A kind of preparation method of nitrile microcellular foaming non-slip gloves

A technology of microporous foaming and nitrile, which is applied to other household appliances, coatings, household appliances, etc., can solve the problems of corroding metal pipes and metal equipment, workshop air is easily polluted by dust, and the production environment is heavily polluted. Dust reduction, green production process, and excellent anti-skid performance

Active Publication Date: 2022-04-19
SHANDONG XINGYU GLOVES
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the advantages of nitrile scrub gloves and nitrile wrinkled gloves are outstanding, there are also many problems that cannot be ignored, including: (1) the preparation process of scrub gloves is to spray a large amount of inorganic salt ( Sodium chloride or sodium sulfate), and then washed with water for many times in Linxi or soaking, not only the air in the workshop is easily polluted by dust, it needs to consume a lot of water resources, and the spilled sodium chloride and sodium sulfate will corrode metal pipes and metal equipment. Equipment breakage is accelerated, which indirectly increases the production cost of the enterprise
(2) Butyronitrile wrinkle gloves need to be impregnated with organic acid and other wrinkle treatment agents, the production environment is polluted, and the sour smell on the surface of the gloves is relatively heavy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of nitrile microcellular foaming non-slip gloves

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The present invention proposes a kind of preparation method of nitrile microcellular foaming non-slip gloves, comprises the steps:

[0051] S1: Dip-coat the glove blank with nitrile pre-vulcanized glue and homogenize it:

[0052] Step 1: Take 90-120 parts by mass of nitrile latex, 1-2 parts by mass of surfactant, 1-5 parts by mass of active agent, 2-8 parts by mass of vulcanizing agent, 1-4 parts by mass of vulcanization accelerator, and 1 part by mass of antioxidant -2 parts by mass are mixed in a proportioning manner to prepare a prevulcanized mortar mother liquor.

[0053] Step 2: Take 90-120 parts by mass of the pre-vulcanized mortar mother liquid prepared in step 1, and add 1-4 parts by mass of thickener to adjust the final viscosity to 1200-3500mpa.s. The thickener is one or a combination of CMC, sodium polyacrylate, casein, PVA, hydroxymethyl ethyl cellulose, and hydroxyethyl propyl cellulose.

[0054] Among them, when the glove embryo is a chemical fiber knitt...

Embodiment 1

[0077] The present embodiment provides a kind of preparation method of nitrile microcellular foamed non-slip gloves, and its method step is as follows:

[0078] (1) Get 100 parts by mass of nitrile latex, 1.2 parts by mass of sodium lauryl sulfate (surfactant), 1.5 parts by mass of vulcanization accelerator BZ, 1.5 parts by mass of zinc oxide (activator), 2 parts by mass of sulfur, antioxidant 264 1.2 parts by mass were mixed uniformly to obtain a prevulcanized mortar mother liquor.

[0079] (2) Take 100 parts by mass of the pre-vulcanized mortar mother liquor, add 1.5 parts by mass of 2% CMC, adjust the viscosity to 2400mpa.s, and obtain a pre-vulcanized nitrile mortar.

[0080] (3) Get 100 mass parts of prevulcanized mortar mother liquor, add 1.5 mass parts of 1% CMC, 1 mass part of potassium oleate and 1 part of expandable microsphere blowing agent (market purchase, particle size 10-20 micron ), foaming at room temperature, the foaming ratio is about 1.1 times; after the f...

Embodiment 2

[0086] The present embodiment provides a kind of preparation method of nitrile microcellular foamed non-slip gloves, and its method step is as follows:

[0087] (1) Get 100 parts by mass of nitrile latex, 2 parts by mass of Pingpingjia (surfactant), 2 parts by mass of accelerator D, 2 parts by mass of zinc oxide (active agent), 6 parts by mass of magnesium oxide, 1.5 parts by mass of antioxidant RD Mix evenly to obtain prevulcanized mortar mother liquor.

[0088] (2) Take 110 parts by mass of the pre-vulcanized mortar mother liquor, add 2 parts by mass of 2% CMC, adjust the viscosity to 2500mpa.s, and obtain a pre-vulcanized nitrile mortar.

[0089] (3) Get 100 mass parts of prevulcanized mortar mother liquor, add 1% CMC of 1 mass part, 0.5 mass parts of potassium laurate and 1.5 parts of expandable microsphere blowing agent (market purchase, particle diameter 10-20 micron ), under normal temperature mechanical stirring and beating foaming, the foaming ratio is about 1.05 tim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of nitrile microporous foamed non-slip gloves. The gloves are dipped in nitrile pre-vulcanized glue once, and then dipped in nitrile pre-vulcanized microporous foamed glue twice. The double-pass nitrile pre-vulcanized microcellular foaming mortar is foaming mortar obtained by foaming with a physical or chemical foaming agent, and the foaming mortar is also mixed with unfoamed expandable microsphere foaming agent . After the second dipping, these expandable microsphere blowing agents are transferred to the surface of the glove, and in the subsequent vulcanization and drying process, the expandable microsphere blowing agent mixed with unfoamed expandable microspheres is re-expanded due to high temperature. Foaming and forming a number of foaming protrusions, so that the nitrile rubber gloves have a large specific surface area and an anti-slip effect close to / exceeding the nitrile scrub gloves, and the gloves are soft and comfortable to wear, and have anti-slip and anti-chemical characteristics. Compared with the frosted gloves, the present invention has the advantages of simpler preparation process, more environmental protection, water saving and the like.

Description

technical field [0001] The invention relates to the technical field of coated gloves, in particular to a preparation method of nitrile microcellular foamed non-slip gloves. Background technique [0002] The preparation method of rubber gloves is generally to form a layer of rubber layer after the textile glove embryo is impregnated with natural latex, synthetic latex, etc. on the surface, so that the gloves are waterproof. [0003] Nitrile latex is a kind of latex with relatively high polarity. The nitrile rubber formed after curing has excellent water resistance, chemical corrosion resistance and oil resistance, and is more and more widely used in the preparation of gloves and the like. However, the texture of nitrile rubber is relatively hard, the surface is relatively flat and smooth, and it becomes smoother when it meets water or oil. When used as protective gloves, its anti-skid effect is poor, and the grip is not good when worn, which leads to the application function ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C41/14B29C41/22B29C44/02B29C44/08B29C35/02C08J9/32C08J9/30C08J9/10C08J5/02C08L9/04C08K13/02C08K3/22C08K3/06C08K5/40C08K3/26B29L31/48
CPCB29C41/14B29C41/22B29C44/022B29C44/08B29C35/0288C08J9/32C08J9/30C08J9/103C08J9/105C08J5/02C08J9/0061C08J9/0066C08J9/0095C08J9/0033C08J2309/04C08J2203/04C08J2203/22B29L2031/4864
Inventor 周海涛孙永峰
Owner SHANDONG XINGYU GLOVES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products