Zinc plating device and method and application

A plating tank, plating bath technology, applied in hot dip plating process, coating, metal material coating process and other directions, can solve problems such as adverse effects on galvanizing quality, increase in the solid content of the plating solution, etc., to achieve constant temperature, prevent The effect of blasting zinc

Inactive Publication Date: 2020-08-25
中电建武汉铁塔有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The previous practice was to manually add H 2 o 2 and ammonia to make Fe 2+ Oxidized to trivalent iron and settled to remove it, the sediment is deposited in the electr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc plating device and method and application
  • Zinc plating device and method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0056] The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, but not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts shall fall within the protection scope of the present invention.

[0057] like figure 1 shown, combined with figure 2 , The galvanizing device of the present invention includes a plating aid pool 1, a galvanizing pot 2, a hydrogen peroxide storage tank 101, an ammonia water storage tank 102, a natural gas zinc furnace 201, a flue gas pipeline 202, a gas-liquid heat exchanger 203, a liquid- Liquid heat exchanger 204 and second gas-liquid heat exchanger 205.

[0058] Wherein, the galvanized incoming material is a steel struct...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a zinc plating device and method and application. A plating assisting pool is divided into a plating assisting tank and a plating assisting settling tank, inclined tube settlingis carried out on a plating assisting solvent in the plating assisting settling tank, supernatant obtained after settling flows back to the plating assisting tank, and it can be effectively preventedthat precipitate settles in the plating assisting tank and causes silting with the passing of time, the content of solids in the plating assisting liquid is increased consequently, and adverse effects are caused on the zinc plating quality. A sludge screw pump and a plate-and-frame filter press are arranged, sludge in the plating assisting settling tank is removed regularly, leachate generated infilter pressing flows back to an inclined tube settling area, and recycling of the leachate is promoted. The temperature in the plating assisting tank is controlled to be 60-80 DEG C, and thus on onehand, the reaction of the Fe2+ removing technology can be ensured; and meanwhile, steel structure parts out of the plating assisting tank can make moisture be quickly volatilized in the transfer process under the action of self residual temperature, and zinc bursting occurring when the steel structure parts enter a zinc plating pot can be avoided.

Description

technical field [0001] The invention relates to the technical field of galvanizing, in particular to a galvanizing device, method and application. Background technique [0002] At present, hot-dip galvanizing is generally required for steel structures such as transmission towers and communication towers. The process steps are as follows: [0003] Pickling: rust removal of steel structural parts; [0004] Water washing: to remove FeCl produced during the pickling process 3 and excess HCl; [0005] Entering the plating bath for treatment: surface treatment of steel structural parts, adding H 2 O 2 and ammonia to remove Fe 2+ ; [0006] Enter the galvanizing pot for galvanizing treatment; [0007] Cooling and passivation to obtain a galvanized finished product. [0008] The above prior art has the following problems: [0009] (1) Entering the treatment process of the plating bath, when the concentration of ferrous ions in the plating solution is too high, the quality o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C2/06C23C2/02
CPCC23C2/003C23C2/02C23C2/06
Inventor 郑治伟王硕刘云王朋王烨迪
Owner 中电建武汉铁塔有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap