Antibacterial nylon filament and production method thereof

A production method and filament technology, applied in filament/thread forming, conjugated synthetic polymer artificial filament, cellulose/protein conjugated artificial filament, etc., can solve the problems of single function and poor antibacterial performance, etc. Achieve the effects of improving antibacterial performance, strong antibacterial ability, and improving comfort performance

Inactive Publication Date: 2020-07-28
周华
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional nylon filament has single fu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial nylon filament and production method thereof
  • Antibacterial nylon filament and production method thereof
  • Antibacterial nylon filament and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] As another embodiment of this case, wherein, the preparation method of the cortex masterbatch includes:

[0051] a, take bamboo charcoal, lithium carbonate, polyhexamethylene guanidine, juniper oil, zinc oxide loaded zirconium phosphate, aminoethylaminopropylmethyldiethoxysilane, mix and stir to obtain antibacterial agent;

[0052] b. Mix the polyamide resin and the antibacterial agent, and granulate through a twin-screw extruder to make a skin-layer masterbatch. The granulation temperature is 220°C to 240°C.

[0053] As another embodiment of the present case, wherein, the preparation method of the core layer masterbatch includes:

[0054] Weigh and mix polyamide resin, cellulose acetate, polylactic acid, and 2-mercaptobenzothiazole, and granulate through a twin-screw extruder to make a core layer masterbatch. The granulation temperature is 240°C to 260°C.

[0055] As another embodiment of this case, wherein, the temperature of the hot plate during the drawing is 50-70...

Embodiment 1

[0058] A kind of antibacterial nylon filament, long filament comprises cortex fiber and core layer fiber, and described cortex fiber accounts for 15% of total amount, and core layer fiber accounts for 85% of total amount; Cortex fiber comprises the following parts by weight Material:

[0059] 40 parts by weight of polyamide resin;

[0060] 10 parts by weight of antibacterial agent.

[0061] Antimicrobials include:

[0062]

[0063] The preparation method of cortex masterbatch comprises:

[0064] a, take bamboo charcoal, lithium carbonate, polyhexamethylene guanidine, juniper oil, zinc oxide loaded zirconium phosphate, aminoethylaminopropylmethyldiethoxysilane, mix and stir to obtain antibacterial agent;

[0065] b. Mix the polyamide resin and the antibacterial agent, and granulate through a twin-screw extruder to make a skin layer masterbatch. The granulation temperature is 220°C.

[0066] In parts by weight, the core fiber includes:

[0067]

[0068] The preparation ...

Embodiment 2

[0075] A kind of antibacterial nylon filament, long filament comprises cortex fiber and core layer fiber, and described cortex fiber accounts for 20% of total proportion, and core layer fiber accounts for total proportion of 80%; Cortex fiber comprises the following parts by weight Material:

[0076] 50 parts by weight of polyamide resin;

[0077] 12 parts by weight of antibacterial agent.

[0078] In parts by weight, the antibacterial agent includes:

[0079]

[0080] The preparation method of cortex masterbatch comprises:

[0081] a, take bamboo charcoal, lithium carbonate, polyhexamethylene guanidine, juniper oil, zinc oxide loaded zirconium phosphate, aminoethylaminopropylmethyldiethoxysilane, mix and stir to obtain antibacterial agent;

[0082] b. Mix the polyamide resin and the antibacterial agent, and granulate through a twin-screw extruder to make a skin layer masterbatch. The granulation temperature is 230°C.

[0083] In parts by weight, the core fiber includes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antibacterial nylon filament. The filament comprises a skin layer fiber and a core layer fiber, wherein the skin layer fiber comprises, by weight, 40-60 parts of polyamide resin and 10-20 parts of antibacterial agent. According to a production method of the antibacterial nylon filament, the composite filament comprises the skin layer fiber and the core layer fiber, and is excellent in mechanical property and strong in antibacterial ability.

Description

technical field [0001] The invention relates to a filament material, in particular to an antibacterial nylon filament and a production method thereof. Background technique [0002] The scientific name of nylon is polyamide fiber, which is the general name of polyamide fibers produced in China. Internationally known as nylon. High strength, wear resistance, good resilience, can be purely spun or blended for various clothing and knitwear. The main varieties are nylon 6 and nylon 66, and their physical properties are similar. Nylon has better hygroscopicity and dyeability than polyester, and is resistant to alkali but not acid. Its fiber strength will decrease when exposed to sunlight for a long time. Nylon has heat setting properties and can maintain the bending deformation formed when heated. Nylon filaments can be made into elastic yarns, and short yarns can be blended with cotton and acrylic to improve its strength and elasticity. In addition to the application in cloth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/12D01F8/02D01F8/14D01F1/10D01D5/34
CPCD01D5/34D01F1/103D01F8/02D01F8/12D01F8/14
Inventor 周华
Owner 周华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap