Preparation method of high-performance release paper

A release paper, high-performance technology, applied in pulp beating method, paper making, paper machine, etc., can solve the problems of release paper use frequency reduction, unstable peel strength, waste materials, etc., to achieve stable peel performance, excellent resistance Oxidative aging ability, effect of increasing strength

Active Publication Date: 2020-09-22
XIANHE CO LTD
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the fact that the coating layer on the release paper in the prior art is prone to aging during long-term storage and high-temperature use, which easily leads to unstable peel strength, and it is also easy to reduce the number of times the release paper is used. reduce the waste of materials, but also greatly increase the cost and other issues, a preparation method of high-performance release paper is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-performance release paper

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] A method for preparing high-performance release paper, comprising the following preparation steps:

[0035](1) Select bleached kraft softwood pulp with a beating degree of 50-60°SR after refining as the raw material slurry, then add acrylic resin-coated titanium dioxide and mix evenly, and the addition amount per ton of paper is 80-120kg;

[0036] (2) Adding the sizing agent alkyl ketene dimer in the pulp, the addition amount is 0.08-0.3wt%;

[0037] (3) On the fourdrinier paper machine, carry out online copying, pressing and dehydration;

[0038] (4) The paper is first dried to a humidity of 25-35wt%, followed by semi-wet drying and pressure treatment at 90-110°C;

[0039] (5) Use starch for surface sizing, the amount of sizing is 0.8-2g / m 2 , followed by drying;

[0040] (6) Prepare base paper after spraying wetting, super calendering, coiling and slitting;

[0041] (7) Corona discharge treatment is carried out on the base paper, and then the anti-oxidation silico...

Embodiment 1

[0045] A method for preparing high-performance release paper, comprising the following preparation steps:

[0046] (1) the bleached kraft softwood pulp of 55 ° of SR is used as the raw material slurry after the degree of beating is selected for use;

[0047] (2) adding the sizing agent alkyl ketene dimer in the slurry, the addition amount is 0.15wt%;

[0048] (3) On the fourdrinier paper machine, carry out online copying, pressing and dehydration;

[0049] (4) The paper is first dried to a humidity of 30wt%, followed by semi-wet drying and pressure treatment at 100°C;

[0050] (5) Use starch for surface sizing, and the sizing amount is 1.3g / m 2 , followed by drying;

[0051] (6) Prepare base paper after spraying wetting, super calendering, coiling and slitting;

[0052] (7) Corona discharge treatment is carried out on the base paper, and then the anti-oxidation silicone emulsion is coated on the base paper, and the coating amount is 1.1g / m 2 , to prepare high-performance ...

Embodiment 2

[0055] A method for preparing high-performance release paper, comprising the following preparation steps:

[0056] (1) select the bleached kraft softwood pulp of 50 ° of SR as the raw material slurry after the beating degree is selected;

[0057] (2) adding the sizing agent alkyl ketene dimer in the slurry, the addition amount is 0.08wt%;

[0058] (3) On the fourdrinier paper machine, carry out online copying, pressing and dehydration;

[0059] (4) The paper is first dried to a humidity of 35wt%, followed by semi-wet drying and pressure treatment at 90°C;

[0060] (5) Use starch for surface sizing, the amount of sizing is 0.9g / m 2 , followed by drying;

[0061] (6) Prepare base paper after spraying wetting, super calendering, coiling and slitting;

[0062] (7) The base paper is treated with corona discharge, and then the anti-oxidation silicone emulsion is coated on the base paper, and the coating amount is 1g / m 2 , to prepare high-performance release paper after drying; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of high-performance release paper, which relates to the technical field of papermaking. The method comprises the following steps: (1) selecting ground bleached sulfate softwood pulp as raw material pulp; (2) adding an internal sizing agent into the raw material pulp; (3) carrying out papermaking on a fourdrinier machine, and carrying out squeezing dehydration; (4) performing semi-wet drying and pressurizing treatment; (5) performing surface sizing and drying; (6) performing spray wetting, super calendaring, coiling and slitting to prepare raw paper;and (7) carrying out corona discharge treatment on the raw paper, then coating the raw paper with an antioxidant organosilicon emulsion, and drying to prepare the high-performance release paper. According to the method, the release layer prepared by coating the raw paper with the antioxidant organosilicon emulsion has excellent antioxidant aging resistance, so that the aging problem caused by long-time storage and high-temperature use of the coating layer on the release paper is prevented, meanwhile, the stripping performance is more stable, and the use frequency of the release paper is higher.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a method for preparing high-performance release paper. Background technique [0002] Release paper is a kind of coated paper, usually composed of a paper base layer and a coating layer, and its basic structure is not much different from that of general coated paper. Release paper has a wide range of uses, and can be used in construction and other industries. The use environment is high-temperature environment, such as in the production of thermosetting resin-impregnated paper high-pressure decorative laminates. Thermosetting resin-impregnated paper high-pressure decorative laminates are made of several special The paper is impregnated with melamine resin (MF resin) and phenolic resin respectively, and then different types of impregnated special paper blanks are stacked together, and the thermosetting sheet made after hot pressing is affected by the evenness and permeability o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21D1/02D21F1/00D21F3/00D21G1/00D21H21/16D21H25/04
CPCD21D1/02D21H21/16D21F1/00D21F3/00D21G1/00D21H25/04
Inventor 张诚史君齐骆华英岳跃振路崇斌郑世安
Owner XIANHE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com