due to its simple production process, various surface decoration patterns and effects, simple use method, and high cost performance. The film materials used for decorative sheets mainly include PVC film and PET film. And composite films, etc., are widely used in indoor and furniture decoration, decoration industry, aircraft interior membrane, cabin membrane and other fields. [0003] Decorative sheets can be divided into two categories according to their luminosity: matte or matte, glossy or mirror. Among them, the production methods of decorative sheets with matte or matte effects mainly include: [0004] (1) Add matting powder in the sheet production process to obtain a plastic sheet with a matte effe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C09D175/14C09D133/12C09D133/08C09D7/63C08L67/02
CPCC09D175/14C09D7/63C09D133/08C08J2367/02C08J2475/14C08J2433/12C08J2433/08C08L33/12C08L33/08C08L75/14
Inventor 刘庆会陈军
Owner 佛山市菲锐表面科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com