Purple green dot kiln-transmutation porcelain and preparation process thereof

A preparation process and green dot technology, which is applied in the field of Zicai green dot kiln-transformed porcelain and its preparation process, can solve problems such as poor appreciation, failure to meet market requirements, poor appearance and visual effects, etc., and reduce production costs and firing temperatures. Effects of low and significant environmental value

Active Publication Date: 2020-08-18
福建省德化县瓷言坊陶瓷工艺有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the preparation process of traditional kiln-transformed glazes, there are high requirements for the use of raw materials and preparation techniques. The kiln-transformed glazed ceramic products produced by a little carelessness have poor visual effects and poor appreciation, and cannot meet the requirements of the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation technology of purple-colored green-dot kiln-transformed porcelain is characterized in that the specific steps are as follows:

[0031] Step 1, preparing a ceramic green body;

[0032] Step 2: Proportionally weigh the raw material components of the purple-colored green-dot kiln-changing glaze, perform wet ball milling on the raw materials of the purple-colored green-dot kiln-changing glaze, pass through a 500-600 mesh sieve after ball milling, and obtain the colorful green-dot kiln-changing glaze. Feldspar, quartz, fluorite, rutile, spodumene, dolomite, and ashes are pulverized into powder materials, and the powder materials together with a high expansion coefficient co-solvent are put into a wet ball mill and mixed for 3-4 hours, and titanium, lead Dan, zinc, iron oxide, calcium, and dispersant are mixed and stirred, then added to the wet ball mill, and continue to mix for 1-2 hours. The mass ratio of ball: water: 1-2:1-1.5:2 for the glaze of the wet bal...

specific Embodiment 1

[0041] A purple-colored green-dot kiln-changed porcelain, comprising a purple-colored green-dot kiln-changed glaze arranged on a ceramic body, the raw material weight components of the purple-colored green-dot kiln-changed glaze are as follows:

[0042] 26 parts of feldspar, 11 parts of quartz, 8 parts of fluorite, 7 parts of rutile, 6 parts of spodumene, 5 parts of dolomite, 2 parts of ashes, 6 parts of high expansion co-solvent, 8 parts of titanium, 7 parts of red lead, 4 parts of zinc, 3 parts of iron oxide, 5 parts of calcium, and 1 part of dispersant.

[0043] The preparation technology of purple-colored green-dot kiln-transformed porcelain is characterized in that the specific steps are as follows:

[0044] Step 1, preparing a ceramic green body;

[0045] Step 2: Carry out proportioning and weighing according to the raw material components of the purple-colored green-dot kiln-changing glaze, carry out wet ball milling on the raw materials of the purple-colored green-dot...

specific Embodiment 2

[0055] A purple-colored green-dot kiln-changed porcelain, comprising a purple-colored green-dot kiln-changed glaze arranged on a ceramic body, the raw materials of the purple-colored green-dot kiln-changed glaze are as follows: 28 parts of feldspar, 14 parts of quartz, fluorite 9 parts, 6 parts of rutile, 7 parts of spodumene, 4 parts of dolomite, 1 part of bone ash, 6 parts of co-solvent with high expansion coefficient, 6 parts of titanium, 8 parts of red lead, 3 parts of zinc, 4 parts of iron oxide, 3 parts of calcium 1 part, dispersant 1 part.

[0056] The preparation technology of purple-colored green-dot kiln-transformed porcelain is characterized in that the specific steps are as follows:

[0057] Step 1, preparing a ceramic green body;

[0058] Step 2: Proportionally weigh the raw material components of the purple-colored green-dot kiln-changing glaze, carry out wet ball milling of the purple-colored green-dot kiln-changing glaze raw materials, pass through a 600-mesh ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of ceramic products, and particularly relates to purple green dot kiln-transmutation porcelain and a preparation process thereof. An additive containing calcium, titanium and low-valence iron is added into alkaline glaze; the principle that titanium has a purple red color in alkaline glaze is taken as the basis, green crystallization spots are formed by calcium and low-valence iron; the substrate has a purple red color, the purple red color has a transition effect and a changing kiln-transmutation effect, and green spots with a diameter of 1-3 mm are uniformly distributed on the purple red color. The characteristic of a traditional multi-color kiln-transmutation glaze material is broken through, the comparison between purple and the green is significant,and a unique artistic effect is achieved. The used raw materials are environmentally friendly. One-time firing and forming can be achieved after twice temperature changing and changing of a firing atmosphere. The production cost of raw materials is effectively reduced, meanwhile, the firing temperature is low, the environment-friendly value is high, and economic benefits and market competitivenessare improved.

Description

technical field [0001] The invention belongs to the field of ceramic products, and in particular relates to a purple-colored green-dot kiln-transformed porcelain and a preparation process thereof. Background technique [0002] Ceramic products are widely used in our country, and the technology for preparing ceramics is also very mature. Kiln change mainly refers to the uncertain and natural change of glaze color on the surface of porcelain due to the temperature change in the kiln during the firing process, and the kiln change glaze produced has a unique visual effect. During the preparation process of the traditional kiln-transformed glaze, the requirements for the use of raw materials and the preparation process are relatively high. The kiln-transformed glaze ceramic products produced by a little carelessness have poor visual effects and poor appreciation, and cannot meet the requirements of the market. [0003] For example, the application number is CN201811469328.2, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86C04B35/622C04B35/64
CPCC03C8/00C04B41/86C04B41/5022C04B35/622C04B35/64C04B2235/6562C04B2235/6567C04B41/0072Y02P40/60
Inventor 颜松柳卢晓霞
Owner 福建省德化县瓷言坊陶瓷工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com