A kind of high flame retardant enameled wire lubricating oil and preparation method thereof

An enameled wire and high flame-retardant technology, which is applied in the field of enameled wire lubricating oil and its preparation, can solve problems such as wax deposits in the coil, easy disconnection, and health effects, and achieve good product consistency, high flame-retardant performance, and easy Volatile effect

Active Publication Date: 2022-05-24
鹤山市江磁线缆有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The 120# rubber solvents used in traditional lubricating oils are all light and volatile petroleum solvents. These solvents will all volatilize into the air, affecting environmental protection, and human inhalation will affect health. In addition, these light petroleum solvents have a low flash point and are volatile Inflammable and explosive items, there are certain risks in the process of storage and use; and the solubility of paraffin is not good, and it is easy to precipitate. Such enameled wires are prone to wax accumulation when winding coils, so they are easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high flame retardant enameled wire lubricant, by weight percentage, comprising the following raw material components: flame retardant base oil 9750g, high-grade fatty acid ester 50g, isoparaffin 150g, siloxane 50g; the flame retardant base oil is trimethylol propane oleate; the high-grade fatty acid ester is sorbitol fatty acid ester (span 80); the isomeric alkane is ExxonMobil Isopar E; the siloxane is dimethicone.

[0033] Preparation method of high flame retardant enameled wire lubricating oil, comprising the following steps:

[0034] At 40-50 ° C, in a 10 liter stainless steel closed container with a mechanical stirring device, first add flame retardant base oil, stir for 5 minutes, add the remaining components, stir for another 25 minutes.

Embodiment 2

[0036] A high flame retardant enameled wire lubricant, by weight percentage, comprising the following raw material components: flame retardant base oil 9550g, high-grade fatty acid ester 100g, isoparaffin 200g, siloxane 150g; the flame retardant base oil is trimethylol propane oleate; the high-grade fatty acid ester is polyethylene glycol 400 bilaurate (PEG400DL); the isomeric alkane is Japanese Izumitsu Ipclean LX; the siloxane is dimethicone.

[0037] The preparation method of the high flame retardant enameled wire lubricating oil is the same as Example 1.

Embodiment 3

[0039] A high flame retardant enameled wire lubricating oil, by weight, comprising the following raw material components: flame retardant base oil 9350g, high-grade fatty acid ester 200g, isoparaffin 300g, siloxane 150g; the flame retardant base oil is trimethylol propane oleate; the high-grade fatty acid ester is polyethylene glycol 6000 bisteastate (PEG6000DS); the isomeric alkane is Petrochemical China D80; the siloxane is dimethicone.

[0040] The preparation method of the high flame retardant enameled wire lubricating oil is the same as Example 1.

[0041] Embodiment 1-3 of the present invention obtained high flame retardant enameled wire surface lubricating effect is good, low friction coefficient, suitable for high-speed line production; in the case of electronic sparks, open flames will not be easily burned, heat resistance oxidation is good, high safety; the surface of the enameled wire is smoother, better to ensure the insulation performance of the enameled wire; each co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high flame-retardant enameled wire lubricating oil, which comprises the following raw material components by weight percentage: 93.5-97.5% of flame-retardant base oil, 0.5-2.0% of high-grade fatty acid ester, 1.5-3.0% of isoparaffin, Siloxane 0.5‑1.5%. The present invention also provides a preparation method of highly flame-retardant enameled wire lubricating oil, comprising the following steps: mixing flame-retardant base oil, higher fatty acid ester, isoparaffin, and siloxane to obtain a mixture; heating the obtained mixture, Stir to obtain high flame retardant enameled wire lubricating oil. The lubricating oil of the present invention is applied to lubricating oil coating on the surface of enameled wires, has the advantages of good lubricating effect and low static friction coefficient, and is suitable for the production of high-speed automatic inductance winding machines; it will not easily burn when encountering electronic sparks or open flames, and has good thermal oxidation resistance , high safety; the surface of the enameled wire is smoother, and the insulation performance of the enameled wire is better guaranteed; the raw materials of each component are commercially available, and the preparation method is simple and the cost is low.

Description

Technical field [0001] The present invention relates to an enameled wire lubricating oil and a preparation method thereof, specifically to a high flame retardant enameled wire lubricating oil and a preparation method thereof. Background [0002] In the enameled wire manufacturing process, after the copper wire is coated with insulation paint and cured, it is also necessary to coat a layer of lubricating oil on the surface to facilitate the protection of the insulating paint film from damage and not easy to break the wire when the coil is wrapped around the production industry through components such as winding machine guide wheels. The traditional enameled wire surface lubricating oil is coated with 120# rubber solvent as a diluent (mass ratio of 95%-99%), dissolved paraffin wax, mineral oil (mass ratio of 1%-5%) coated on the surface of enameled wire, 120# rubber solvent volatilization, paraffin wax and mineral oil attached to the surface of the wire to play a lubricating role. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10N30/06C10N40/32C10N30/08
CPCC10M169/044C10M2207/283C10M2209/104C10M2203/022C10M2229/041C10M2209/109
Inventor 赵志感黄秀芬区维忠
Owner 鹤山市江磁线缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products