Stripping agent special for room-temperature vulcanized silicone rubber for insulator and stripping method

A room temperature vulcanization and insulator technology, applied in recycling technology, plastic recycling, etc., can solve problems such as waste of insulating devices, degradation of hydrophobicity and hydrophobic migration performance, and decreased ability to prevent pollution flashover, and achieve the effect of reducing pollution and

Inactive Publication Date: 2020-07-24
武汉疏能新材料有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these insulators (ceramic or glass insulators) coated with room temperature vulcanized silicone rubber (RTV) will reduce or lose the hydrophobicity and hydrophobic migration properties of the room temperature vulcanized silicone rubber (RTV) coating due to climate and environmental reasons during use. Decrease the anti-pollution flashover ability of insulators, seriously affecting the safety of power transmission
At present, it is generally used to directly replace room temperature vulcanized silicone rubber (RTV) insulators with reduced anti-pollution flashover capabilities, resulting in environmental pollution and waste of insulating devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1) Mix 50 parts of butanone, 20 parts of ethanol and 5 parts of ethyl acetate, and disperse at 300-500r / min for 5min to obtain a mixed solution;

[0020] 2) Slowly add 15 parts of concentrated hydrochloric acid (HCl) to the mixed solution obtained in step 1), and disperse at 300-500r / min for 5min;

[0021] 3) to step 2) slowly add 10 parts of vitriol oil (H 2 SO 4 ), and disperse at 300-500r / min for 5min to obtain a special release agent for room temperature vulcanized silicone rubber (RTV) for insulators;

[0022] 4) Soak the insulator coated with room temperature vulcanized silicone rubber (RTV) in step 3) in the special release agent for room temperature vulcanized silicone rubber (RTV) for insulators for 24 hours;

[0023] 5) Take out the insulator soaked in step 4), wear acid and alkali resistant rubber gloves, and peel off the room temperature vulcanized silicone rubber (RTV) on the surface of the insulator to restore the surface of the insulator to be smooth an...

Embodiment 2

[0025] 1) Mix 60 parts of methyl ethyl ketone, 10 parts of methanol and 3 parts of ethyl acetate, and disperse at 300-500r / min for 5min to obtain a mixed solution;

[0026] 2) Slowly add 20 parts of concentrated hydrochloric acid (HCl) to the mixed solution obtained in step 1), and disperse at 300-500r / min for 5min;

[0027] 3) to step 2) slowly add 7 parts of concentrated sulfuric acid (H 2 SO 4 ), and disperse at 300-500r / min for 5min to obtain a special release agent for room temperature vulcanized silicone rubber (RTV) for insulators;

[0028] 4) Soak the insulator coated with room temperature vulcanized silicone rubber (RTV) in step 3) in the special release agent for room temperature vulcanized silicone rubber (RTV) for insulators for 24 hours;

[0029] 5) Take out the insulator soaked in step 4), wear acid and alkali resistant rubber gloves, and peel off the room temperature vulcanized silicone rubber (RTV) on the surface of the insulator to restore the surface of the...

Embodiment 3

[0031] 1) Mix 70 parts of acetone, 10 parts of ethanol and 2 parts of butyl acetate, and disperse at 300-500r / min for 5min to obtain a mixed solution;

[0032] 2) Slowly add 13 parts of concentrated hydrochloric acid (HCl) to the mixed solution obtained in step 1), and disperse at 300-500r / min for 5min;

[0033] 3) Slowly add 5 parts of concentrated nitric acid (HNO 3 ), and disperse at 300-500r / min for 5min to obtain a special release agent for room temperature vulcanized silicone rubber (RTV) for insulators;

[0034] 4) Soak the insulator coated with room temperature vulcanized silicone rubber (RTV) in step 3) in the special release agent for room temperature vulcanized silicone rubber (RTV) for insulators for 24 hours;

[0035] 5) Take out the insulator soaked in step 4), wear acid and alkali resistant rubber gloves, and peel off the room temperature vulcanized silicone rubber (RTV) on the surface of the insulator to restore the surface of the insulator to be smooth and sm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stripping agent special for room-temperature vulcanized silicone rubber for an insulator and a stripping method. The stripping agent is prepared from, by mass, 50-70 parts ofsolvent butanone, 10-30 parts of cosolvent methyl alcohol, 10-20 parts of stripping auxiliary concentrated hydrochloric acid, 5-10 parts of functional auxiliary concentrated sulfuric acid and 2-5 parts of builder ethyl acetate. The stripping agent can effectively strip an RTV coating on the surface of the insulator (glass or ceramic insulator) coated with room temperature vulcanized silicone rubber (RTV) so that the surface of the insulator is recovered to be smooth and flat. Therefore, the effects of recycling and reducing pollution are achieved.

Description

technical field [0001] The invention belongs to the field of electric equipment reuse, and in particular relates to a special stripping agent for room temperature vulcanized silicone rubber for insulators and a stripping method. Background technique [0002] Insulators are the most common insulating devices in power transmission. According to their different insulating materials, they can be divided into ceramic insulators, glass insulators and composite insulators, among which ceramic insulators and glass insulators are more widely used. In some environmentally polluted areas, insulators (ceramic or glass insulators) for power transmission are generally coated with room temperature vulcanized silicone rubber (RTV) coatings to improve the hydrophobicity and hydrophobic migration performance of the insulator surface, thereby improving the flashover of the insulator voltage, reducing the risk of pollution flashover of insulators. However, these insulators (ceramic or glass in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J11/08C08L83/04
CPCC08J11/08C08J2383/04Y02W30/62
Inventor 陈智朱仕惠兰洋王芹
Owner 武汉疏能新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products