A kind of method of reclaiming rhodium chloride from rhodium slag

A technology for rhodium chloride and rhodium slag, which is applied in the field of recycling rhodium chloride, can solve problems such as high equipment requirements, environmental pollution, and complicated processes, and achieve the effect of improving separation effect, improving conversion rate, and simple operation method

Active Publication Date: 2021-07-02
LUXI CATALYST
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although these methods can reclaim most of the rhodium in the spent catalyst, the inventors have found that there are many problems, some of which are relatively complicated and highly toxic, some have higher requirements for equipment, and some will produce obvious environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] (1) Get 500g rhodium ash and 300g sodium formate to mix, put into the muffle furnace, carry out pre-reduction under the condition of 250 ℃;

[0053] (2) Add hydrochloric acid to the pre-reduced rhodium ash at 80° C., mechanically stir for 2 hours, and repeat 4 times to reduce the iron content in the rhodium ash as much as possible.

[0054] (3) The rhodium ash after iron removal is mixed with 10 mass times of sodium bisulfate and 1 times of sodium chloride, ground and mixed into powder with a mortar and placed in a porcelain boat.

[0055] (4) Put the sample into a muffle furnace, raise the temperature to 350°C, keep it warm for 2 hours, then raise the temperature to 600°C, react for 3h, cool down and take it out to room temperature.

[0056] (5) adding desalted water to extract the molten material to obtain a khaki solution, filtering the extracted material, and collecting the filtrate.

[0057] (6) Add 10% sodium hydroxide solution to the filtrate, adjust the pH to 8...

Embodiment 2

[0064] Raw material, amount of raw material, device and steps are the same as in Example 1, except that the pre-reduction after the mixing of rhodium ash and formate is not carried out. Analysis and detection show that the purity of rhodium chloride is 99.34%, and the recovery rate of rhodium is 92.68%.

Embodiment 3

[0066] The raw materials, raw material amounts, devices and steps are the same as in Example 1, except that an appropriate amount of acid is not added to the pre-reduced rhodium ash, and the base metal in the rhodium ash is not eluted in advance. Analysis and detection showed that the purity of rhodium chloride was 99.52%, and the recovery rate of rhodium was 92.32%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for recovering rhodium chloride from rhodium slag, which comprises rhodium ash pretreatment, pickling rhodium ash, acid salt melting of alkali metal, cationic resin adsorption, evaporative crystallization and formic acid reduction. Rhodium ash is first pretreated with formate, and then pickled to remove most of the base metals. After drying, it is mixed with acid salts of alkali metals and additives to form a powder and melted in a muffle furnace. Deionized water is used to extract the melt, and the treated extract is passed through cationic resin to completely remove base metals, and then concentrated and dried to obtain high-purity rhodium trichloride. After the resin is saturated with iron, the resin is eluted with hydrochloric acid. Adding formic acid to the eluent to reduce rhodium realizes the separation of rhodium and iron in the resin eluent. The purpose of the present invention is to reclaim rhodium chloride, a kind of simple recovery process is provided, the method for reclaiming rhodium chloride from rhodium slag that is pollution-free to the environment and the purity of rhodium chloride is high.

Description

technical field [0001] The invention belongs to the recovery of precious metals, in particular to a method for recovering rhodium chloride from rhodium slag. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] Rhodium compounds are widely used in basic chemical industry and pharmaceutical chemical industry as the main raw material of electroplating solution, acetic acid synthesis catalyst and olefin oxo synthesis catalyst. In order to facilitate the use, measurement and transportation of rhodium compounds, rhodium is usually processed into rhodium chloride products for future use. Therefore, it is of great significance to recover rhodium in the spent rhodium catalyst in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G55/00C22B11/00C22B7/00C22B1/00
CPCC01G55/001C01G55/005C01P2006/80C22B1/005C22B11/042Y02P10/20
Inventor 张照飞田斌李伟雪胡大春孟凡民刘晓臻刘丽丽曹全福
Owner LUXI CATALYST