Honeysuckle ES fiber and preparation process thereof

A technology of honeysuckle and honeysuckle extract, applied in the field of fiber manufacturing, can solve the problems of poor adhesion, easy high temperature carbonization, antibacterial, low hygroscopic performance, etc., and achieves improved dispersion uniformity, improved washing resistance, and small thermal shrinkage. Effect

Inactive Publication Date: 2020-06-12
BESTEE MATERIAL (TSINGTAO) CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are some technical defects in the preparation process of applying honeysuckle extract to ES fibers in the prior art, especially the high-temperature carbonization of honeysuckle extract in the high-temperature melting process of ES masterbatch, resulting in obvious carbonization spots on the spinning, Seriously affect the quality of finished products of ES fiber
In addition, the adhesion ability of honeysuckle extract on ES fibers is poor, and the functional degradation of ES fibers is serious after multiple washings
[0005] The existing technology has the following technical defects: (1) the existing honeysuckle ES fiber has low antibacterial and hygroscopic properties; (2) the existing honeysuckle ES fiber has obvious carbonization spots; (3) the existing honeysuckle ES fiber does not washable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1 A kind of honeysuckle ES fiber and preparation method thereof

[0041] A preparation method of honeysuckle ES fiber, comprising the following steps:

[0042] Step 1. Preparation of functional modified powder

[0043] (1) Raw material selection

[0044] The raw materials used include honeysuckle extract, ferric oxide, zinc stearate, sodium di-sec-octyl maleate sulfonate, and superfine activated carbon powder.

[0045] The honeysuckle extract: honeysuckle chlorogenic acid content 98%, particle size 80 mesh;

[0046] Described di-sec-octyl sodium maleate sulfonate: solid content 55%;

[0047] The superfine activated carbon powder: it is shell activated carbon powder, with a fineness of 10,000 mesh, a moisture content of 4-5%, and an iodine value of 700-800.

[0048] (2) Pretreatment

[0049] The honeysuckle extract was pretreated as follows: put the honeysuckle extract at 90°C for heat treatment for 1.5 hours; then lower the temperature to 22°C, pour it i...

Embodiment 2

[0065] Embodiment 2 A kind of honeysuckle ES fiber and preparation method thereof

[0066] A preparation method of honeysuckle ES fiber, comprising the following steps:

[0067] Step 1. Preparation of functional modified powder

[0068] (1) Raw material selection

[0069] The raw materials used include honeysuckle extract, ferric oxide, zinc stearate, sodium di-sec-octyl maleate sulfonate, and superfine activated carbon powder.

[0070] The honeysuckle extract: honeysuckle chlorogenic acid content 98%, particle size 80 mesh;

[0071] Described di-sec-octyl sodium maleate sulfonate: solid content 55%;

[0072] The superfine activated carbon powder: it is shell activated carbon powder, with a fineness of 10,000 mesh, a moisture content of 4-5%, and an iodine value of 700-800.

[0073] (2) Pretreatment

[0074] The honeysuckle extract was pretreated as follows: put the honeysuckle extract at 89°C for heat treatment for 1 hour; then lower the temperature to 20°C, pour it into...

Embodiment 3

[0090] Embodiment 3 A kind of honeysuckle ES fiber and preparation method thereof

[0091] A preparation method of honeysuckle ES fiber, comprising the following steps:

[0092] Step 1. Preparation of functional modified powder

[0093] (1) Raw material selection

[0094] The raw materials used include honeysuckle extract, ferric oxide, zinc stearate, sodium di-sec-octyl maleate sulfonate, and superfine activated carbon powder.

[0095] The honeysuckle extract: honeysuckle chlorogenic acid content 98%, particle size 80 mesh;

[0096] Described di-sec-octyl sodium maleate sulfonate: solid content 55%;

[0097] The superfine activated carbon powder: it is shell activated carbon powder, with a fineness of 10,000 mesh, a moisture content of 4-5%, and an iodine value of 700-800.

[0098] (2) Pretreatment

[0099] The honeysuckle extract was pretreated as follows: put the honeysuckle extract at 96°C for heat treatment for 1.5 hours; then lower the temperature to 25°C, pour it i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a honeysuckle ES fiber. For the ES fiber, the content of honeysuckle extract is 0.1-5 %. The preparation method comprises the following steps: preparation of functional modified powder, preparation of functional skin layer master batch and melt spinning. The preparation of the functional modified powder comprises the steps of raw material selection, pretreatment, preparation of a modification solution and preparation of the functional modified powder. The dispersion uniformity of honeysuckle active ingredients in the honeysuckle ES fiber preparedby the method is obviously improved, so that the honeysuckle ES fiber has obvious antibacterial, antiviral and moisture absorption effects, and the prepared honeysuckle ES fiber does not have macroscopic carbonized spots.

Description

technical field [0001] The invention belongs to the technical field of fiber manufacturing, and in particular relates to a honeysuckle ES fiber and a preparation process thereof. Background technique [0002] As a new type of heat-bonding composite fiber, ES fiber has been highly praised in the world. After the ES fiber is heat-treated, the fiber and the fiber are bonded to each other to form a non-woven fabric without binder. Different heat treatment methods can be used to obtain non-woven fabrics with different effects. [0003] Honeysuckle is the dry flower bud or the first flower of Lonicerae Lonicerae. Rod-shaped, thick at the top and thin at the bottom, slightly curved, 2-3cm long, 3mm in diameter at the upper part, 1.5mm in diameter at the lower part, yellowish-white or greenish-white surface, densely covered with pubescence. The main active ingredients are chlorogenic acid and luteolin. Chlorogenic acid of honeysuckle has a wide range of pharmacological effects. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/46D01F1/10
CPCD01F1/10D01F1/103D01F6/46
Inventor 黄效华刘彦明刘洁刘宇甄丽黄效谦
Owner BESTEE MATERIAL (TSINGTAO) CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com