A high-strength corrosion-resistant aluminum alloy door and window and its preparation method

A technology for corrosion-resistant aluminum alloy and aluminum alloy doors and windows, applied in the production field of aluminum alloy doors and windows, can solve the problems of easy falling off and wear of the corrosion-resistant layer, affecting the strength of the aluminum alloy, affecting the internal stress, etc., to achieve good plasticity, improve strength, and improve mechanical properties. the effect of strength

Active Publication Date: 2021-06-22
新沂天源节能材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the general corrosion-resistant methods for aluminum alloys are anodic oxidation, electrophoretic coating, powder spraying, etc., which can play a certain corrosion-resistant effect on the surface of aluminum alloys, but anodic oxidation will affect its internal stress and affect the aluminum alloy. Strength; while the surface corrosion-resistant layer formed by painting and powder spraying is easy to fall off and wear, and cannot be protected for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-strength corrosion-resistant aluminum alloy door and window, the high-strength corrosion-resistant aluminum alloy door and window is made of a high-strength corrosion-resistant aluminum alloy material, and the high-strength corrosion-resistant aluminum alloy material includes the following components in proportion by weight: zinc 1 part, manganese 0.5 part, iron 1 part, magnesium 1 part, copper 0.5 part, cobalt 0.1 part, nickel 0.5 part, zirconium 0.5 part, strontium 0.1 part and modified rare earth element 0.5 part, the balance is aluminum and unavoidable Impurities, the content of which is no more than 1 part. The modified rare earth element includes the following components by weight: 30 parts of yttrium, 20 parts of gadolinium and 20 parts of lutetium. The modified rare earth element is modified by nano-silicon carbide particles with a particle diameter of 50-150 nm.

[0023] A method for preparing high-strength corrosion-resistant aluminum alloy doors and w...

Embodiment 2

[0028] A high-strength corrosion-resistant aluminum alloy door and window, the high-strength corrosion-resistant aluminum alloy door and window is made of a high-strength corrosion-resistant aluminum alloy material, and the high-strength corrosion-resistant aluminum alloy material includes the following components in proportion by weight: zinc 4 parts, 1 part of manganese, 5 parts of iron, 5 parts of magnesium, 1 part of copper, 0.5 parts of cobalt, 1 part of nickel, 1 part of zirconium, 0.5 parts of strontium and 1.5 parts of modified rare earth elements, the balance is aluminum and unavoidable Impurities, the content of which is no more than 1 part. The modified rare earth elements include the following components by weight: 45 parts of yttrium, 35 parts of gadolinium and 35 parts of lutetium. The modified rare earth element is modified by nano-silicon carbide particles with a particle diameter of 50-150 nm.

[0029] A method for preparing high-strength corrosion-resistant ...

Embodiment 3

[0034] A high-strength corrosion-resistant aluminum alloy door and window, the high-strength corrosion-resistant aluminum alloy door and window is made of a high-strength corrosion-resistant aluminum alloy material, and the high-strength corrosion-resistant aluminum alloy material includes the following components in proportion by weight: zinc 2.5 parts, 0.75 parts of manganese, 3 parts of iron, 3 parts of magnesium, 0.7 parts of copper, 0.3 parts of cobalt, 0.7 parts of nickel, 0.7 parts of zirconium, 0.3 parts of strontium and 1 part of modified rare earth elements, and the balance is aluminum and unavoidable Impurities, the content of which is no more than 1 part. The modified rare earth elements include the following components by weight: 37 parts of yttrium, 27 parts of gadolinium and 27 parts of lutetium. The modified rare earth element is modified by nano-silicon carbide particles with a particle diameter of 50-150 nm.

[0035] A method for preparing high-strength corr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength corrosion-resistant aluminum alloy door and window and a preparation method thereof, belonging to the technical field of aluminum alloy door and window production. The corrosion-resistant aluminum alloy material includes the following components by weight: 1-4 parts of zinc, 0.5-1 parts of manganese, 1-5 parts of iron, 1-5 parts of magnesium, 0.5-1 parts of copper, and 0.1-0.5 parts of cobalt , 0.5-1 part of nickel, 0.5-1 part of zirconium, 0.1-0.5 part of strontium and 0.5-1.5 part of modified rare earth element, the balance is aluminum and inevitable impurities, and the content of said impurities does not exceed 1 part. The high-strength corrosion-resistant aluminum alloy door and window is made of a mixture of various metals, and has high metal strength and good corrosion resistance; the preparation method of the high-strength corrosion-resistant aluminum alloy door and window is simple and has a wide range of sources. , suitable for large-scale industrial promotion.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy door and window production, and in particular relates to a high-strength corrosion-resistant aluminum alloy door and window and a preparation method thereof. Background technique [0002] Because aluminum alloy has the characteristics of low density, good mechanical properties, good processing performance, non-toxic, easy to recycle, good electrical conductivity, heat transfer and corrosion resistance, it is widely used in marine industry, chemical industry, aerospace, metal packaging, transportation, etc. It is widely used in transportation and other fields. With the rapid development of aluminum alloys, aluminum alloys have been widely used in the manufacture of doors and windows. Because many doors and windows are exposed to the air and need to carry a certain amount of pressure, aluminum alloys are required to have good strength and certain corrosion resistance. [0003] At present, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C21/10C22C21/06C22C1/02C22F1/04C22F1/053C22F1/047
CPCC22C1/026C22C21/00C22C21/06C22C21/10C22F1/04C22F1/047C22F1/053
Inventor 杨智勇
Owner 新沂天源节能材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products