Special protective material for polar rubber and preparation method thereof

A technology of protective material and polar rubber, which is applied in the field of special protective material for polar rubber and its preparation, can solve the problems of easy migration and frost spraying and high price, and achieve the effects of low price, alleviating adhesion and improving dispersibility.

Active Publication Date: 2021-09-21
常州市五洲化工有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Anti-aging agent NBC (nickel dibutyl dithiocarbamate) is a commonly used anti-ozone aging material for polar rubber, and can improve the heat resistance of polar rubber; however, it has the disadvantages of high price, easy migration and frosting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special protective material for polar rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A special protective material for polar rubber of the present invention consists of the following components (by weight): 40 parts of nickel dibutyldithiocarbamate, 30 parts of nickel terephthalate, and 30 parts of calcium terephthalate .

[0022] The method for preparing the special protective material for polar rubber comprises the following steps:

[0023] (1) Under constant stirring, mix alkali reduction waste water, dibutylamine, carbon disulfide and caustic soda in a certain proportion. After completely dissolving, add activated carbon with a mass percentage of 0.2% of the solution, and stir for 10 minutes to make it evenly dispersed in solution, and then filtered to obtain a decolorized, clear sodium salt solution;

[0024] (2) Under constant stirring, mix the sodium salt solution obtained in step (1) with the nickel chloride solution with a mass percentage of 35%, and continue to stir and react at a speed of 150 rpm for 60 minutes to obtain a mixed slurry A;

...

Embodiment 2

[0029] The difference between embodiment 2 and embodiment 1 is:

[0030] A special protective material for polar rubber of the present invention consists of the following components (by weight): 50 parts of nickel dibutyldithiocarbamate, 40 parts of nickel terephthalate, and 10 parts of calcium terephthalate .

[0031] The method for preparing the special protective material for polar rubber comprises the following steps:

[0032] (1) Under constant stirring, mix alkali reduction waste water, dibutylamine, carbon disulfide and caustic soda in a certain proportion. After completely dissolving, add activated carbon with a mass percentage of 0.2% of the solution, and stir for 20 minutes to make it evenly dispersed in solution, and then filtered to obtain a decolorized, clear sodium salt solution;

[0033] (2) Under continuous stirring, mix the sodium salt solution obtained in step (1) with the nickel chloride solution with a mass percentage of 60%, and continue to stir and reac...

Embodiment 3

[0037] The difference between embodiment 3 and embodiment 1 is:

[0038] A special protective material for polar rubber of the present invention consists of the following components (by weight): 45 parts of nickel dibutyldithiocarbamate, 35 parts of nickel terephthalate, and 20 parts of calcium terephthalate .

[0039] The method for preparing the special protective material for polar rubber comprises the following steps:

[0040] (1) Under constant stirring, mix the alkali reduction wastewater, dibutylamine, carbon disulfide and caustic soda in a certain proportion. After completely dissolving, add activated carbon with a mass percentage of 0.2% of the solution, and stir for 15 minutes to make it evenly dispersed in solution, and then filtered to obtain a decolorized, clear sodium salt solution;

[0041] (2) Under constant stirring, mix the sodium salt solution obtained in step (1) with the nickel chloride solution with a mass percentage of 45%, and continue to stir and rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special protection material for polar rubber and a preparation method thereof. The protective material is composed of the following components (by weight): 40-50 parts of nickel dibutyldithiocarbamate; 30-40 parts of nickel terephthalate; and 10-30 parts of calcium terephthalate. The preparation method of the protective material includes the following steps: (1) mixing and dissolving alkali weight reduction wastewater, dibutylamine, carbon disulfide and caustic soda in a certain proportion, and filtering through activated carbon to obtain a clear solution; (2) obtaining a clear solution from (1) After reacting the solution of nickel chloride solution with nickel chloride solution, slurry A is obtained; (3) after reacting the alkali-reduced water filtered by activated carbon with calcium chloride solution, slurry B is obtained; (4) the slurry of (2) After A and (3) slurry B are evenly mixed, the target product is obtained through separation, washing and drying. The protective material of the invention has moderate price, good dispersibility in the rubber material, excellent protective performance, and can also improve the defect that the rubber material is easy to stick.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a special protective material for polar rubber and a preparation method thereof. Background technique [0002] Among the commonly used rubber types, polar rubber mainly includes neoprene, nitrile rubber, hydrogenated nitrile rubber, carboxylated nitrile rubber, fluororubber, polyurethane rubber, polyether rubber, polysulfide rubber, acrylate rubber, chlorinated Polyvinyl chloride rubber, chlorosulfonated polyethylene rubber, etc. The properties of this type of rubber are: good oil resistance, good heat resistance, high strength and low insulation, so it is often used in oil-resistant and high-temperature-resistant occasions. [0003] During the processing, storage and use of rubber and its products, aging symptoms such as cracking, stickiness, hardening, softening, pulverization, discoloration, and mildew will appear due to the combined effects of internal and extern...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/39C08K5/098C08L23/34C08L9/02C08K13/02C08K3/22C08K3/06C08K3/04
CPCC08K5/098C08K5/39C08K2003/2296C08K2201/014C08L23/34C08L9/02C08K13/02C08K3/22C08K3/06C08K3/04
Inventor 张莉娜唐英俊方春平
Owner 常州市五洲化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com